Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_131_5_37474750_4sKrhV.cif"

There are 56 T-atoms per unit cell
There are 112 O-atoms per unit cell

Framework density = 22.25 T-atoms per nm^3
Material density = 2.220 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6223 Angstrom
T1  -- O2  = 1.6245 Angstrom
T1  -- O3  = 1.6424 Angstrom
T1  -- O4  = 1.6696 Angstrom
      mean = 1.6397 Angstrom
        t1 = 0.022070  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009526  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6388 Angstrom
T2  -- O5  = 1.6368 Angstrom
T2  -- O6  = 1.6816 Angstrom
T2  -- O7  = 1.6262 Angstrom
      mean = 1.6459 Angstrom
        t1 = 0.025370  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013702  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6255 Angstrom
T3  -- O6  = 1.6255 Angstrom
T3  -- O8  = 1.6549 Angstrom
T3  -- O8  = 1.6549 Angstrom
      mean = 1.6402 Angstrom
        t1 = 0.043139  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040223  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6264 Angstrom
T4  -- O4  = 1.6264 Angstrom
T4  -- O9  = 1.5718 Angstrom
T4  -- O10 = 1.5830 Angstrom
      mean = 1.6019 Angstrom
        t1 = 0.035480  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024710  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6202 Angstrom
T5  -- O7  = 1.6202 Angstrom
T5  -- O11 = 1.5644 Angstrom
T5  -- O12 = 1.6360 Angstrom
      mean = 1.6102 Angstrom
        t1 = 0.032028  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027874  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5644 A <--> 1.6816 A
          Mean   = 1.6319 A
          StdDev = 0.0272 A

       t1 Range  = 0.0221 <-- 0.0316 --> 0.0431
       t2 Range  = 0.0095 <-- 0.0232 --> 0.0402

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.035 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.699 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.026 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.155 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.171 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.715 deg; O3  -- O4  = 3 A
       108.699 deg <-- 109.467 deg --> 111.715 deg

O3  -- T2  -- O5  = 112.110 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.902 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.009 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 108.726 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.253 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 106.702 deg; O6  -- O7  = 3 A
       106.702 deg <-- 109.450 deg --> 112.110 deg

O6  -- T3  -- O6  = 102.659 deg; O6  -- O6  = 3 A
O6  -- T3  -- O8  = 117.995 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 105.618 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 105.618 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 117.995 deg; O6  -- O8  = 3 A
O8  -- T3  -- O8  = 107.538 deg; O8  -- O8  = 3 A
       102.659 deg <-- 109.570 deg --> 117.995 deg

O4  -- T4  -- O4  = 119.665 deg; O4  -- O4  = 3 A
O4  -- T4  -- O9  = 106.816 deg; O4  -- O9  = 3 A
O4  -- T4  -- O10 = 108.028 deg; O4  -- O10 = 3 A
O4  -- T4  -- O9  = 106.816 deg; O4  -- O9  = 3 A
O4  -- T4  -- O10 = 108.028 deg; O4  -- O10 = 3 A
O9  -- T4  -- O10 = 106.838 deg; O9  -- O10 = 3 A
       106.816 deg <-- 109.365 deg --> 119.665 deg

O7  -- T5  -- O7  = 111.008 deg; O7  -- O7  = 3 A
O7  -- T5  -- O11 = 106.221 deg; O7  -- O11 = 3 A
O7  -- T5  -- O12 = 113.793 deg; O7  -- O12 = 3 A
O7  -- T5  -- O11 = 106.221 deg; O7  -- O11 = 3 A
O7  -- T5  -- O12 = 113.793 deg; O7  -- O12 = 3 A
O11 -- T5  -- O12 = 105.021 deg; O11 -- O12 = 3 A
       105.021 deg <-- 109.343 deg --> 113.793 deg

        O-T-O SUMMARY
          Range  = 102.6586 deg <--> 119.6652 deg
          Mean   = 109.6725 deg
          StdDev = 3.9953 deg

        O--O SUMMARY
          Range  = 2.5334 A <--> 2.8123 A
          Mean   = 2.6626 A
          StdDev = 0.0797 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 106.035 deg; T1  -- T2  = 4.9926 A
T1  - O1  - T1  - O3  - T4  =  89.971 deg; T1  -- T4  = 4.2845 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4945 A
T2  - O2  - T1  - O3  - T4  = 140.421 deg; T2  -- T4  = 5.6641 A
T2  - O2  - T1  - O4  - T1  = 127.139 deg; T2  -- T1  = 5.6584 A
T4  - O3  - T1  - O4  - T1  =  87.781 deg; T4  -- T1  = 4.2519 A

T1  - O3  - T2  - O5  - T3  = 107.542 deg; T1  -- T3  = 4.8497 A
T1  - O3  - T2  - O6  - T5  =  98.174 deg; T1  -- T5  = 4.6948 A
T1  - O3  - T2  - O7  - T2  = 138.399 deg; T1  -- T2  = 5.6859 A
T3  - O5  - T2  - O6  - T5  = 141.501 deg; T3  -- T5  = 5.6743 A
T3  - O5  - T2  - O7  - T2  =  88.058 deg; T3  -- T2  = 4.0868 A
T5  - O6  - T2  - O7  - T2  =  91.347 deg; T5  -- T2  = 4.3517 A

T2  - O6  - T3  - O6  - T2  =  86.116 deg; T2  -- T2  = 3.9652 A
T2  - O6  - T3  - O8  - T3  =  91.942 deg; T2  -- T3  = 4.0868 A
T2  - O6  - T3  - O8  - T3  = 178.058 deg; T2  -- T3  = 5.6820 A
T2  - O6  - T3  - O8  - T3  = 178.058 deg; T2  -- T3  = 5.6820 A
T2  - O6  - T3  - O8  - T3  =  91.942 deg; T2  -- T3  = 4.0868 A
T3  - O8  - T3  - O8  - T3  =  90.000 deg; T3  -- T3  = 3.9300 A

T1  - O4  - T4  - O4  - T1  = 175.561 deg; T1  -- T1  = 5.8213 A
T1  - O4  - T4  - O9  - T4  =  90.029 deg; T1  -- T4  = 4.2845 A
T1  - O4  - T4  - O10 - T4  =  92.219 deg; T1  -- T4  = 4.2519 A
T1  - O4  - T4  - O9  - T4  =  90.029 deg; T1  -- T4  = 4.2845 A
T1  - O4  - T4  - O10 - T4  =  92.219 deg; T1  -- T4  = 4.2519 A
T4  - O9  - T4  - O10 - T4  =  90.000 deg; T4  -- T4  = 4.3339 A

T2  - O7  - T5  - O7  - T2  = 102.937 deg; T2  -- T2  = 4.8596 A
T2  - O7  - T5  - O11 - T5  =  88.653 deg; T2  -- T5  = 4.3517 A
T2  - O7  - T5  - O12 - T5  = 128.499 deg; T2  -- T5  = 5.5863 A
T2  - O7  - T5  - O11 - T5  =  88.653 deg; T2  -- T5  = 4.3517 A
T2  - O7  - T5  - O12 - T5  = 128.499 deg; T2  -- T5  = 5.5863 A
T5  - O11 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.3967 A

        T-T-T SUMMARY
          Range  = 86.1161 deg <--> 178.0581 deg
          Mean   = 110.7915 deg
          StdDev = 29.2902 deg

        T--T SUMMARY
          Range  = 3.9300 A <--> 5.8213 A
          Mean   = 4.7808 A
          StdDev = 0.6609 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 163.807 deg ; T1  -- T1   3.2123 A

T1  -- O2  -- T1  = 150.725 deg ; T1  -- T1   3.1435 A

T1  -- O3  -- T2  = 142.421 deg ; T1  -- T2   3.1064 A

T1  -- O4  -- T4  = 124.188 deg ; T1  -- T4   2.9128 A

T2  -- O5  -- T2  = 130.730 deg ; T2  -- T2   2.9757 A

T2  -- O6  -- T3  = 122.813 deg ; T2  -- T3   2.9039 A

T2  -- O7  -- T5  = 146.190 deg ; T2  -- T5   3.1061 A

T3  -- O8  -- T3  = 114.195 deg ; T3  -- T3   2.7789 A

T4  -- O9  -- T4  = 174.912 deg ; T4  -- T4   3.1405 A

T4  -- O10 -- T4  = 141.237 deg ; T4  -- T4   2.9867 A

T5  -- O11 -- T5  = 172.292 deg ; T5  -- T5   3.1217 A

T5  -- O12 -- T5  = 142.251 deg ; T5  -- T5   3.0961 A


        T-O-T SUMMARY
          Range  = 114.1948° <--> 174.9117 deg
          Mean   = 142.4544 deg
          StdDev = 17.1233 deg

        T--T SUMMARY
          Range  = 2.7789 A <--> 3.2123 A
          Mean   = 3.0445 A
          StdDev = 0.1188 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T3  = 2.7789 Angstrom
T3  -- T3  = 2.7789 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 16 28 51 87 129 165 199 240 289 353 429 492 546 627
TD10 = 929
Circuit symbol = 4.5.4.7.4.7
Weight = 10
Vertex symbol  = 4.5.4.8.4.10
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 34 58 88 120 153 196 247 306 366 405 465 566 641
TD10 = 930
Circuit symbol = 4.5.4.9_{2}.6.7_{2}
Weight = 10
Vertex symbol  = 4.5.4.10_{2}.8.10_{2}
Weight = 34

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 20 40 64 86 115 160 208 256 301 346 420 502 562 635
TD10 = 963
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.10_{4}.12_{4}.12_{4}
Weight = 62

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 7 12 24 43 73 118 168 205 229 263 333 428 507 555 594
TD10 = 884
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.10
Weight = 17

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 34 58 89 122 153 189 241 301 358 418 472 534 635
TD10 = 918
Circuit symbol = 4.5.4.6.4.6
Weight = 10
Vertex symbol  = 4.5.4.10.4.10
Weight = 24

<TD10> = 926.143
Average ring size = 6.0329