Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_131_5_26428706_7JvdHA.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 27.12 T-atoms per nm^3
Material density = 2.706 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7271 Angstrom
T1  -- O2  = 1.7686 Angstrom
T1  -- O3  = 1.5338 Angstrom
T1  -- O4  = 1.8087 Angstrom
      mean = 1.7095 Angstrom
        t1 = 0.125525  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.089084  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.8156 Angstrom
T2  -- O5  = 1.5909 Angstrom
T2  -- O6  = 1.7388 Angstrom
T2  -- O7  = 1.4232 Angstrom
      mean = 1.6421 Angstrom
        t1 = 0.090278  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.105664  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.4386 Angstrom
T3  -- O8  = 1.6417 Angstrom
T3  -- O9  = 1.5594 Angstrom
T3  -- O10 = 1.4688 Angstrom
      mean = 1.5272 Angstrom
        t1 = 0.096656  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.077810  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6215 Angstrom
T4  -- O9  = 1.6215 Angstrom
T4  -- O11 = 1.4907 Angstrom
T4  -- O11 = 1.4907 Angstrom
      mean = 1.5561 Angstrom
        t1 = 0.084432  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049453  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5882 Angstrom
T5  -- O12 = 1.6551 Angstrom
T5  -- O13 = 1.5801 Angstrom
T5  -- O10 = 1.5882 Angstrom
      mean = 1.6029 Angstrom
        t1 = 0.058145  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037185  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4232 A <--> 1.8156 A
          Mean   = 1.6146 A
          StdDev = 0.1245 A

       t1 Range  = 0.0581 <-- 0.0910 --> 0.1255
       t2 Range  = 0.0372 <-- 0.0718 --> 0.1057

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.298 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 100.720 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 118.436 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  93.315 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 127.054 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  94.324 deg; O3  -- O4  = 2 A
       93.315 deg <-- 107.525 deg --> 127.054 deg

O4  -- T2  -- O5  = 111.328 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 119.101 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 112.811 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 107.590 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.768 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  =  95.994 deg; O6  -- O7  = 2 A
       95.994 deg <-- 109.265 deg --> 119.101 deg

O7  -- T3  -- O8  = 112.520 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  =  97.564 deg; O7  -- O9  = 2 A
O7  -- T3  -- O10 =  95.312 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 117.276 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 113.559 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 116.838 deg; O9  -- O10 = 3 A
       95.312 deg <-- 108.845 deg --> 117.276 deg

O9  -- T4  -- O9  = 128.888 deg; O9  -- O9  = 3 A
O9  -- T4  -- O11 = 107.321 deg; O9  -- O11 = 3 A
O9  -- T4  -- O11 = 105.194 deg; O9  -- O11 = 2 A
O9  -- T4  -- O11 = 105.194 deg; O9  -- O11 = 2 A
O9  -- T4  -- O11 = 107.321 deg; O9  -- O11 = 3 A
O11 -- T4  -- O11 =  99.091 deg; O11 -- O11 = 2 A
       99.091 deg <-- 108.835 deg --> 128.888 deg

O10 -- T5  -- O12 = 115.262 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 109.284 deg; O10 -- O13 = 3 A
O10 -- T5  -- O10 =  92.908 deg; O10 -- O10 = 2 A
O12 -- T5  -- O13 = 113.081 deg; O12 -- O13 = 3 A
O12 -- T5  -- O10 = 115.262 deg; O12 -- O10 = 3 A
O13 -- T5  -- O10 = 109.284 deg; O13 -- O10 = 3 A
       92.908 deg <-- 109.180 deg --> 115.262 deg

        O-T-O SUMMARY
          Range  = 92.9078 deg <--> 128.8884 deg
          Mean   = 109.1993 deg
          StdDev = 9.4507 deg

        O--O SUMMARY
          Range  = 2.1491 A <--> 3.2022 A
          Mean   = 2.6123 A
          StdDev = 0.2503 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 157.992 deg ; T1  -- T1   3.3908 A

T1  -- O2  -- T1  = 143.210 deg ; T1  -- T1   3.3564 A

T1  -- O3  -- T1  = 153.418 deg ; T1  -- T1   2.9854 A

T1  -- O4  -- T2  = 169.323 deg ; T1  -- T2   3.6086 A

T2  -- O5  -- T2  = 111.202 deg ; T2  -- T2   2.6253 A

T2  -- O6  -- T2  = 137.766 deg ; T2  -- T2   3.2441 A

T2  -- O7  -- T3  = 160.708 deg ; T2  -- T3   2.8213 A

T3  -- O8  -- T3  = 129.037 deg ; T3  -- T3   2.9640 A

T3  -- O9  -- T4  = 101.632 deg ; T3  -- T4   2.4659 A

T3  -- O10 -- T5  = 122.912 deg ; T3  -- T5   2.6861 A

T4  -- O11 -- T4  = 150.896 deg ; T4  -- T4   2.8857 A

T5  -- O12 -- T5  = 173.154 deg ; T5  -- T5   3.3044 A

T5  -- O13 -- T5  = 126.992 deg ; T5  -- T5   2.8281 A


        T-O-T SUMMARY
          Range  = 101.6324° <--> 173.1539 deg
          Mean   = 140.2366 deg
          StdDev = 21.3514 deg

        T--T SUMMARY
          Range  = 2.4659 A <--> 3.6086 A
          Mean   = 3.0136 A
          StdDev = 0.3414 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O9  = 2.2566 A
O7  -- O10 = 2.1491 A
O11 -- O11 = 2.2686 A
O11 -- O11 = 2.2686 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T3  = 3.4895 Angstrom
  T1  -- T5  = 3.3979 Angstrom
  T1  -- T1  = 2.9854 Angstrom
  T1  -- T1  = 3.3564 Angstrom
  T1  -- T1  = 3.3908 Angstrom
T2  -- T2  = 2.6253 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.4895 Angstrom
  T3  -- T2  = 2.8213 Angstrom
  T3  -- T3  = 2.9640 Angstrom
  T3  -- T4  = 2.4659 Angstrom
  T3  -- T5  = 2.6861 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.3270 Angstrom
  T4  -- T2  = 3.3270 Angstrom
  T4  -- T3  = 2.4659 Angstrom
  T4  -- T3  = 2.4659 Angstrom
  T4  -- T4  = 2.8857 Angstrom
  T4  -- T4  = 2.8857 Angstrom
T5  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 3.3979 Angstrom
  T5  -- T3  = 2.6861 Angstrom
  T5  -- T5  = 3.3044 Angstrom
  T5  -- T5  = 2.8281 Angstrom
  T5  -- T1  = 3.3979 Angstrom
  T5  -- T3  = 2.6861 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 8 14 25 42 67 104 154 207 253 303 371 451 528 600 685
TD10 = 879
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.12_{2}
Weight = 25

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 16 26 45 77 114 150 193 250 314 376 438 514 610 704
TD10 = 885
Circuit symbol = 4.4.4.8_{2}.6.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.11.6.8
Weight = 22

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 17 30 51 80 113 148 188 237 299 365 434 510 593 687
TD10 = 878
Circuit symbol = 4.6.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 4.6.4.10.4.11
Weight = 26

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 34 56 80 110 153 202 248 302 369 438 506 580 680
TD10 = 915
Circuit symbol = 4.4.4.8.6.6
Weight = 8
Vertex symbol  = 4.4.4.11_{2}.10.10
Weight = 32

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 16 28 51 85 122 154 183 228 300 378 442 509 599 703
TD10 = 881
Circuit symbol = 4.6.4.6_{2}.4.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.10
Weight = 21

<TD10> = 885.000
Average ring size = 5.4378