Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_130_2_31105_QlYRC4.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.37 T-atoms per nm^3
Material density = 1.932 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6100 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O4  = 1.6217 Angstrom
T1  -- O3  = 1.6210 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.005273  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001055  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6099 Angstrom
T2  -- O2  = 1.6202 Angstrom
T2  -- O3  = 1.6208 Angstrom
T2  -- O4  = 1.6217 Angstrom
      mean = 1.6181 Angstrom
        t1 = 0.005206  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001081  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6099 A <--> 1.6217 A
          Mean   = 1.6182 A
          StdDev = 0.0048 A

       t1 Range  = 0.0052 <-- 0.0052 --> 0.0053
       t2 Range  = 0.0011 <-- 0.0011 --> 0.0011

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.543 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.532 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.564 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.379 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.414 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.395 deg; O4  -- O3  = 3 A
       109.379 deg <-- 109.471 deg --> 109.564 deg

O1  -- T2  -- O2  = 109.600 deg; O1  -- O2  = 3 A
O1  -- T2  -- O3  = 109.556 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 109.502 deg; O1  -- O4  = 3 A
O2  -- T2  -- O3  = 109.359 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.391 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.418 deg; O3  -- O4  = 3 A
       109.359 deg <-- 109.471 deg --> 109.600 deg

        O-T-O SUMMARY
          Range  = 109.3588 deg <--> 109.6003 deg
          Mean   = 109.4712 deg
          StdDev = 0.0827 deg

        O--O SUMMARY
          Range  = 2.6387 A <--> 2.6466 A
          Mean   = 2.6425 A
          StdDev = 0.0033 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  89.972 deg; T2  -- T2  = 4.4230 A
T2  - O1  - T1  - O4  - T2  = 127.406 deg; T2  -- T2  = 5.5896 A
T2  - O1  - T1  - O3  - T2  =  90.005 deg; T2  -- T2  = 4.4258 A
T2  - O2  - T1  - O4  - T2  = 120.822 deg; T2  -- T2  = 5.2622 A
T2  - O2  - T1  - O3  - T2  = 120.566 deg; T2  -- T2  = 5.2747 A
T2  - O4  - T1  - O3  - T2  = 105.214 deg; T2  -- T2  = 4.8095 A

T1  - O1  - T2  - O2  - T1  =  90.028 deg; T1  -- T1  = 4.4252 A
T1  - O1  - T2  - O3  - T1  = 127.379 deg; T1  -- T1  = 5.5889 A
T1  - O1  - T2  - O4  - T1  =  89.995 deg; T1  -- T1  = 4.4255 A
T1  - O2  - T2  - O3  - T1  = 120.812 deg; T1  -- T1  = 5.2619 A
T1  - O2  - T2  - O4  - T1  = 120.570 deg; T1  -- T1  = 5.2748 A
T1  - O3  - T2  - O4  - T1  = 105.204 deg; T1  -- T1  = 4.8092 A

        T-T-T SUMMARY
          Range  = 89.9718 deg <--> 127.4061 deg
          Mean   = 108.9977 deg
          StdDev = 15.0286 deg

        T--T SUMMARY
          Range  = 4.4230 A <--> 5.5896 A
          Mean   = 4.9642 A
          StdDev = 0.4449 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 176.414 deg ; T1  -- T2   3.2183 A

T1  -- O2  -- T2  = 139.031 deg ; T1  -- T2   3.0356 A

T1  -- O3  -- T2  = 139.135 deg ; T1  -- T2   3.0379 A

T1  -- O4  -- T2  = 136.815 deg ; T1  -- T2   3.0157 A


        T-O-T SUMMARY
          Range  = 136.8145° <--> 176.4140 deg
          Mean   = 147.8487 deg
          StdDev = 16.6488 deg

        T--T SUMMARY
          Range  = 3.0157 A <--> 3.2183 A
          Mean   = 3.0769 A
          StdDev = 0.0828 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

<TD10> = 867.000
Average ring size = 5.8182