Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_6111_0M1hCD.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.78 T-atoms per nm^3
Material density = 1.774 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6209 Angstrom
T1  -- O2  = 1.6210 Angstrom
T1  -- O4  = 1.6493 Angstrom
T1  -- O3  = 1.6157 Angstrom
      mean = 1.6267 Angstrom
        t1 = 0.012644  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007007  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6264 Angstrom
T2  -- O5  = 1.6103 Angstrom
T2  -- O6  = 1.6103 Angstrom
T2  -- O7  = 1.6361 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.018005  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013279  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6103 A <--> 1.6493 A
          Mean   = 1.6237 A
          StdDev = 0.0126 A

       t1 Range  = 0.0126 <-- 0.0153 --> 0.0180
       t2 Range  = 0.0070 <-- 0.0101 --> 0.0133

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.483 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 110.005 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.450 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 110.009 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.451 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.426 deg; O4  -- O3  = 3 A
       108.483 deg <-- 109.470 deg --> 110.009 deg

O4  -- T2  -- O5  = 107.627 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.631 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 114.354 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.539 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.811 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.805 deg; O6  -- O7  = 3 A
       107.627 deg <-- 109.461 deg --> 114.354 deg

        O-T-O SUMMARY
          Range  = 107.6271 deg <--> 114.3539 deg
          Mean   = 109.5912 deg
          StdDev = 1.8990 deg

        O--O SUMMARY
          Range  = 2.6123 A <--> 2.7416 A
          Mean   = 2.6558 A
          StdDev = 0.0388 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  89.827 deg; T2  -- T1  = 4.2745 A
T2  - O1  - T1  - O4  - T1  =  89.827 deg; T2  -- T1  = 4.2745 A
T2  - O1  - T1  - O3  - T1  = 140.418 deg; T2  -- T1  = 5.6778 A
T1  - O2  - T1  - O4  - T1  = 108.702 deg; T1  -- T1  = 5.2615 A
T1  - O2  - T1  - O3  - T1  = 111.942 deg; T1  -- T1  = 5.3610 A
T1  - O4  - T1  - O3  - T1  = 111.944 deg; T1  -- T1  = 5.3611 A

T1  - O4  - T2  - O5  - T2  =  90.171 deg; T1  -- T2  = 4.2745 A
T1  - O4  - T2  - O6  - T2  =  90.171 deg; T1  -- T2  = 4.2745 A
T1  - O4  - T2  - O7  - T2  = 179.704 deg; T1  -- T2  = 5.5177 A
T2  - O5  - T2  - O6  - T2  = 109.539 deg; T2  -- T2  = 5.2615 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2135 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2136 A

        T-T-T SUMMARY
          Range  = 89.8273 deg <--> 179.7036 deg
          Mean   = 109.5979 deg
          StdDev = 28.3320 deg

        T--T SUMMARY
          Range  = 4.2135 A <--> 5.6778 A
          Mean   = 4.8294 A
          StdDev = 0.5809 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.997 deg ; T1  -- T1   3.2374 A

T1  -- O2  -- T1  = 173.997 deg ; T1  -- T1   3.2375 A

T1  -- O3  -- T1  = 180.000 deg ; T1  -- T1   3.2313 A

T1  -- O4  -- T2  = 117.530 deg ; T1  -- T2   2.8009 A

T2  -- O5  -- T2  = 179.877 deg ; T2  -- T2   3.2206 A

T2  -- O6  -- T2  = 179.877 deg ; T2  -- T2   3.2207 A

T2  -- O7  -- T2  = 112.257 deg ; T2  -- T2   2.7169 A


        T-O-T SUMMARY
          Range  = 112.2574° <--> 180.0000 deg
          Mean   = 159.6480 deg
          StdDev = 28.7034 deg

        T--T SUMMARY
          Range  = 2.7169 A <--> 3.2375 A
          Mean   = 3.0950 A
          StdDev = 0.2158 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7169 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 31 48 69 93 120 150 186 226 266 305 343 382 419
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 25 42 63 84 110 148 186 214 250 308 361 384 404
TD10 = 685
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12_{2}.*
Weight = 24

<TD10> = 708.000
Average ring size = 5.5714