Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_5313_ZfoJDd.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 26.36 T-atoms per nm^3
Material density = 2.630 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6391 Angstrom
T1  -- O2  = 1.6382 Angstrom
T1  -- O3  = 1.6440 Angstrom
T1  -- O4  = 1.6941 Angstrom
      mean = 1.6538 Angstrom
        t1 = 0.047913  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037841  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6142 Angstrom
T2  -- O5  = 1.5786 Angstrom
T2  -- O6  = 1.5780 Angstrom
T2  -- O7  = 1.6933 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.090419  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.087381  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5780 A <--> 1.6941 A
          Mean   = 1.6349 A
          StdDev = 0.0419 A

       t1 Range  = 0.0479 <-- 0.0692 --> 0.0904
       t2 Range  = 0.0378 <-- 0.0626 --> 0.0874

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 113.907 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.364 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.543 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 103.214 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.636 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 119.296 deg; O3  -- O4  = 3 A
       103.214 deg <-- 109.493 deg --> 119.296 deg

O4  -- T2  -- O5  =  95.080 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  =  94.879 deg; O4  -- O6  = 2 A
O4  -- T2  -- O7  = 134.052 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 120.978 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 106.796 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 106.696 deg; O6  -- O7  = 3 A
       94.879 deg <-- 109.747 deg --> 134.052 deg

        O-T-O SUMMARY
          Range  = 94.8794 deg <--> 134.0524 deg
          Mean   = 109.7738 deg
          StdDev = 11.8357 deg

        O--O SUMMARY
          Range  = 2.3514 A <--> 3.0453 A
          Mean   = 2.6660 A
          StdDev = 0.2137 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 163.440 deg; T1  -- T1  = 5.4942 A
T1  - O1  - T1  - O3  - T2  =  87.321 deg; T1  -- T2  = 4.0235 A
T1  - O1  - T1  - O4  - T1  =  98.201 deg; T1  -- T1  = 4.5992 A
T1  - O2  - T1  - O3  - T2  =  87.389 deg; T1  -- T2  = 4.0198 A
T1  - O2  - T1  - O4  - T1  =  97.994 deg; T1  -- T1  = 4.5854 A
T2  - O3  - T1  - O4  - T1  =  96.685 deg; T2  -- T1  = 4.7313 A

T1  - O4  - T2  - O5  - T2  =  80.909 deg; T1  -- T2  = 4.0198 A
T1  - O4  - T2  - O6  - T2  = 161.311 deg; T1  -- T2  = 5.5291 A
T1  - O4  - T2  - O7  - T2  =  80.981 deg; T1  -- T2  = 4.0235 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.0628 A
T2  - O5  - T2  - O7  - T2  = 121.168 deg; T2  -- T2  = 5.4942 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.0637 A

        T-T-T SUMMARY
          Range  = 80.9094 deg <--> 163.4402 deg
          Mean   = 103.9713 deg
          StdDev = 27.7977 deg

        T--T SUMMARY
          Range  = 4.0198 A <--> 5.5291 A
          Mean   = 4.5630 A
          StdDev = 0.5775 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 116.050 deg ; T1  -- T1   2.7808 A

T1  -- O2  -- T1  = 115.521 deg ; T1  -- T1   2.7713 A

T1  -- O3  -- T1  = 180.000 deg ; T1  -- T1   3.2880 A

T1  -- O4  -- T2  = 133.589 deg ; T1  -- T2   3.0407 A

T2  -- O5  -- T2  = 175.052 deg ; T2  -- T2   3.1543 A

T2  -- O6  -- T2  = 175.028 deg ; T2  -- T2   3.1531 A

T2  -- O7  -- T2  =  98.325 deg ; T2  -- T2   2.5622 A


        T-O-T SUMMARY
          Range  = 98.3253° <--> 180.0000 deg
          Mean   = 141.9380 deg
          StdDev = 31.8633 deg

        T--T SUMMARY
          Range  = 2.5622 A <--> 3.2880 A
          Mean   = 2.9643 A
          StdDev = 0.2457 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7808 Angstrom
T1  -- T1  = 2.7713 Angstrom
T2  -- T2  = 2.5622 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 31 48 69 93 120 150 186 226 268 313 361 416 475
TD10 = 731
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 8 14 25 42 63 84 110 148 186 214 250 310 371 408 449
TD10 = 685
Circuit symbol = 4.4.4.4.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.4.4.12_{2}.*
Weight = 24

<TD10> = 708.000
Average ring size = 5.5714