Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_39851_pJmzwJ.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 23.63 T-atoms per nm^3
Material density = 2.358 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5716 Angstrom
T1  -- O1  = 1.5716 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O2  = 1.6212 Angstrom
      mean = 1.5964 Angstrom
        t1 = 0.056344  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040510  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6177 Angstrom
T2  -- O2  = 1.6352 Angstrom
T2  -- O2  = 1.6352 Angstrom
T2  -- O3  = 1.6842 Angstrom
      mean = 1.6431 Angstrom
        t1 = 0.032764  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019185  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5716 A <--> 1.6842 A
          Mean   = 1.6197 A
          StdDev = 0.0346 A

       t1 Range  = 0.0328 <-- 0.0446 --> 0.0563
       t2 Range  = 0.0192 <-- 0.0298 --> 0.0405

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  99.678 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 104.351 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 122.178 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 122.178 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 104.351 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 105.537 deg; O2  -- O2  = 3 A
       99.678 deg <-- 109.712 deg --> 122.178 deg

O4  -- T2  -- O2  = 108.339 deg; O4  -- O2  = 3 A
O4  -- T2  -- O2  = 108.339 deg; O4  -- O2  = 3 A
O4  -- T2  -- O3  = 109.361 deg; O4  -- O3  = 3 A
O2  -- T2  -- O2  = 104.616 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 112.973 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 112.973 deg; O2  -- O3  = 3 A
       104.616 deg <-- 109.433 deg --> 112.973 deg

        O-T-O SUMMARY
          Range  = 99.6779 deg <--> 122.1782 deg
          Mean   = 110.0479 deg
          StdDev = 6.7624 deg

        O--O SUMMARY
          Range  = 2.4022 A <--> 2.7950 A
          Mean   = 2.6501 A
          StdDev = 0.1158 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  =  99.329 deg; T1  -- T2  = 4.6199 A
T1  - O1  - T1  - O2  - T2  = 147.638 deg; T1  -- T2  = 5.8181 A
T1  - O1  - T1  - O2  - T1  =  99.678 deg; T1  -- T1  = 4.8044 A
T2  - O1  - T1  - O2  - T2  =  77.382 deg; T2  -- T2  = 3.6437 A
T2  - O1  - T1  - O2  - T1  = 147.638 deg; T2  -- T1  = 5.8181 A
T2  - O2  - T1  - O2  - T1  =  99.329 deg; T2  -- T1  = 4.6199 A

T2  - O4  - T2  - O2  - T1  = 126.986 deg; T2  -- T1  = 5.5053 A
T2  - O4  - T2  - O2  - T1  = 126.986 deg; T2  -- T1  = 5.5053 A
T2  - O4  - T2  - O3  - T2  = 109.361 deg; T2  -- T2  = 5.3890 A
T1  - O2  - T2  - O2  - T1  = 102.618 deg; T1  -- T1  = 4.5495 A
T1  - O2  - T2  - O3  - T2  =  87.751 deg; T1  -- T2  = 4.3669 A
T1  - O2  - T2  - O3  - T2  =  87.751 deg; T1  -- T2  = 4.3669 A

        T-T-T SUMMARY
          Range  = 77.3820 deg <--> 147.6385 deg
          Mean   = 109.8383 deg
          StdDev = 23.3560 deg

        T--T SUMMARY
          Range  = 3.6437 A <--> 5.8181 A
          Mean   = 4.8982 A
          StdDev = 0.6773 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1433 A

T1  -- O2  -- T2  = 127.016 deg ; T1  -- T2   2.9144 A

T2  -- O3  -- T2  = 180.000 deg ; T2  -- T2   3.3685 A

T2  -- O4  -- T2  = 180.000 deg ; T2  -- T2   3.2355 A


        T-O-T SUMMARY
          Range  = 127.0157° <--> 180.0000 deg
          Mean   = 166.7539 deg
          StdDev = 23.6953 deg

        T--T SUMMARY
          Range  = 2.9144 A <--> 3.3685 A
          Mean   = 3.1654 A
          StdDev = 0.1710 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 24 47 72 106 140 187 234 289 350 418 486 569 650 739
TD10 = 1115
Circuit symbol = 4.5.5.5.7.7
Weight = 12
Vertex symbol  = 4.5.5.5.8.8
Weight = 20

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 11 26 48 71 105 143 184 234 292 347 417 491 564 650 744
TD10 = 1119
Circuit symbol = 4.8_{4}.5.8_{4}.5.8_{4}
Weight = 34
Vertex symbol  = 4.8_{4}.5.8_{4}.5.8_{4}
Weight = 34

<TD10> = 1117.000
Average ring size = 6.4615