Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_30273_8MZ7KA.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.23 T-atoms per nm^3
Material density = 3.315 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6499 Angstrom
T1  -- O4  = 1.7056 Angstrom
T1  -- O3  = 1.6197 Angstrom
T1  -- O1  = 1.6024 Angstrom
      mean = 1.6444 Angstrom
        t1 = 0.038901  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026934  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6083 Angstrom
T2  -- O4  = 1.6277 Angstrom
T2  -- O4  = 1.8945 Angstrom
T2  -- O4  = 1.8945 Angstrom
T2  -- O3  = 1.6083 Angstrom
T2  -- O4  = 1.6277 Angstrom
      mean = 1.7102 Angstrom

        T-O SUMMARY
          Range  = 1.6024 A <--> 1.8945 A
          Mean   = 1.6726 A
          StdDev = 0.0970 A

       t1 Range  = 0.0389 <-- 0.0195 --> 0.0389
       t2 Range  = 0.0269 <-- 0.0135 --> 0.0269

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O4  = 114.730 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 105.863 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 107.273 deg; O2  -- O1  = 3 A
O4  -- T1  -- O3  = 107.814 deg; O4  -- O3  = 3 A
O4  -- T1  -- O1  = 113.455 deg; O4  -- O1  = 3 A
O3  -- T1  -- O1  = 107.201 deg; O3  -- O1  = 3 A
       105.863 deg <-- 109.389 deg --> 114.730 deg

O3  -- T2  -- O4  =  97.147 deg; O3  -- O4  = 2 A
O3  -- T2  -- O4  = 106.220 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 103.651 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 128.256 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 100.070 deg; O3  -- O4  = 2 A
O4  -- T2  -- O4  = 123.754 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  =  16.137 deg; O4  -- O4  = 1 A
O4  -- T2  -- O3  = 100.070 deg; O4  -- O3  = 2 A
O4  -- T2  -- O4  = 139.891 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 107.617 deg; O4  -- O4  = 3 A
O4  -- T2  -- O3  = 103.651 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  =  16.137 deg; O4  -- O4  = 1 A
O4  -- T2  -- O3  = 106.220 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 123.754 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  =  97.147 deg; O3  -- O4  = 2 A
       16.137 deg <-- 97.981 deg --> 139.891 deg

        O-T-O SUMMARY
          Range  = 16.1372 deg <--> 139.8911 deg
          Mean   = 101.0938 deg
          StdDev = 29.9772 deg

        O--O SUMMARY
          Range  = 0.5605 A <--> 3.1089 A
          Mean   = 2.5408 A
          StdDev = 0.6858 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2047 A

T1  -- O2  -- T1  = 128.802 deg ; T1  -- T1   2.9760 A

T1  -- O3  -- T2  = 147.573 deg ; T1  -- T2   3.0996 A

T1  -- O4  -- T2  = 162.000 deg ; T1  -- T2   3.5559 A
T1  -- O4  -- T2  = 108.320 deg ; T1  -- T2   2.7025 A
T2  -- O4  -- T2  =  56.246 deg ; T2  -- T2   1.6768 A


        T-O-T SUMMARY
          Range  = 56.2461° <--> 180.0000 deg
          Mean   = 137.2396 deg
          StdDev = 35.4001 deg

        T--T SUMMARY
          Range  = 1.6768 A <--> 3.5559 A
          Mean   = 2.9777 A
          StdDev = 0.4961 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O4  = 0.5605 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1852 Angstrom
  T1  -- T2  = 2.7025 Angstrom
  T1  -- T2  = 3.0996 Angstrom
  T1  -- T1  = 2.9760 Angstrom
  T1  -- T1  = 3.2047 Angstrom
T2  -- T1  = 2.7025 Angstrom
T2  -- T2  = 1.6768 Angstrom
T2  -- T1  = 2.7025 Angstrom