Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_30256_Y07oCi.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.56 T-atoms per nm^3
Material density = 2.351 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6069 Angstrom
T1  -- O2  = 1.6787 Angstrom
T1  -- O4  = 1.6712 Angstrom
T1  -- O3  = 1.6434 Angstrom
      mean = 1.6500 Angstrom
        t1 = 0.054561  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.054959  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6151 Angstrom
T2  -- O4  = 1.6141 Angstrom
T2  -- O3  = 1.6151 Angstrom
T2  -- O4  = 1.6141 Angstrom
      mean = 1.6146 Angstrom
        t1 = 0.095843  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.102663  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6069 A <--> 1.6787 A
          Mean   = 1.6382 A
          StdDev = 0.0287 A

       t1 Range  = 0.0546 <-- 0.0752 --> 0.0958
       t2 Range  = 0.0550 <-- 0.0788 --> 0.1027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 114.665 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  =  99.126 deg; O1  -- O4  = 2 A
O1  -- T1  -- O3  = 108.097 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 120.381 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 103.624 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 110.680 deg; O4  -- O3  = 3 A
       99.126 deg <-- 109.429 deg --> 120.381 deg

O3  -- T2  -- O4  =  99.918 deg; O3  -- O4  = 2 A
O3  -- T2  -- O3  = 133.514 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  =  97.171 deg; O3  -- O4  = 2 A
O4  -- T2  -- O3  =  97.171 deg; O4  -- O3  = 2 A
O4  -- T2  -- O4  = 135.782 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  =  99.918 deg; O3  -- O4  = 2 A
       97.171 deg <-- 110.579 deg --> 135.782 deg

        O-T-O SUMMARY
          Range  = 97.1706 deg <--> 135.7816 deg
          Mean   = 109.8011 deg
          StdDev = 13.3630 deg

        O--O SUMMARY
          Range  = 2.4217 A <--> 2.9909 A
          Mean   = 2.6522 A
          StdDev = 0.2073 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.073 deg; T1  -- T2  = 4.4026 A
T1  - O1  - T1  - O4  - T1  = 127.890 deg; T1  -- T1  = 5.6594 A
T1  - O1  - T1  - O3  - T2  = 110.076 deg; T1  -- T2  = 5.1748 A
T2  - O2  - T1  - O4  - T1  =  97.102 deg; T2  -- T1  = 4.6075 A
T2  - O2  - T1  - O3  - T2  =  93.686 deg; T2  -- T2  = 4.4948 A
T1  - O4  - T1  - O3  - T2  = 120.968 deg; T1  -- T2  = 5.3829 A

T1  - O3  - T2  - O4  - T1  = 101.043 deg; T1  -- T1  = 4.7559 A
T1  - O3  - T2  - O3  - T1  = 118.063 deg; T1  -- T1  = 5.3163 A
T1  - O3  - T2  - O4  - T1  =  86.314 deg; T1  -- T1  = 4.2146 A
T1  - O4  - T2  - O3  - T1  =  86.314 deg; T1  -- T1  = 4.2146 A
T1  - O4  - T2  - O4  - T1  = 165.795 deg; T1  -- T1  = 6.0760 A
T1  - O3  - T2  - O4  - T1  = 101.043 deg; T1  -- T1  = 4.7559 A

        T-T-T SUMMARY
          Range  = 86.3139 deg <--> 165.7950 deg
          Mean   = 108.9418 deg
          StdDev = 22.0680 deg

        T--T SUMMARY
          Range  = 4.2146 A <--> 6.0760 A
          Mean   = 4.9438 A
          StdDev = 0.5760 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2138 A

T1  -- O2  -- T1  = 133.576 deg ; T1  -- T1   3.0856 A

T1  -- O3  -- T2  = 139.946 deg ; T1  -- T2   3.0615 A

T1  -- O4  -- T2  = 141.329 deg ; T1  -- T2   3.1001 A


        T-O-T SUMMARY
          Range  = 133.5757° <--> 180.0000 deg
          Mean   = 148.7128 deg
          StdDev = 18.5916 deg

        T--T SUMMARY
          Range  = 3.0615 A <--> 3.2138 A
          Mean   = 3.1152 A
          StdDev = 0.0595 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 42 65 93 125 163 207 255 308 366 429 498 572 650
TD10 = 990
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 27
Vertex symbol  = 4.8_{8}.6.6.6.6
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 42 64 90 126 166 206 252 306 368 432 496 568 650
TD10 = 985
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 988.333
Average ring size = 6.4000