Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_30253_dZK08x.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 21.90 T-atoms per nm^3
Material density = 2.185 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6136 Angstrom
T1  -- O2  = 1.6240 Angstrom
T1  -- O3  = 1.6144 Angstrom
T1  -- O4  = 1.6182 Angstrom
      mean = 1.6176 Angstrom
        t1 = 0.004932  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000978  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6183 Angstrom
T2  -- O4  = 1.6198 Angstrom
T2  -- O3  = 1.6183 Angstrom
T2  -- O4  = 1.6198 Angstrom
      mean = 1.6190 Angstrom
        t1 = 0.007374  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006175  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6136 A <--> 1.6240 A
          Mean   = 1.6181 A
          StdDev = 0.0035 A

       t1 Range  = 0.0049 <-- 0.0062 --> 0.0074
       t2 Range  = 0.0010 <-- 0.0036 --> 0.0062

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.687 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.788 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.678 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.866 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.004 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.800 deg; O3  -- O4  = 3 A
       108.866 deg <-- 109.470 deg --> 109.800 deg

O3  -- T2  -- O4  = 109.416 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 108.174 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 110.367 deg; O3  -- O4  = 3 A
O4  -- T2  -- O3  = 110.367 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 109.092 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  = 109.416 deg; O3  -- O4  = 3 A
       108.174 deg <-- 109.472 deg --> 110.367 deg

        O-T-O SUMMARY
          Range  = 108.1744 deg <--> 110.3671 deg
          Mean   = 109.4618 deg
          StdDev = 0.6145 deg

        O--O SUMMARY
          Range  = 2.6213 A <--> 2.6584 A
          Mean   = 2.6424 A
          StdDev = 0.0097 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  95.273 deg; T1  -- T2  = 4.6742 A
T1  - O1  - T1  - O3  - T1  = 133.562 deg; T1  -- T1  = 5.6907 A
T1  - O1  - T1  - O4  - T2  = 104.593 deg; T1  -- T2  = 4.9810 A
T2  - O2  - T1  - O3  - T1  = 109.684 deg; T2  -- T1  = 4.9565 A
T2  - O2  - T1  - O4  - T2  =  92.064 deg; T2  -- T2  = 4.4371 A
T1  - O3  - T1  - O4  - T2  = 112.639 deg; T1  -- T2  = 5.0191 A

T1  - O3  - T2  - O4  - T1  = 107.177 deg; T1  -- T1  = 4.9614 A
T1  - O3  - T2  - O3  - T1  = 140.631 deg; T1  -- T1  = 5.8333 A
T1  - O3  - T2  - O4  - T1  =  87.936 deg; T1  -- T1  = 4.2800 A
T1  - O4  - T2  - O3  - T1  =  87.936 deg; T1  -- T1  = 4.2800 A
T1  - O4  - T2  - O4  - T1  = 134.723 deg; T1  -- T1  = 5.6617 A
T1  - O3  - T2  - O4  - T1  = 107.177 deg; T1  -- T1  = 4.9614 A

        T-T-T SUMMARY
          Range  = 87.9355 deg <--> 140.6313 deg
          Mean   = 110.0660 deg
          StdDev = 17.6925 deg

        T--T SUMMARY
          Range  = 4.2800 A <--> 5.8333 A
          Mean   = 4.9912 A
          StdDev = 0.5153 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2272 A

T1  -- O2  -- T1  = 131.720 deg ; T1  -- T1   2.9640 A

T1  -- O3  -- T2  = 146.765 deg ; T1  -- T2   3.0977 A

T1  -- O4  -- T2  = 142.612 deg ; T1  -- T2   3.0671 A


        T-O-T SUMMARY
          Range  = 131.7196° <--> 180.0000 deg
          Mean   = 150.2741 deg
          StdDev = 18.3086 deg

        T--T SUMMARY
          Range  = 2.9640 A <--> 3.2272 A
          Mean   = 3.0890 A
          StdDev = 0.0954 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 42 65 93 125 163 207 255 308 366 429 498 572 650
TD10 = 990
Circuit symbol = 4.8_{8}.6.6.6.6
Weight = 27
Vertex symbol  = 4.8_{8}.6.6.6.6
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 24 42 64 90 126 166 206 252 306 368 432 496 568 650
TD10 = 985
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 988.333
Average ring size = 6.4000