Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_28222_WyrIkv.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 20.44 T-atoms per nm^3
Material density = 2.040 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6208 Angstrom
T1  -- O2  = 1.6204 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6207 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.006732  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000853  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6209 Angstrom
T2  -- O3  = 1.6209 Angstrom
T2  -- O4  = 1.6209 Angstrom
T2  -- O4  = 1.6209 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.006766  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000233  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6204 A <--> 1.6211 A
          Mean   = 1.6208 A
          StdDev = 0.0002 A

       t1 Range  = 0.0067 <-- 0.0067 --> 0.0068
       t2 Range  = 0.0002 <-- 0.0005 --> 0.0009

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.370 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.621 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.375 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.596 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.309 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.555 deg; O3  -- O4  = 3 A
       109.309 deg <-- 109.471 deg --> 109.621 deg

O3  -- T2  -- O3  = 109.365 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 109.494 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.519 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.519 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.494 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 109.438 deg; O4  -- O4  = 3 A
       109.365 deg <-- 109.471 deg --> 109.519 deg

        O-T-O SUMMARY
          Range  = 109.3093 deg <--> 109.6208 deg
          Mean   = 109.4756 deg
          StdDev = 0.0954 deg

        O--O SUMMARY
          Range  = 2.6437 A <--> 2.6495 A
          Mean   = 2.6469 A
          StdDev = 0.0017 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 109.126 deg; T2  -- T1  = 4.9738 A
T2  - O1  - T1  - O3  - T1  =  99.863 deg; T2  -- T1  = 4.6464 A
T2  - O1  - T1  - O4  - T2  =  87.265 deg; T2  -- T2  = 4.1891 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3128 A
T1  - O2  - T1  - O4  - T2  = 127.316 deg; T1  -- T2  = 5.4653 A
T1  - O3  - T1  - O4  - T2  = 137.496 deg; T1  -- T2  = 5.6530 A

T1  - O3  - T2  - O3  - T1  = 141.748 deg; T1  -- T1  = 5.7416 A
T1  - O3  - T2  - O4  - T1  = 110.458 deg; T1  -- T1  = 4.9869 A
T1  - O3  - T2  - O4  - T1  =  92.735 deg; T1  -- T1  = 4.3941 A
T1  - O3  - T2  - O4  - T1  =  92.735 deg; T1  -- T1  = 4.3941 A
T1  - O3  - T2  - O4  - T1  = 110.458 deg; T1  -- T1  = 4.9869 A
T1  - O4  - T2  - O4  - T1  = 105.367 deg; T1  -- T1  = 4.8234 A

        T-T-T SUMMARY
          Range  = 87.2645 deg <--> 141.7477 deg
          Mean   = 108.6962 deg
          StdDev = 17.9922 deg

        T--T SUMMARY
          Range  = 4.1891 A <--> 5.7416 A
          Mean   = 4.8766 A
          StdDev = 0.5168 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.656 deg ; T1  -- T1   3.0330 A

T1  -- O2  -- T1  = 142.208 deg ; T1  -- T1   3.0661 A

T1  -- O3  -- T2  = 139.188 deg ; T1  -- T2   3.0385 A

T1  -- O4  -- T2  = 138.614 deg ; T1  -- T2   3.0325 A


        T-O-T SUMMARY
          Range  = 138.6136° <--> 142.2079 deg
          Mean   = 139.6664 deg
          StdDev = 1.5084 deg

        T--T SUMMARY
          Range  = 3.0325 A <--> 3.0661 A
          Mean   = 3.0425 A
          StdDev = 0.0140 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 162 194 224 252 278 302 324 344
TD10 = 781
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 162 194 224 252 278 302 324 344
TD10 = 781
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 781.000
Average ring size = 5.1429