Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_27131_8aRwyw.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.93 T-atoms per nm^3
Material density = 1.789 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6158 Angstrom
T1  -- O3  = 1.6152 Angstrom
T1  -- O4  = 1.6154 Angstrom
      mean = 1.6155 Angstrom
        t1 = 0.004444  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002424  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6149 Angstrom
T2  -- O5  = 1.6158 Angstrom
T2  -- O6  = 1.6152 Angstrom
T2  -- O4  = 1.6154 Angstrom
      mean = 1.6153 Angstrom
        t1 = 0.004322  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001782  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6149 A <--> 1.6158 A
          Mean   = 1.6154 A
          StdDev = 0.0003 A

       t1 Range  = 0.0043 <-- 0.0044 --> 0.0044
       t2 Range  = 0.0018 <-- 0.0021 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.460 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.054 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.009 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.455 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.416 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.430 deg; O3  -- O4  = 3 A
       109.009 deg <-- 109.471 deg --> 110.430 deg

O3  -- T2  -- O5  = 109.026 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.421 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 110.424 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.469 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.063 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.420 deg; O6  -- O4  = 3 A
       109.026 deg <-- 109.471 deg --> 110.424 deg

        O-T-O SUMMARY
          Range  = 109.0090 deg <--> 110.4296 deg
          Mean   = 109.4712 deg
          StdDev = 0.4878 deg

        O--O SUMMARY
          Range  = 2.6306 A <--> 2.6532 A
          Mean   = 2.6379 A
          StdDev = 0.0078 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 110.125 deg; T2  -- T1  = 5.2115 A
T2  - O1  - T1  - O3  - T1  = 120.790 deg; T2  -- T1  = 5.5272 A
T2  - O1  - T1  - O4  - T2  =  83.215 deg; T2  -- T2  = 4.1505 A
T1  - O2  - T1  - O3  - T1  = 109.424 deg; T1  -- T1  = 5.2756 A
T1  - O2  - T1  - O4  - T2  = 110.124 deg; T1  -- T2  = 5.2116 A
T1  - O3  - T1  - O4  - T2  = 120.757 deg; T1  -- T2  = 5.5264 A

T1  - O3  - T2  - O5  - T2  = 120.729 deg; T1  -- T2  = 5.5255 A
T1  - O3  - T2  - O6  - T1  =  83.188 deg; T1  -- T1  = 4.1494 A
T1  - O3  - T2  - O4  - T2  = 110.125 deg; T1  -- T2  = 5.2106 A
T2  - O5  - T2  - O6  - T1  = 120.812 deg; T2  -- T1  = 5.5279 A
T2  - O5  - T2  - O4  - T2  = 109.446 deg; T2  -- T2  = 5.2754 A
T1  - O6  - T2  - O4  - T2  = 110.124 deg; T1  -- T2  = 5.2106 A

        T-T-T SUMMARY
          Range  = 83.1876 deg <--> 120.8121 deg
          Mean   = 108.4900 deg
          StdDev = 12.9281 deg

        T--T SUMMARY
          Range  = 4.1494 A <--> 5.5279 A
          Mean   = 5.1302 A
          StdDev = 0.4830 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2316 A

T1  -- O2  -- T1  = 179.928 deg ; T1  -- T1   3.2316 A

T1  -- O3  -- T2  = 150.718 deg ; T1  -- T2   3.1252 A

T1  -- O4  -- T2  = 150.639 deg ; T1  -- T2   3.1253 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2316 A

T2  -- O6  -- T2  = 179.935 deg ; T2  -- T2   3.2304 A


        T-O-T SUMMARY
          Range  = 150.6393° <--> 180.0000 deg
          Mean   = 170.2034 deg
          StdDev = 13.9521 deg

        T--T SUMMARY
          Range  = 3.1252 A <--> 3.2316 A
          Mean   = 3.1960 A
          StdDev = 0.0505 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391