Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_27050_ogIP3l.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.49 T-atoms per nm^3
Material density = 1.646 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6157 Angstrom
T1  -- O2  = 1.6171 Angstrom
T1  -- O4  = 1.6203 Angstrom
T1  -- O3  = 1.6170 Angstrom
      mean = 1.6175 Angstrom
        t1 = 0.005942  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002750  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6168 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O5  = 1.6154 Angstrom
T2  -- O6  = 1.6180 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005404  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002211  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6213 A
          Mean   = 1.6177 A
          StdDev = 0.0020 A

       t1 Range  = 0.0054 <-- 0.0057 --> 0.0059
       t2 Range  = 0.0022 <-- 0.0025 --> 0.0027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.180 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.807 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 108.673 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.144 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 110.449 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.576 deg; O4  -- O3  = 3 A
       108.673 deg <-- 109.471 deg --> 110.449 deg

O3  -- T2  -- O4  = 109.521 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.222 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.736 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.221 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.921 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.202 deg; O5  -- O6  = 3 A
       109.202 deg <-- 109.471 deg --> 109.921 deg

        O-T-O SUMMARY
          Range  = 108.6731 deg <--> 110.4485 deg
          Mean   = 109.4964 deg
          StdDev = 0.4594 deg

        O--O SUMMARY
          Range  = 2.6265 A <--> 2.6565 A
          Mean   = 2.6423 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  89.993 deg; T2  -- T1  = 4.3682 A
T2  - O1  - T1  - O4  - T1  = 130.502 deg; T2  -- T1  = 5.6819 A
T2  - O1  - T1  - O3  - T2  =  90.021 deg; T2  -- T2  = 4.3326 A
T1  - O2  - T1  - O4  - T1  = 121.942 deg; T1  -- T1  = 5.5820 A
T1  - O2  - T1  - O3  - T2  =  89.993 deg; T1  -- T2  = 4.4219 A
T1  - O4  - T1  - O3  - T2  = 123.097 deg; T1  -- T2  = 5.5683 A

T2  - O3  - T2  - O4  - T1  = 129.927 deg; T2  -- T1  = 5.6680 A
T2  - O3  - T2  - O5  - T2  = 121.966 deg; T2  -- T2  = 5.5813 A
T2  - O3  - T2  - O6  - T1  = 123.702 deg; T2  -- T1  = 5.5835 A
T1  - O4  - T2  - O5  - T2  =  90.007 deg; T1  -- T2  = 4.3682 A
T1  - O4  - T2  - O6  - T1  =  89.979 deg; T1  -- T1  = 4.3311 A
T2  - O5  - T2  - O6  - T1  =  90.007 deg; T2  -- T1  = 4.4219 A

        T-T-T SUMMARY
          Range  = 89.9794 deg <--> 130.5025 deg
          Mean   = 109.1942 deg
          StdDev = 17.8251 deg

        T--T SUMMARY
          Range  = 4.3311 A <--> 5.6819 A
          Mean   = 5.0467 A
          StdDev = 0.6230 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2315 A

T1  -- O2  -- T1  = 154.148 deg ; T1  -- T1   3.1523 A

T1  -- O3  -- T2  = 147.085 deg ; T1  -- T2   3.1014 A

T1  -- O4  -- T2  = 137.809 deg ; T1  -- T2   3.0243 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2308 A

T2  -- O6  -- T2  = 153.758 deg ; T2  -- T2   3.1515 A


        T-O-T SUMMARY
          Range  = 137.8092° <--> 180.0000 deg
          Mean   = 158.8000 deg
          StdDev = 16.1050 deg

        T--T SUMMARY
          Range  = 3.0243 A <--> 3.2315 A
          Mean   = 3.1486 A
          StdDev = 0.0730 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

<TD10> = 787.000
Average ring size = 6.0000