Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_26604_lT0AUr.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.09 T-atoms per nm^3
Material density = 2.104 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6202 Angstrom
T1  -- O2  = 1.6217 Angstrom
T1  -- O3  = 1.6231 Angstrom
T1  -- O4  = 1.6215 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.007345  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001652  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6209 Angstrom
T2  -- O3  = 1.6208 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O5  = 1.6218 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007042  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000785  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6202 A <--> 1.6231 A
          Mean   = 1.6214 A
          StdDev = 0.0008 A

       t1 Range  = 0.0070 <-- 0.0072 --> 0.0073
       t2 Range  = 0.0008 <-- 0.0012 --> 0.0017

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.204 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.825 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.558 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.521 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.232 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.486 deg; O3  -- O4  = 3 A
       109.204 deg <-- 109.471 deg --> 109.825 deg

O2  -- T2  -- O3  = 109.309 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.601 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.509 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.259 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.672 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.478 deg; O4  -- O5  = 3 A
       109.259 deg <-- 109.471 deg --> 109.672 deg

        O-T-O SUMMARY
          Range  = 109.2037 deg <--> 109.8250 deg
          Mean   = 109.4710 deg
          StdDev = 0.1822 deg

        O--O SUMMARY
          Range  = 2.6426 A <--> 2.6539 A
          Mean   = 2.6478 A
          StdDev = 0.0033 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  82.691 deg; T2  -- T2  = 3.9822 A
T2  - O1  - T1  - O3  - T1  = 142.895 deg; T2  -- T1  = 5.8076 A
T2  - O1  - T1  - O4  - T2  =  96.892 deg; T2  -- T2  = 4.5180 A
T2  - O2  - T1  - O3  - T1  =  92.835 deg; T2  -- T1  = 4.4284 A
T2  - O2  - T1  - O4  - T2  = 110.606 deg; T2  -- T2  = 4.9529 A
T1  - O3  - T1  - O4  - T2  = 118.868 deg; T1  -- T2  = 5.2715 A

T1  - O2  - T2  - O3  - T1  =  97.309 deg; T1  -- T1  = 4.5255 A
T1  - O2  - T2  - O4  - T2  = 118.243 deg; T1  -- T2  = 5.1756 A
T1  - O2  - T2  - O5  - T1  =  83.108 deg; T1  -- T1  = 4.0047 A
T1  - O3  - T2  - O4  - T2  = 119.918 deg; T1  -- T2  = 5.2088 A
T1  - O3  - T2  - O5  - T1  = 110.606 deg; T1  -- T1  = 4.9529 A
T2  - O4  - T2  - O5  - T1  = 119.816 deg; T2  -- T1  = 5.2142 A

        T-T-T SUMMARY
          Range  = 82.6910 deg <--> 142.8947 deg
          Mean   = 107.8156 deg
          StdDev = 17.0777 deg

        T--T SUMMARY
          Range  = 3.9822 A <--> 5.8076 A
          Mean   = 4.8369 A
          StdDev = 0.5305 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 146.789 deg ; T1  -- T1   3.1052 A

T1  -- O2  -- T2  = 137.355 deg ; T1  -- T2   3.0206 A

T1  -- O3  -- T2  = 136.864 deg ; T1  -- T2   3.0167 A

T1  -- O4  -- T2  = 136.070 deg ; T1  -- T2   3.0074 A

T2  -- O5  -- T2  = 136.209 deg ; T2  -- T2   3.0097 A


        T-O-T SUMMARY
          Range  = 136.0697° <--> 146.7893 deg
          Mean   = 138.6573 deg
          StdDev = 4.1444 deg

        T--T SUMMARY
          Range  = 3.0074 A <--> 3.1052 A
          Mean   = 3.0319 A
          StdDev = 0.0374 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 833.000
Average ring size = 5.3333