Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_23360_TmuPGi.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 20.93 T-atoms per nm^3
Material density = 2.088 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6594 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.7502 Angstrom
T1  -- O4  = 1.6835 Angstrom
      mean = 1.6784 Angstrom
        t1 = 0.075839  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.062461  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6253 Angstrom
T2  -- O4  = 1.6368 Angstrom
T2  -- O5  = 1.6176 Angstrom
T2  -- O6  = 1.3612 Angstrom
      mean = 1.5602 Angstrom
        t1 = 0.150465  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.118458  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.3612 A <--> 1.7502 A
          Mean   = 1.6193 A
          StdDev = 0.1068 A

       t1 Range  = 0.0758 <-- 0.1132 --> 0.1505
       t2 Range  = 0.0625 <-- 0.0905 --> 0.1185

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.785 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.320 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  95.975 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 105.978 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.573 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 119.329 deg; O3  -- O4  = 3 A
       95.975 deg <-- 109.327 deg --> 119.329 deg

O3  -- T2  -- O4  = 122.938 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 116.420 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  85.282 deg; O3  -- O6  = 2 A
O4  -- T2  -- O5  = 120.641 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  =  84.549 deg; O4  -- O6  = 2 A
O5  -- T2  -- O6  = 100.705 deg; O5  -- O6  = 2 A
       84.549 deg <-- 105.089 deg --> 122.938 deg

        O-T-O SUMMARY
          Range  = 84.5494 deg <--> 122.9384 deg
          Mean   = 107.5227 deg
          StdDev = 13.3916 deg

        O--O SUMMARY
          Range  = 2.0270 A <--> 2.9637 A
          Mean   = 2.6129 A
          StdDev = 0.3210 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  98.147 deg; T2  -- T1  = 4.5682 A
T2  - O1  - T1  - O3  - T2  =  84.464 deg; T2  -- T2  = 3.8958 A
T2  - O1  - T1  - O4  - T1  = 137.880 deg; T2  -- T1  = 5.5581 A
T1  - O2  - T1  - O3  - T2  = 107.628 deg; T1  -- T2  = 5.1047 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.5882 A
T2  - O3  - T1  - O4  - T1  = 132.117 deg; T2  -- T1  = 5.7099 A

T1  - O3  - T2  - O4  - T2  = 107.469 deg; T1  -- T2  = 4.8318 A
T1  - O3  - T2  - O5  - T2  = 122.279 deg; T1  -- T2  = 4.7899 A
T1  - O3  - T2  - O6  - T1  =  95.536 deg; T1  -- T1  = 4.2895 A
T2  - O4  - T2  - O5  - T2  = 100.705 deg; T2  -- T2  = 4.5990 A
T2  - O4  - T2  - O6  - T1  = 131.318 deg; T2  -- T1  = 5.7185 A
T2  - O5  - T2  - O6  - T1  = 102.073 deg; T2  -- T1  = 4.4854 A

        T-T-T SUMMARY
          Range  = 84.4641 deg <--> 137.8801 deg
          Mean   = 109.9550 deg
          StdDev = 17.5068 deg

        T--T SUMMARY
          Range  = 3.8958 A <--> 5.7185 A
          Mean   = 4.8738 A
          StdDev = 0.5689 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 162.876 deg ; T1  -- T1   3.2817 A

T1  -- O2  -- T1  = 163.159 deg ; T1  -- T1   3.2066 A

T1  -- O3  -- T2  = 108.868 deg ; T1  -- T2   2.7467 A

T1  -- O4  -- T2  = 132.611 deg ; T1  -- T2   3.0405 A

T2  -- O5  -- T2  = 179.845 deg ; T2  -- T2   3.2353 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   2.7224 A


        T-O-T SUMMARY
          Range  = 108.8680° <--> 180.0000 deg
          Mean   = 154.5599 deg
          StdDev = 26.0904 deg

        T--T SUMMARY
          Range  = 2.7224 A <--> 3.2817 A
          Mean   = 3.0389 A
          StdDev = 0.2301 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O6  = 2.0324 A
O4  -- O6  = 2.0270 A
O5  -- O6  = 2.2995 A
O5  -- O6  = 2.2995 A
T1  -- T2  = 2.7467 Angstrom
T2  -- T1  = 2.7467 Angstrom
T2  -- T2  = 2.7224 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 39 61 89 118 153 198 241 287 349 409 465 541 619
TD10 = 936
Circuit symbol = 4.4.5.7.5.7
Weight = 11
Vertex symbol  = 4.4.5.8_{2}.5.8_{2}
Weight = 27

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 61 88 120 155 192 241 295 344 404 473 539 613
TD10 = 934
Circuit symbol = 4.5.5.5.7.7
Weight = 12
Vertex symbol  = 4.5.5.5.8.8
Weight = 21

<TD10> = 935.000
Average ring size = 5.6000