Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_23339_MMw9xl.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.68 T-atoms per nm^3
Material density = 2.163 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6140 Angstrom
T1  -- O2  = 1.6055 Angstrom
T1  -- O3  = 1.6177 Angstrom
T1  -- O4  = 1.6451 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.028502  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017553  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6153 Angstrom
T2  -- O4  = 1.6151 Angstrom
T2  -- O5  = 1.6217 Angstrom
T2  -- O6  = 1.6473 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.045774  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042960  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6055 A <--> 1.6473 A
          Mean   = 1.6227 A
          StdDev = 0.0143 A

       t1 Range  = 0.0285 <-- 0.0371 --> 0.0458
       t2 Range  = 0.0176 <-- 0.0303 --> 0.0430

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.989 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.619 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.719 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 102.582 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.667 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 116.072 deg; O3  -- O4  = 3 A
       102.582 deg <-- 109.441 deg --> 116.072 deg

O3  -- T2  -- O4  =  98.905 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 101.624 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.561 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 113.786 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 116.564 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 113.989 deg; O5  -- O6  = 3 A
       98.905 deg <-- 109.072 deg --> 116.564 deg

        O-T-O SUMMARY
          Range  = 98.9050 deg <--> 116.5642 deg
          Mean   = 109.0080 deg
          StdDev = 5.6061 deg

        O--O SUMMARY
          Range  = 2.4547 A <--> 2.7752 A
          Mean   = 2.6396 A
          StdDev = 0.1020 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  97.992 deg; T2  -- T2  = 4.6736 A
T2  - O1  - T1  - O3  - T1  = 101.121 deg; T2  -- T1  = 4.9621 A
T2  - O1  - T1  - O4  - T1  =  91.702 deg; T2  -- T1  = 4.3098 A
T2  - O2  - T1  - O3  - T1  = 123.590 deg; T2  -- T1  = 5.4832 A
T2  - O2  - T1  - O4  - T1  = 141.863 deg; T2  -- T1  = 5.4721 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2706 A

T1  - O3  - T2  - O4  - T1  =  82.008 deg; T1  -- T1  = 4.0645 A
T1  - O3  - T2  - O5  - T2  =  92.971 deg; T1  -- T2  = 4.5459 A
T1  - O3  - T2  - O6  - T2  =  88.298 deg; T1  -- T2  = 4.3098 A
T1  - O4  - T2  - O5  - T2  = 127.115 deg; T1  -- T2  = 5.4287 A
T1  - O4  - T2  - O6  - T2  = 141.863 deg; T1  -- T2  = 5.6512 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2828 A

        T-T-T SUMMARY
          Range  = 82.0082 deg <--> 141.8626 deg
          Mean   = 106.7752 deg
          StdDev = 21.4935 deg

        T--T SUMMARY
          Range  = 4.0645 A <--> 5.6512 A
          Mean   = 4.8160 A
          StdDev = 0.5729 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.443 deg ; T1  -- T1   3.2277 A

T1  -- O2  -- T1  = 121.120 deg ; T1  -- T1   2.7965 A

T1  -- O3  -- T2  = 162.966 deg ; T1  -- T2   3.1974 A

T1  -- O4  -- T2  = 133.276 deg ; T1  -- T2   2.9930 A

T2  -- O5  -- T2  = 142.357 deg ; T2  -- T2   3.0699 A

T2  -- O6  -- T2  = 130.034 deg ; T2  -- T2   2.9863 A


        T-O-T SUMMARY
          Range  = 121.1205° <--> 178.4433 deg
          Mean   = 144.6995 deg
          StdDev = 20.1245 deg

        T--T SUMMARY
          Range  = 2.7965 A <--> 3.2277 A
          Mean   = 3.0451 A
          StdDev = 0.1460 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7965 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000