Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_23314_CBt_fd.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.58 T-atoms per nm^3
Material density = 1.754 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6174 Angstrom
T1  -- O2  = 1.6202 Angstrom
T1  -- O3  = 1.6267 Angstrom
T1  -- O4  = 1.6135 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006888  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002319  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6451 Angstrom
T2  -- O4  = 1.6112 Angstrom
T2  -- O5  = 1.6196 Angstrom
T2  -- O6  = 1.6256 Angstrom
      mean = 1.6254 Angstrom
        t1 = 0.016006  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018168  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6112 A <--> 1.6451 A
          Mean   = 1.6224 A
          StdDev = 0.0100 A

       t1 Range  = 0.0069 <-- 0.0114 --> 0.0160
       t2 Range  = 0.0023 <-- 0.0102 --> 0.0182

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.892 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.104 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.089 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.439 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.485 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.819 deg; O3  -- O4  = 3 A
       108.485 deg <-- 109.471 deg --> 110.089 deg

O3  -- T2  -- O4  = 108.715 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 112.991 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.516 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 107.781 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.040 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 108.781 deg; O5  -- O6  = 3 A
       107.781 deg <-- 109.471 deg --> 112.991 deg

        O-T-O SUMMARY
          Range  = 107.7809 deg <--> 112.9913 deg
          Mean   = 109.4833 deg
          StdDev = 1.3215 deg

        O--O SUMMARY
          Range  = 2.6102 A <--> 2.7223 A
          Mean   = 2.6497 A
          StdDev = 0.0265 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  86.810 deg; T2  -- T2  = 4.1539 A
T2  - O1  - T1  - O3  - T1  = 141.225 deg; T2  -- T1  = 5.4164 A
T2  - O1  - T1  - O4  - T1  =  88.170 deg; T2  -- T1  = 4.1277 A
T2  - O2  - T1  - O3  - T1  = 123.498 deg; T2  -- T1  = 5.3433 A
T2  - O2  - T1  - O4  - T1  = 127.644 deg; T2  -- T1  = 5.6097 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2144 A

T1  - O3  - T2  - O4  - T1  =  93.190 deg; T1  -- T1  = 4.3905 A
T1  - O3  - T2  - O5  - T2  = 142.424 deg; T1  -- T2  = 5.7616 A
T1  - O3  - T2  - O6  - T2  =  91.830 deg; T1  -- T2  = 4.1277 A
T1  - O4  - T2  - O5  - T2  = 114.875 deg; T1  -- T2  = 5.3994 A
T1  - O4  - T2  - O6  - T2  = 127.644 deg; T1  -- T2  = 5.4472 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3321 A

        T-T-T SUMMARY
          Range  = 86.8098 deg <--> 142.4237 deg
          Mean   = 111.7187 deg
          StdDev = 20.9665 deg

        T--T SUMMARY
          Range  = 4.1277 A <--> 5.7616 A
          Mean   = 4.9164 A
          StdDev = 0.6516 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.227 deg ; T1  -- T1   2.8851 A

T1  -- O2  -- T1  = 142.886 deg ; T1  -- T1   3.0720 A

T1  -- O3  -- T2  = 121.659 deg ; T1  -- T2   2.8569 A

T1  -- O4  -- T2  = 160.605 deg ; T1  -- T2   3.1786 A

T2  -- O5  -- T2  = 170.321 deg ; T2  -- T2   3.2277 A

T2  -- O6  -- T2  = 125.425 deg ; T2  -- T2   2.8895 A


        T-O-T SUMMARY
          Range  = 121.6593° <--> 170.3212 deg
          Mean   = 141.1872 deg
          StdDev = 18.8265 deg

        T--T SUMMARY
          Range  = 2.8569 A <--> 3.2277 A
          Mean   = 3.0183 A
          StdDev = 0.1504 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 307 340 370 403
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 306 339 370 401
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000