Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_23291_2OPZDI.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.07 T-atoms per nm^3
Material density = 2.202 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6181 Angstrom
T1  -- O2  = 1.6200 Angstrom
T1  -- O3  = 1.6269 Angstrom
T1  -- O4  = 1.6180 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.008364  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004010  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6279 Angstrom
T2  -- O4  = 1.6197 Angstrom
T2  -- O5  = 1.6128 Angstrom
T2  -- O6  = 1.6279 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.009271  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003463  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6128 A <--> 1.6279 A
          Mean   = 1.6214 A
          StdDev = 0.0052 A

       t1 Range  = 0.0084 <-- 0.0088 --> 0.0093
       t2 Range  = 0.0035 <-- 0.0037 --> 0.0040

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.573 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.670 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.092 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.009 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.408 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.070 deg; O3  -- O4  = 3 A
       108.670 deg <-- 109.470 deg --> 111.070 deg

O3  -- T2  -- O4  = 108.657 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.739 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.040 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 108.762 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.903 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.722 deg; O5  -- O6  = 3 A
       108.657 deg <-- 109.470 deg --> 110.903 deg

        O-T-O SUMMARY
          Range  = 108.6568 deg <--> 111.0701 deg
          Mean   = 109.4542 deg
          StdDev = 0.8061 deg

        O--O SUMMARY
          Range  = 2.6277 A <--> 2.6753 A
          Mean   = 2.6477 A
          StdDev = 0.0146 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 114.340 deg; T2  -- T2  = 5.0359 A
T2  - O1  - T1  - O3  - T1  =  83.832 deg; T2  -- T1  = 4.1209 A
T2  - O1  - T1  - O4  - T1  =  90.680 deg; T2  -- T1  = 4.1021 A
T2  - O2  - T1  - O3  - T1  = 121.331 deg; T2  -- T1  = 5.4967 A
T2  - O2  - T1  - O4  - T1  = 140.447 deg; T2  -- T1  = 5.5640 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3072 A

T1  - O3  - T2  - O4  - T1  = 115.497 deg; T1  -- T1  = 5.0684 A
T1  - O3  - T2  - O5  - T2  = 135.074 deg; T1  -- T2  = 5.6807 A
T1  - O3  - T2  - O6  - T2  =  89.320 deg; T1  -- T2  = 4.1021 A
T1  - O4  - T2  - O5  - T2  =  92.225 deg; T1  -- T2  = 4.5355 A
T1  - O4  - T2  - O6  - T2  = 140.447 deg; T1  -- T2  = 5.6291 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3437 A

        T-T-T SUMMARY
          Range  = 83.8318 deg <--> 140.4473 deg
          Mean   = 109.1839 deg
          StdDev = 21.5387 deg

        T--T SUMMARY
          Range  = 4.1021 A <--> 5.6807 A
          Mean   = 4.8451 A
          StdDev = 0.6405 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 177.452 deg ; T1  -- T1   3.2355 A

T1  -- O2  -- T1  = 122.690 deg ; T1  -- T1   2.8432 A

T1  -- O3  -- T2  = 127.835 deg ; T1  -- T2   2.9233 A

T1  -- O4  -- T2  = 142.852 deg ; T1  -- T2   3.0690 A

T2  -- O5  -- T2  = 174.931 deg ; T2  -- T2   3.2225 A

T2  -- O6  -- T2  = 126.912 deg ; T2  -- T2   2.9127 A


        T-O-T SUMMARY
          Range  = 122.6901° <--> 177.4521 deg
          Mean   = 145.4455 deg
          StdDev = 22.8667 deg

        T--T SUMMARY
          Range  = 2.8432 A <--> 3.2355 A
          Mean   = 3.0344 A
          StdDev = 0.1548 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 539
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 539
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000