Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_22314_EabqGC.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.70 T-atoms per nm^3
Material density = 1.666 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6194 Angstrom
T1  -- O4  = 1.6198 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005714  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001241  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6196 Angstrom
T2  -- O4  = 1.6197 Angstrom
T2  -- O5  = 1.6206 Angstrom
T2  -- O6  = 1.6171 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.005843  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000734  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6158 A <--> 1.6208 A
          Mean   = 1.6191 A
          StdDev = 0.0017 A

       t1 Range  = 0.0057 <-- 0.0058 --> 0.0058
       t2 Range  = 0.0007 <-- 0.0010 --> 0.0012

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.513 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.379 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.239 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.577 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.508 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.611 deg; O3  -- O4  = 3 A
       109.239 deg <-- 109.471 deg --> 109.611 deg

O3  -- T2  -- O4  = 109.546 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.399 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.791 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.282 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.202 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.607 deg; O5  -- O6  = 3 A
       109.202 deg <-- 109.471 deg --> 109.791 deg

        O-T-O SUMMARY
          Range  = 109.2016 deg <--> 109.7906 deg
          Mean   = 109.4630 deg
          StdDev = 0.1728 deg

        O--O SUMMARY
          Range  = 2.6381 A <--> 2.6479 A
          Mean   = 2.6439 A
          StdDev = 0.0035 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  =  92.936 deg; T2  -- T2  = 4.4241 A
T2  - O1  - T1  - O3  - T1  = 124.325 deg; T2  -- T1  = 5.5563 A
T2  - O1  - T1  - O4  - T1  =  91.638 deg; T2  -- T1  = 4.3627 A
T2  - O2  - T1  - O3  - T1  = 130.099 deg; T2  -- T1  = 5.6915 A
T2  - O2  - T1  - O4  - T1  = 124.030 deg; T2  -- T1  = 5.3668 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4272 A

T1  - O3  - T2  - O4  - T1  =  87.064 deg; T1  -- T1  = 4.2031 A
T1  - O3  - T2  - O5  - T2  = 129.534 deg; T1  -- T2  = 5.5195 A
T1  - O3  - T2  - O6  - T2  =  88.362 deg; T1  -- T2  = 4.3627 A
T1  - O4  - T2  - O5  - T2  = 132.820 deg; T1  -- T2  = 5.5864 A
T1  - O4  - T2  - O6  - T2  = 124.030 deg; T1  -- T2  = 5.5214 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.4218 A

        T-T-T SUMMARY
          Range  = 87.0644 deg <--> 132.8202 deg
          Mean   = 110.3063 deg
          StdDev = 19.1333 deg

        T--T SUMMARY
          Range  = 4.2031 A <--> 5.6915 A
          Mean   = 5.0019 A
          StdDev = 0.6001 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 175.094 deg ; T1  -- T1   3.2286 A

T1  -- O2  -- T1  = 138.294 deg ; T1  -- T1   3.0292 A

T1  -- O3  -- T2  = 141.107 deg ; T1  -- T2   3.0542 A

T1  -- O4  -- T2  = 140.427 deg ; T1  -- T2   3.0482 A

T2  -- O5  -- T2  = 140.189 deg ; T2  -- T2   3.0476 A

T2  -- O6  -- T2  = 164.294 deg ; T2  -- T2   3.2038 A


        T-O-T SUMMARY
          Range  = 138.2939° <--> 175.0941 deg
          Mean   = 149.9008 deg
          StdDev = 14.5162 deg

        T--T SUMMARY
          Range  = 3.0292 A <--> 3.2286 A
          Mean   = 3.1019 A
          StdDev = 0.0823 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 32 48 67 92 120 150 185 224 266 312 361 414 472
TD10 = 726
Circuit symbol = 4.4.4.8_{3}.6.6
Weight = 18
Vertex symbol  = 4.4.4.8_{2}.8.8
Weight = 26

<TD10> = 726.000
Average ring size = 5.6000