Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_20360_k19MLz.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.66 T-atoms per nm^3
Material density = 2.161 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6038 Angstrom
T1  -- O2  = 1.6288 Angstrom
T1  -- O4  = 1.5927 Angstrom
T1  -- O3  = 1.6532 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.154970  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.123193  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6428 Angstrom
T2  -- O4  = 1.6577 Angstrom
T2  -- O5  = 1.5698 Angstrom
T2  -- O6  = 1.6592 Angstrom
      mean = 1.6324 Angstrom
        t1 = 0.039886  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038387  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5698 A <--> 1.6592 A
          Mean   = 1.6260 A
          StdDev = 0.0317 A

       t1 Range  = 0.0399 <-- 0.0974 --> 0.1550
       t2 Range  = 0.0384 <-- 0.0808 --> 0.1232

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 117.026 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 125.679 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 101.035 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  =  77.917 deg; O2  -- O4  = 2 A
O2  -- T1  -- O3  = 141.890 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  =  78.421 deg; O4  -- O3  = 2 A
       77.917 deg <-- 106.995 deg --> 141.890 deg

O3  -- T2  -- O4  = 110.233 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 104.152 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 106.806 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.473 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 118.482 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 106.707 deg; O5  -- O6  = 3 A
       104.152 deg <-- 109.309 deg --> 118.482 deg

        O-T-O SUMMARY
          Range  = 77.9165 deg <--> 141.8895 deg
          Mean   = 107.8139 deg
          StdDev = 17.8472 deg

        O--O SUMMARY
          Range  = 2.0257 A <--> 3.1021 A
          Mean   = 2.5993 A
          StdDev = 0.3097 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  72.595 deg; T1  -- T2  = 3.7413 A
T1  - O1  - T1  - O4  - T1  = 128.188 deg; T1  -- T1  = 5.6310 A
T1  - O1  - T1  - O3  - T2  = 142.246 deg; T1  -- T2  = 5.9943 A
T2  - O2  - T1  - O4  - T1  = 127.600 deg; T2  -- T1  = 5.4353 A
T2  - O2  - T1  - O3  - T2  =  77.308 deg; T2  -- T2  = 3.8311 A
T1  - O4  - T1  - O3  - T2  =  88.388 deg; T1  -- T2  = 4.2375 A

T1  - O3  - T2  - O4  - T2  = 119.953 deg; T1  -- T2  = 5.3647 A
T1  - O3  - T2  - O5  - T2  = 131.188 deg; T1  -- T2  = 5.3369 A
T1  - O3  - T2  - O6  - T1  = 102.692 deg; T1  -- T1  = 4.7899 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2088 A
T2  - O4  - T2  - O6  - T1  = 103.696 deg; T2  -- T1  = 4.8887 A
T2  - O5  - T2  - O6  - T1  = 106.370 deg; T2  -- T1  = 4.7104 A

        T-T-T SUMMARY
          Range  = 72.5950 deg <--> 142.2462 deg
          Mean   = 109.1584 deg
          StdDev = 21.3471 deg

        T--T SUMMARY
          Range  = 3.7413 A <--> 5.9943 A
          Mean   = 4.9040 A
          StdDev = 0.6906 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.674 deg ; T1  -- T1   3.0012 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2576 A

T1  -- O3  -- T2  = 138.000 deg ; T1  -- T2   3.0771 A

T1  -- O4  -- T2  = 140.193 deg ; T1  -- T2   3.0564 A

T2  -- O5  -- T2  = 178.872 deg ; T2  -- T2   3.1395 A

T2  -- O6  -- T2  = 115.280 deg ; T2  -- T2   2.8031 A


        T-O-T SUMMARY
          Range  = 115.2801° <--> 180.0000 deg
          Mean   = 148.5033 deg
          StdDev = 23.6788 deg

        T--T SUMMARY
          Range  = 2.8031 A <--> 3.2576 A
          Mean   = 3.0558 A
          StdDev = 0.1399 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O4  = 2.0257 A
O2  -- O4  = 2.0257 A
O3  -- O4  = 2.0525 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 61 88 120 155 192 241 295 344 404 473 539 613
TD10 = 934
Circuit symbol = 4.5.5.5.7.7
Weight = 12
Vertex symbol  = 4.5.5.5.8.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 39 61 89 118 153 198 241 287 349 409 465 541 619
TD10 = 936
Circuit symbol = 4.4.5.7.5.7
Weight = 11
Vertex symbol  = 4.4.5.8_{2}.5.8_{2}
Weight = 27

<TD10> = 935.000
Average ring size = 5.6000