Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_20167_42Odfl.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.47 T-atoms per nm^3
Material density = 2.142 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6675 Angstrom
T1  -- O2  = 1.6398 Angstrom
T1  -- O3  = 1.5389 Angstrom
T1  -- O4  = 1.5070 Angstrom
      mean = 1.5883 Angstrom
        t1 = 0.114701  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090078  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6577 Angstrom
T2  -- O5  = 1.5918 Angstrom
T2  -- O6  = 1.6796 Angstrom
T2  -- O4  = 1.7120 Angstrom
      mean = 1.6603 Angstrom
        t1 = 0.065263  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038223  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5070 A <--> 1.7120 A
          Mean   = 1.6243 A
          StdDev = 0.0677 A

       t1 Range  = 0.0653 <-- 0.0900 --> 0.1147
       t2 Range  = 0.0382 <-- 0.0642 --> 0.0901

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 121.886 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.639 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 105.161 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 112.082 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.800 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  80.460 deg; O3  -- O4  = 2 A
       80.460 deg <-- 107.838 deg --> 121.886 deg

O3  -- T2  -- O5  =  99.214 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 105.219 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 117.467 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 108.531 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 105.010 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 119.290 deg; O6  -- O4  = 3 A
       99.214 deg <-- 109.122 deg --> 119.290 deg

        O-T-O SUMMARY
          Range  = 80.4602 deg <--> 121.8858 deg
          Mean   = 107.8683 deg
          StdDev = 11.0422 deg

        O--O SUMMARY
          Range  = 1.9674 A <--> 2.9267 A
          Mean   = 2.6158 A
          StdDev = 0.2511 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 104.525 deg; T1  -- T2  = 4.9516 A
T1  - O1  - T1  - O3  - T1  = 113.635 deg; T1  -- T1  = 5.4219 A
T1  - O1  - T1  - O4  - T2  =  98.469 deg; T1  -- T2  = 4.8692 A
T2  - O2  - T1  - O3  - T1  = 140.638 deg; T2  -- T1  = 5.8155 A
T2  - O2  - T1  - O4  - T2  =  72.230 deg; T2  -- T2  = 3.6132 A
T1  - O3  - T1  - O4  - T2  =  92.400 deg; T1  -- T2  = 4.5810 A

T1  - O3  - T2  - O5  - T2  =  99.938 deg; T1  -- T2  = 4.6942 A
T1  - O3  - T2  - O6  - T2  = 101.596 deg; T1  -- T2  = 4.5965 A
T1  - O3  - T2  - O4  - T1  = 107.770 deg; T1  -- T1  = 4.9496 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3196 A
T2  - O5  - T2  - O4  - T1  = 115.648 deg; T2  -- T1  = 5.3324 A
T2  - O6  - T2  - O4  - T1  = 135.968 deg; T2  -- T1  = 5.6580 A

        T-T-T SUMMARY
          Range  = 72.2304 deg <--> 140.6376 deg
          Mean   = 106.8684 deg
          StdDev = 18.7208 deg

        T--T SUMMARY
          Range  = 3.6132 A <--> 5.8155 A
          Mean   = 4.9243 A
          StdDev = 0.6012 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.110 deg ; T1  -- T1   3.1985 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2796 A

T1  -- O3  -- T2  = 137.282 deg ; T1  -- T2   2.9773 A

T1  -- O4  -- T2  = 155.911 deg ; T1  -- T2   3.1484 A

T2  -- O5  -- T2  = 163.700 deg ; T2  -- T2   3.1515 A

T2  -- O6  -- T2  = 123.140 deg ; T2  -- T2   2.9542 A


        T-O-T SUMMARY
          Range  = 123.1399° <--> 180.0000 deg
          Mean   = 151.1906 deg
          StdDev = 18.4768 deg

        T--T SUMMARY
          Range  = 2.9542 A <--> 3.2796 A
          Mean   = 3.1183 A
          StdDev = 0.1176 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 1.9674 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 61 88 120 155 192 241 295 344 404 473 539 613
TD10 = 934
Circuit symbol = 4.5.5.5.7.7
Weight = 12
Vertex symbol  = 4.5.5.5.8.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 22 39 61 89 118 153 198 241 287 349 409 465 541 619
TD10 = 936
Circuit symbol = 4.4.5.7.5.7
Weight = 11
Vertex symbol  = 4.4.5.8_{2}.5.8_{2}
Weight = 27

<TD10> = 935.000
Average ring size = 5.6000