Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_19794_1KjYv3.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.34 T-atoms per nm^3
Material density = 1.930 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6252 Angstrom
T1  -- O2  = 1.6208 Angstrom
T1  -- O3  = 1.6247 Angstrom
T1  -- O4  = 1.6105 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.009905  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005716  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6135 Angstrom
T2  -- O5  = 1.6182 Angstrom
T2  -- O6  = 1.6048 Angstrom
T2  -- O7  = 1.6098 Angstrom
      mean = 1.6116 Angstrom
        t1 = 0.006234  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004081  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6048 A <--> 1.6252 A
          Mean   = 1.6159 A
          StdDev = 0.0070 A

       t1 Range  = 0.0062 <-- 0.0081 --> 0.0099
       t2 Range  = 0.0041 <-- 0.0049 --> 0.0057

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.758 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.803 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.901 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.764 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.722 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.860 deg; O3  -- O4  = 3 A
       107.722 deg <-- 109.468 deg --> 110.758 deg

O4  -- T2  -- O5  = 110.884 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.021 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.443 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 108.406 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.304 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.745 deg; O6  -- O7  = 3 A
       108.406 deg <-- 109.467 deg --> 110.884 deg

        O-T-O SUMMARY
          Range  = 107.7217 deg <--> 110.8838 deg
          Mean   = 109.4688 deg
          StdDev = 0.9258 deg

        O--O SUMMARY
          Range  = 2.6096 A <--> 2.6712 A
          Mean   = 2.6380 A
          StdDev = 0.0186 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 112.234 deg; T1  -- T1  = 5.3849 A
T1  - O1  - T1  - O3  - T1  = 113.435 deg; T1  -- T1  = 5.3071 A
T1  - O1  - T1  - O4  - T2  = 111.313 deg; T1  -- T2  = 5.3050 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4918 A
T1  - O2  - T1  - O4  - T2  = 115.456 deg; T1  -- T2  = 5.4352 A
T1  - O3  - T1  - O4  - T2  = 112.912 deg; T1  -- T2  = 5.2422 A

T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3975 A
T2  - O4  - T2  - O6  - T1  = 119.638 deg; T2  -- T1  = 5.3544 A
T2  - O4  - T2  - O7  - T2  = 119.074 deg; T2  -- T2  = 5.3619 A
T2  - O5  - T2  - O6  - T1  = 112.912 deg; T2  -- T1  = 5.3252 A
T2  - O5  - T2  - O7  - T2  = 111.751 deg; T2  -- T2  = 5.3109 A
T1  - O6  - T2  - O7  - T2  = 103.329 deg; T1  -- T2  = 5.0146 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 119.6380 deg
          Mean   = 110.0248 deg
          StdDev = 9.7957 deg

        T--T SUMMARY
          Range  = 4.3975 A <--> 5.4352 A
          Mean   = 5.1682 A
          StdDev = 0.3452 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.277 deg ; T1  -- T1   3.2448 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2416 A

T1  -- O3  -- T1  = 145.834 deg ; T1  -- T1   3.1061 A

T1  -- O4  -- T2  = 161.778 deg ; T1  -- T2   3.1833 A

T2  -- O5  -- T2  = 136.876 deg ; T2  -- T2   3.0099 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2096 A

T2  -- O7  -- T2  = 169.466 deg ; T2  -- T2   3.2060 A


        T-O-T SUMMARY
          Range  = 136.8763° <--> 180.0000 deg
          Mean   = 163.8901 deg
          StdDev = 15.7180 deg

        T--T SUMMARY
          Range  = 3.0099 A <--> 3.2448 A
          Mean   = 3.1716 A
          StdDev = 0.0795 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 412 455 492 527
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 412 455 492 527
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000