Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_18185_12LZO1.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.12 T-atoms per nm^3
Material density = 2.207 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6251 Angstrom
T1  -- O2  = 1.6327 Angstrom
T1  -- O3  = 1.6061 Angstrom
T1  -- O4  = 1.6064 Angstrom
      mean = 1.6176 Angstrom
        t1 = 0.042462  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032429  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6178 Angstrom
T2  -- O4  = 1.6172 Angstrom
T2  -- O5  = 1.6583 Angstrom
T2  -- O6  = 1.6857 Angstrom
      mean = 1.6447 Angstrom
        t1 = 0.053366  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037529  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6061 A <--> 1.6857 A
          Mean   = 1.6312 A
          StdDev = 0.0261 A

       t1 Range  = 0.0425 <-- 0.0479 --> 0.0534
       t2 Range  = 0.0324 <-- 0.0350 --> 0.0375

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 121.096 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.883 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 102.228 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.889 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.898 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 116.427 deg; O3  -- O4  = 3 A
       102.228 deg <-- 109.570 deg --> 121.096 deg

O3  -- T2  -- O4  = 113.206 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 104.474 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.240 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 103.987 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.690 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 124.500 deg; O5  -- O6  = 3 A
       103.987 deg <-- 109.516 deg --> 124.500 deg

        O-T-O SUMMARY
          Range  = 102.2276 deg <--> 124.4997 deg
          Mean   = 108.3381 deg
          StdDev = 6.1618 deg

        O--O SUMMARY
          Range  = 2.5154 A <--> 2.9594 A
          Mean   = 2.6384 A
          StdDev = 0.1032 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 108.593 deg; T2  -- T1  = 4.6729 A
T2  - O1  - T1  - O3  - T1  =  83.770 deg; T2  -- T1  = 4.1407 A
T2  - O1  - T1  - O4  - T2  = 134.883 deg; T2  -- T2  = 5.4311 A
T1  - O2  - T1  - O3  - T1  = 150.512 deg; T1  -- T1  = 5.8947 A
T1  - O2  - T1  - O4  - T2  = 104.615 deg; T1  -- T2  = 4.5784 A
T1  - O3  - T1  - O4  - T2  =  82.018 deg; T1  -- T2  = 4.0890 A

T1  - O3  - T2  - O4  - T2  =  81.596 deg; T1  -- T2  = 4.0890 A
T1  - O3  - T2  - O5  - T2  = 104.909 deg; T1  -- T2  = 4.5118 A
T1  - O3  - T2  - O6  - T1  = 134.883 deg; T1  -- T1  = 5.4311 A
T2  - O4  - T2  - O5  - T2  = 159.426 deg; T2  -- T2  = 5.9838 A
T2  - O4  - T2  - O6  - T1  =  82.402 deg; T2  -- T1  = 4.1407 A
T2  - O5  - T2  - O6  - T1  = 104.749 deg; T2  -- T1  = 4.5320 A

        T-T-T SUMMARY
          Range  = 81.5961 deg <--> 159.4258 deg
          Mean   = 111.4258 deg
          StdDev = 27.8076 deg

        T--T SUMMARY
          Range  = 4.0890 A <--> 5.9838 A
          Mean   = 4.8084 A
          StdDev = 0.7081 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.020 deg ; T1  -- T1   2.8290 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2653 A

T1  -- O3  -- T2  = 130.267 deg ; T1  -- T2   2.9250 A

T1  -- O4  -- T2  = 132.979 deg ; T1  -- T2   2.9560 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.3166 A

T2  -- O6  -- T2  = 110.144 deg ; T2  -- T2   2.7642 A


        T-O-T SUMMARY
          Range  = 110.1444° <--> 180.0000 deg
          Mean   = 142.4017 deg
          StdDev = 27.8630 deg

        T--T SUMMARY
          Range  = 2.7642 A <--> 3.3166 A
          Mean   = 3.0094 A
          StdDev = 0.2114 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7642 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 60 89 121 157 199 247 299 355 417 485 557 633
TD10 = 946
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12_{48}
Weight = 39

<TD10> = 946.000
Average ring size = 10.6000