Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_17991_n0pGie.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 21.30 T-atoms per nm^3
Material density = 2.126 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5588 Angstrom
T1  -- O2  = 1.5449 Angstrom
T1  -- O3  = 1.5952 Angstrom
T1  -- O4  = 1.6386 Angstrom
      mean = 1.5844 Angstrom
        t1 = 0.127074  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.087168  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6673 Angstrom
T2  -- O6  = 1.6624 Angstrom
T2  -- O7  = 1.6311 Angstrom
T2  -- O4  = 1.6120 Angstrom
      mean = 1.6432 Angstrom
        t1 = 0.034697  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017586  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5449 A <--> 1.6673 A
          Mean   = 1.6138 A
          StdDev = 0.0426 A

       t1 Range  = 0.0347 <-- 0.0809 --> 0.1271
       t2 Range  = 0.0176 <-- 0.0524 --> 0.0872

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 131.722 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 114.345 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  80.724 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 113.933 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  81.046 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 112.791 deg; O3  -- O4  = 3 A
       80.724 deg <-- 105.760 deg --> 131.722 deg

O5  -- T2  -- O6  = 117.129 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.591 deg; O5  -- O7  = 3 A
O5  -- T2  -- O4  = 106.561 deg; O5  -- O4  = 3 A
O6  -- T2  -- O7  = 108.801 deg; O6  -- O7  = 3 A
O6  -- T2  -- O4  = 106.423 deg; O6  -- O4  = 3 A
O7  -- T2  -- O4  = 109.098 deg; O7  -- O4  = 3 A
       106.423 deg <-- 109.434 deg --> 117.129 deg

        O-T-O SUMMARY
          Range  = 80.7243 deg <--> 131.7215 deg
          Mean   = 104.8782 deg
          StdDev = 14.1332 deg

        O--O SUMMARY
          Range  = 2.0697 A <--> 2.8410 A
          Mean   = 2.5427 A
          StdDev = 0.2615 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 155.741 deg; T1  -- T1  = 5.8051 A
T1  - O1  - T1  - O3  - T1  = 114.259 deg; T1  -- T1  = 5.2749 A
T1  - O1  - T1  - O4  - T2  =  80.354 deg; T1  -- T2  = 4.0919 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2764 A
T1  - O2  - T1  - O4  - T2  =  90.674 deg; T1  -- T2  = 4.3463 A
T1  - O3  - T1  - O4  - T2  = 112.440 deg; T1  -- T2  = 5.3532 A

T2  - O5  - T2  - O6  - T2  = 123.695 deg; T2  -- T2  = 5.7928 A
T2  - O5  - T2  - O7  - T1  = 105.462 deg; T2  -- T1  = 5.2325 A
T2  - O5  - T2  - O4  - T2  = 111.375 deg; T2  -- T2  = 5.4291 A
T2  - O6  - T2  - O7  - T1  = 113.275 deg; T2  -- T1  = 5.4248 A
T2  - O6  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.5912 A
T1  - O7  - T2  - O4  - T2  = 112.440 deg; T1  -- T2  = 5.4010 A

        T-T-T SUMMARY
          Range  = 80.3539 deg <--> 155.7414 deg
          Mean   = 105.3888 deg
          StdDev = 17.8868 deg

        T--T SUMMARY
          Range  = 4.0919 A <--> 5.8051 A
          Mean   = 5.0129 A
          StdDev = 0.5758 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.960 deg ; T1  -- T1   2.8477 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.0897 A

T1  -- O3  -- T1  = 179.349 deg ; T1  -- T1   3.1903 A

T1  -- O4  -- T2  = 178.064 deg ; T1  -- T2   3.2501 A

T2  -- O5  -- T2  = 153.389 deg ; T2  -- T2   3.2450 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.3249 A

T2  -- O7  -- T2  = 169.303 deg ; T2  -- T2   3.2479 A


        T-O-T SUMMARY
          Range  = 131.9602° <--> 180.0000 deg
          Mean   = 167.4378 deg
          StdDev = 17.1832 deg

        T--T SUMMARY
          Range  = 2.8477 A <--> 3.3249 A
          Mean   = 3.1708 A
          StdDev = 0.1491 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.0716 A
O1  -- O4  = 2.0716 A
O2  -- O4  = 2.0697 A
O2  -- O4  = 2.0697 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 24 41 63 91 123 160 202 249 301 358 420 487 559 635
TD10 = 969
Circuit symbol = 4.6_{2}.6.6.6.6
Weight = 22
Vertex symbol  = 4.6_{2}.6.6.6.6
Weight = 22

<TD10> = 969.000
Average ring size = 5.6000