Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_12_2_17339_SfHgFY.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 17.71 T-atoms per nm^3
Material density = 1.767 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.6152 Angstrom
T1  -- O3  = 1.6194 Angstrom
T1  -- O4  = 1.6200 Angstrom
      mean = 1.6176 Angstrom
        t1 = 0.004910  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001196  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6195 Angstrom
T2  -- O5  = 1.6159 Angstrom
T2  -- O6  = 1.6158 Angstrom
T2  -- O7  = 1.6201 Angstrom
      mean = 1.6178 Angstrom
        t1 = 0.005018  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000922  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6201 A
          Mean   = 1.6177 A
          StdDev = 0.0021 A

       t1 Range  = 0.0049 <-- 0.0050 --> 0.0050
       t2 Range  = 0.0009 <-- 0.0011 --> 0.0012

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.377 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.689 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.350 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.434 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.389 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.587 deg; O3  -- O4  = 3 A
       109.350 deg <-- 109.471 deg --> 109.689 deg

O4  -- T2  -- O5  = 109.458 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.363 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.594 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.405 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.661 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.346 deg; O6  -- O7  = 3 A
       109.346 deg <-- 109.471 deg --> 109.661 deg

        O-T-O SUMMARY
          Range  = 109.3458 deg <--> 109.6891 deg
          Mean   = 109.4664 deg
          StdDev = 0.1157 deg

        O--O SUMMARY
          Range  = 2.6367 A <--> 2.6471 A
          Mean   = 2.6420 A
          StdDev = 0.0033 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 118.000 deg; T2  -- T1  = 5.3880 A
T2  - O1  - T1  - O3  - T1  =  89.996 deg; T2  -- T1  = 4.3267 A
T2  - O1  - T1  - O4  - T1  = 118.020 deg; T2  -- T1  = 5.3915 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4479 A
T1  - O2  - T1  - O4  - T1  = 111.355 deg; T1  -- T1  = 5.3330 A
T1  - O3  - T1  - O4  - T1  = 125.721 deg; T1  -- T1  = 5.5992 A

T1  - O4  - T2  - O5  - T2  = 117.990 deg; T1  -- T2  = 5.3918 A
T1  - O4  - T2  - O6  - T2  = 118.084 deg; T1  -- T2  = 5.3906 A
T1  - O4  - T2  - O7  - T2  =  90.004 deg; T1  -- T2  = 4.3267 A
T2  - O5  - T2  - O6  - T2  = 111.321 deg; T2  -- T2  = 5.3332 A
T2  - O5  - T2  - O7  - T2  = 125.713 deg; T2  -- T2  = 5.5998 A
T2  - O6  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4477 A

        T-T-T SUMMARY
          Range  = 89.9963 deg <--> 125.7206 deg
          Mean   = 110.4097 deg
          StdDev = 13.4152 deg

        T--T SUMMARY
          Range  = 4.3267 A <--> 5.5998 A
          Mean   = 5.1338 A
          StdDev = 0.4822 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.752 deg ; T1  -- T1   3.2270 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2304 A

T1  -- O3  -- T1  = 141.849 deg ; T1  -- T1   3.0610 A

T1  -- O4  -- T2  = 141.466 deg ; T1  -- T2   3.0580 A

T2  -- O5  -- T2  = 173.942 deg ; T2  -- T2   3.2272 A

T2  -- O6  -- T2  = 180.000 deg ; T2  -- T2   3.2317 A

T2  -- O7  -- T2  = 141.671 deg ; T2  -- T2   3.0606 A


        T-O-T SUMMARY
          Range  = 141.4655° <--> 180.0000 deg
          Mean   = 161.8115 deg
          StdDev = 17.7639 deg

        T--T SUMMARY
          Range  = 3.0580 A <--> 3.2317 A
          Mean   = 3.1566 A
          StdDev = 0.0845 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182