Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_128_2_7095_aC35ig.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.56 T-atoms per nm^3
Material density = 1.852 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6185 Angstrom
T1  -- O2  = 1.6100 Angstrom
T1  -- O3  = 1.6226 Angstrom
T1  -- O1  = 1.6185 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.004623  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000350  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6101 Angstrom
T2  -- O3  = 1.6225 Angstrom
T2  -- O4  = 1.6184 Angstrom
T2  -- O4  = 1.6184 Angstrom
      mean = 1.6174 Angstrom
        t1 = 0.004597  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000477  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6100 A <--> 1.6226 A
          Mean   = 1.6174 A
          StdDev = 0.0046 A

       t1 Range  = 0.0046 <-- 0.0046 --> 0.0046
       t2 Range  = 0.0003 <-- 0.0004 --> 0.0005

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.867 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.169 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.180 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.570 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.867 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.169 deg; O3  -- O1  = 3 A
       109.169 deg <-- 109.470 deg --> 109.867 deg

O2  -- T2  -- O3  = 109.565 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.866 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.866 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.169 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.169 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 109.187 deg; O4  -- O4  = 3 A
       109.169 deg <-- 109.470 deg --> 109.866 deg

        O-T-O SUMMARY
          Range  = 109.1692 deg <--> 109.8668 deg
          Mean   = 109.4704 deg
          StdDev = 0.3143 deg

        O--O SUMMARY
          Range  = 2.6382 A <--> 2.6425 A
          Mean   = 2.6412 A
          StdDev = 0.0014 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.999 deg; T1  -- T2  = 4.4480 A
T1  - O1  - T1  - O3  - T2  = 111.270 deg; T1  -- T2  = 5.0154 A
T1  - O1  - T1  - O1  - T1  = 118.270 deg; T1  -- T1  = 5.2764 A
T2  - O2  - T1  - O3  - T2  = 135.002 deg; T2  -- T2  = 5.7450 A
T2  - O2  - T1  - O1  - T1  =  89.999 deg; T2  -- T1  = 4.4480 A
T2  - O3  - T1  - O1  - T1  = 111.270 deg; T2  -- T1  = 5.0154 A

T1  - O2  - T2  - O3  - T2  =  90.001 deg; T1  -- T2  = 4.4480 A
T1  - O2  - T2  - O4  - T1  = 134.998 deg; T1  -- T1  = 5.7449 A
T1  - O2  - T2  - O4  - T2  =  90.001 deg; T1  -- T2  = 4.4480 A
T2  - O3  - T2  - O4  - T1  = 111.268 deg; T2  -- T1  = 5.0153 A
T2  - O3  - T2  - O4  - T2  = 118.276 deg; T2  -- T2  = 5.2764 A
T1  - O4  - T2  - O4  - T2  = 111.268 deg; T1  -- T2  = 5.0153 A

        T-T-T SUMMARY
          Range  = 89.9992 deg <--> 135.0016 deg
          Mean   = 109.3017 deg
          StdDev = 15.8611 deg

        T--T SUMMARY
          Range  = 4.4480 A <--> 5.7450 A
          Mean   = 4.9913 A
          StdDev = 0.4571 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 143.426 deg ; T1  -- T1   3.0735 A

T1  -- O2  -- T2  = 173.754 deg ; T1  -- T2   3.2154 A

T1  -- O3  -- T2  = 135.381 deg ; T1  -- T2   3.0022 A

T2  -- O4  -- T2  = 143.431 deg ; T2  -- T2   3.0734 A


        T-O-T SUMMARY
          Range  = 135.3814° <--> 173.7543 deg
          Mean   = 148.9982 deg
          StdDev = 14.9003 deg

        T--T SUMMARY
          Range  = 3.0022 A <--> 3.2154 A
          Mean   = 3.0911 A
          StdDev = 0.0787 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 833.000
Average ring size = 5.3333