Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_128_2_7029_Gi2bYw.cif"

There are 20 T-atoms per unit cell
There are 40 O-atoms per unit cell

Framework density = 17.18 T-atoms per nm^3
Material density = 1.714 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6265 Angstrom
T1  -- O2  = 1.6156 Angstrom
T1  -- O3  = 1.5857 Angstrom
T1  -- O1  = 1.6265 Angstrom
      mean = 1.6136 Angstrom
        t1 = 0.007582  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004894  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6162 Angstrom
T2  -- O3  = 1.6162 Angstrom
T2  -- O3  = 1.6162 Angstrom
T2  -- O3  = 1.6162 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.007752  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005202  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5857 A <--> 1.6265 A
          Mean   = 1.6141 A
          StdDev = 0.0150 A

       t1 Range  = 0.0076 <-- 0.0077 --> 0.0078
       t2 Range  = 0.0049 <-- 0.0050 --> 0.0052

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.808 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.654 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.555 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 108.311 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 108.808 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 110.654 deg; O3  -- O1  = 3 A
       108.311 deg <-- 109.465 deg --> 110.654 deg

O3  -- T2  -- O3  = 107.943 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.241 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.241 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.241 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.241 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 107.943 deg; O3  -- O3  = 3 A
       107.943 deg <-- 109.475 deg --> 110.241 deg

        O-T-O SUMMARY
          Range  = 107.9428 deg <--> 110.6545 deg
          Mean   = 109.4699 deg
          StdDev = 1.0057 deg

        O--O SUMMARY
          Range  = 2.5951 A <--> 2.6574 A
          Mean   = 2.6370 A
          StdDev = 0.0186 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 129.356 deg; T1  -- T2  = 5.5209 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1753 A
T1  - O1  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 4.3753 A
T2  - O2  - T1  - O3  - T1  = 129.356 deg; T2  -- T1  = 5.5209 A
T2  - O2  - T1  - O1  - T1  = 116.258 deg; T2  -- T1  = 5.4215 A
T1  - O3  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 4.3753 A

T1  - O3  - T2  - O3  - T1  = 127.483 deg; T1  -- T1  = 5.6581 A
T1  - O3  - T2  - O3  - T1  = 101.288 deg; T1  -- T1  = 4.8784 A
T1  - O3  - T2  - O3  - T1  = 101.288 deg; T1  -- T1  = 4.8784 A
T1  - O3  - T2  - O3  - T1  = 101.288 deg; T1  -- T1  = 4.8784 A
T1  - O3  - T2  - O3  - T1  = 101.288 deg; T1  -- T1  = 4.8784 A
T1  - O3  - T2  - O3  - T1  = 127.483 deg; T1  -- T1  = 5.6581 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 129.3561 deg
          Mean   = 108.7573 deg
          StdDev = 15.5456 deg

        T--T SUMMARY
          Range  = 4.1753 A <--> 5.6581 A
          Mean   = 5.0183 A
          StdDev = 0.5098 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.351 deg ; T1  -- T1   2.9524 A

T1  -- O2  -- T1  = 175.975 deg ; T1  -- T1   3.2291 A

T1  -- O3  -- T2  = 160.270 deg ; T1  -- T2   3.1546 A


        T-O-T SUMMARY
          Range  = 130.3508° <--> 175.9747 deg
          Mean   = 155.5319 deg
          StdDev = 19.1251 deg

        T--T SUMMARY
          Range  = 2.9524 A <--> 3.2291 A
          Mean   = 3.1120 A
          StdDev = 0.1182 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 34 48 66 96 127 151 183 232 281 316 357 427 499
TD10 = 738
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 18 28 52 78 88 112 162 204 220 254 328 396 414 448
TD10 = 759
Circuit symbol = 6.6.6.6.6.6
Weight = 23
Vertex symbol  = 6.6.6.6.6.6
Weight = 23

<TD10> = 742.200
Average ring size = 5.0000