Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_128_2_5623_hhoV7x.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 20.20 T-atoms per nm^3
Material density = 2.015 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6198 Angstrom
T1  -- O2  = 1.6186 Angstrom
T1  -- O4  = 1.6198 Angstrom
T1  -- O3  = 1.6209 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006686  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002411  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6153 Angstrom
T2  -- O3  = 1.6199 Angstrom
T2  -- O4  = 1.6192 Angstrom
T2  -- O5  = 1.6204 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.005723  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001232  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6153 A <--> 1.6209 A
          Mean   = 1.6192 A
          StdDev = 0.0016 A

       t1 Range  = 0.0057 <-- 0.0062 --> 0.0067
       t2 Range  = 0.0012 <-- 0.0018 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.621 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.884 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.774 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.310 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.646 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.589 deg; O4  -- O3  = 3 A
       108.621 deg <-- 109.471 deg --> 109.884 deg

O2  -- T2  -- O3  = 109.432 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.520 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.161 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 109.981 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.322 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 109.409 deg; O4  -- O5  = 3 A
       109.161 deg <-- 109.471 deg --> 109.981 deg

        O-T-O SUMMARY
          Range  = 108.6211 deg <--> 109.9808 deg
          Mean   = 109.4706 deg
          StdDev = 0.3475 deg

        O--O SUMMARY
          Range  = 2.6302 A <--> 2.6530 A
          Mean   = 2.6442 A
          StdDev = 0.0064 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 109.393 deg; T1  -- T2  = 5.0013 A
T1  - O1  - T1  - O4  - T2  = 109.070 deg; T1  -- T2  = 5.0122 A
T1  - O1  - T1  - O3  - T2  = 109.474 deg; T1  -- T2  = 5.0130 A
T2  - O2  - T1  - O4  - T2  = 117.706 deg; T2  -- T2  = 5.2497 A
T2  - O2  - T1  - O3  - T2  = 117.632 deg; T2  -- T2  = 5.2352 A
T2  - O4  - T1  - O3  - T2  =  92.387 deg; T2  -- T2  = 4.4349 A

T1  - O2  - T2  - O3  - T1  = 124.853 deg; T1  -- T1  = 5.4372 A
T1  - O2  - T2  - O4  - T1  = 124.807 deg; T1  -- T1  = 5.4232 A
T1  - O2  - T2  - O5  - T2  = 109.393 deg; T1  -- T2  = 4.9866 A
T1  - O3  - T2  - O4  - T1  =  74.959 deg; T1  -- T1  = 3.7392 A
T1  - O3  - T2  - O5  - T2  = 109.225 deg; T1  -- T2  = 5.0024 A
T1  - O4  - T2  - O5  - T2  = 109.319 deg; T1  -- T2  = 4.9935 A

        T-T-T SUMMARY
          Range  = 74.9589 deg <--> 124.8526 deg
          Mean   = 109.0180 deg
          StdDev = 13.2221 deg

        T--T SUMMARY
          Range  = 3.7392 A <--> 5.4372 A
          Mean   = 4.9607 A
          StdDev = 0.4464 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 143.220 deg ; T1  -- T1   3.0741 A

T1  -- O2  -- T2  = 141.604 deg ; T1  -- T2   3.0541 A

T1  -- O3  -- T2  = 142.121 deg ; T1  -- T2   3.0654 A

T1  -- O4  -- T2  = 143.921 deg ; T1  -- T2   3.0798 A

T2  -- O5  -- T2  = 141.137 deg ; T2  -- T2   3.0562 A


        T-O-T SUMMARY
          Range  = 141.1367° <--> 143.9214 deg
          Mean   = 142.4005 deg
          StdDev = 1.0356 deg

        T--T SUMMARY
          Range  = 3.0541 A <--> 3.0798 A
          Mean   = 3.0659 A
          StdDev = 0.0100 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391