Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_127_2_73_uOVAbD.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.61 T-atoms per nm^3
Material density = 1.957 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6235 Angstrom
T1  -- O2  = 1.6162 Angstrom
T1  -- O3  = 1.6202 Angstrom
T1  -- O4  = 1.6180 Angstrom
      mean = 1.6195 Angstrom
        t1 = 0.006408  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001758  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6208 Angstrom
T2  -- O5  = 1.6225 Angstrom
T2  -- O6  = 1.6232 Angstrom
T2  -- O4  = 1.6201 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007479  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001569  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6162 A <--> 1.6235 A
          Mean   = 1.6206 A
          StdDev = 0.0024 A

       t1 Range  = 0.0064 <-- 0.0069 --> 0.0075
       t2 Range  = 0.0016 <-- 0.0017 --> 0.0018

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.255 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.414 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.947 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.755 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.963 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.494 deg; O3  -- O4  = 3 A
       108.963 deg <-- 109.471 deg --> 109.947 deg

O3  -- T2  -- O5  = 109.403 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.692 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.450 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.396 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.975 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.908 deg; O6  -- O4  = 3 A
       108.975 deg <-- 109.471 deg --> 109.908 deg

        O-T-O SUMMARY
          Range  = 108.9626 deg <--> 109.9469 deg
          Mean   = 109.4842 deg
          StdDev = 0.3148 deg

        O--O SUMMARY
          Range  = 2.6323 A <--> 2.6553 A
          Mean   = 2.6464 A
          StdDev = 0.0064 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  88.479 deg; T1  -- T2  = 4.3422 A
T1  - O1  - T1  - O3  - T2  = 130.403 deg; T1  -- T2  = 5.6551 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3372 A
T2  - O2  - T1  - O3  - T2  = 114.116 deg; T2  -- T2  = 5.1135 A
T2  - O2  - T1  - O4  - T1  = 115.176 deg; T2  -- T1  = 5.0599 A
T2  - O3  - T1  - O4  - T1  = 115.116 deg; T2  -- T1  = 5.0639 A

T1  - O3  - T2  - O5  - T2  = 115.176 deg; T1  -- T2  = 5.1281 A
T1  - O3  - T2  - O6  - T2  =  91.521 deg; T1  -- T2  = 4.3422 A
T1  - O3  - T2  - O4  - T1  = 112.892 deg; T1  -- T1  = 5.0778 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2772 A
T2  - O5  - T2  - O4  - T1  = 115.116 deg; T2  -- T1  = 5.1321 A
T2  - O6  - T2  - O4  - T1  = 129.215 deg; T2  -- T1  = 5.4815 A

        T-T-T SUMMARY
          Range  = 88.4788 deg <--> 130.4035 deg
          Mean   = 110.7246 deg
          StdDev = 13.8036 deg

        T--T SUMMARY
          Range  = 4.2772 A <--> 5.6551 A
          Mean   = 4.9728 A
          StdDev = 0.4343 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.610 deg ; T1  -- T1   2.9501 A

T1  -- O2  -- T1  = 159.214 deg ; T1  -- T1   3.1793 A

T1  -- O3  -- T2  = 139.753 deg ; T1  -- T2   3.0432 A

T1  -- O4  -- T2  = 140.749 deg ; T1  -- T2   3.0500 A

T2  -- O5  -- T2  = 138.175 deg ; T2  -- T2   3.0312 A

T2  -- O6  -- T2  = 136.730 deg ; T2  -- T2   3.0177 A


        T-O-T SUMMARY
          Range  = 130.6102° <--> 159.2141 deg
          Mean   = 140.8720 deg
          StdDev = 8.8727 deg

        T--T SUMMARY
          Range  = 2.9501 A <--> 3.1793 A
          Mean   = 3.0452 A
          StdDev = 0.0687 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

<TD10> = 867.000
Average ring size = 5.8182