Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_125_2_24297_55yFMG.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 20.33 T-atoms per nm^3
Material density = 2.028 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6035 Angstrom
T1  -- O2  = 1.6227 Angstrom
T1  -- O3  = 1.6519 Angstrom
T1  -- O4  = 1.6055 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.076729  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066038  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6129 Angstrom
T2  -- O5  = 1.6334 Angstrom
T2  -- O6  = 1.6243 Angstrom
T2  -- O7  = 1.6128 Angstrom
      mean = 1.6208 Angstrom
        t1 = 0.018524  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010997  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6035 A <--> 1.6519 A
          Mean   = 1.6209 A
          StdDev = 0.0151 A

       t1 Range  = 0.0185 <-- 0.0476 --> 0.0767
       t2 Range  = 0.0110 <-- 0.0385 --> 0.0660

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 117.191 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.489 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  91.976 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 118.099 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  94.701 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 108.125 deg; O3  -- O4  = 3 A
       91.976 deg <-- 108.097 deg --> 118.489 deg

O4  -- T2  -- O5  = 113.172 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.303 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 104.863 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.800 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.516 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.073 deg; O6  -- O7  = 3 A
       104.863 deg <-- 109.455 deg --> 113.172 deg

        O-T-O SUMMARY
          Range  = 91.9762 deg <--> 118.4888 deg
          Mean   = 107.0805 deg
          StdDev = 8.3120 deg

        O--O SUMMARY
          Range  = 2.3079 A <--> 2.8083 A
          Mean   = 2.5990 A
          StdDev = 0.1537 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.6759 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1216 A
T1  - O1  - T1  - O4  - T2  =  89.264 deg; T1  -- T2  = 4.3629 A
T1  - O2  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.5090 A
T1  - O2  - T1  - O4  - T2  =  89.538 deg; T1  -- T2  = 4.4667 A
T1  - O3  - T1  - O4  - T2  =  91.384 deg; T1  -- T2  = 4.3196 A

T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3050 A
T2  - O4  - T2  - O6  - T2  = 121.309 deg; T2  -- T2  = 5.6035 A
T2  - O4  - T2  - O7  - T1  = 108.292 deg; T2  -- T1  = 5.1587 A
T2  - O5  - T2  - O6  - T2  = 131.950 deg; T2  -- T2  = 5.6537 A
T2  - O5  - T2  - O7  - T1  =  90.736 deg; T2  -- T1  = 4.3629 A
T2  - O6  - T2  - O7  - T1  = 109.478 deg; T2  -- T1  = 5.2825 A

        T-T-T SUMMARY
          Range  = 89.2636 deg <--> 135.0000 deg
          Mean   = 103.9853 deg
          StdDev = 17.2260 deg

        T--T SUMMARY
          Range  = 4.1216 A <--> 5.6759 A
          Mean   = 4.8355 A
          StdDev = 0.5777 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.438 deg ; T1  -- T1   3.1394 A

T1  -- O2  -- T1  = 120.820 deg ; T1  -- T1   2.8221 A

T1  -- O3  -- T1  = 130.805 deg ; T1  -- T1   3.0040 A

T1  -- O4  -- T2  = 168.736 deg ; T1  -- T2   3.2029 A

T2  -- O5  -- T2  = 178.085 deg ; T2  -- T2   3.2664 A

T2  -- O6  -- T2  = 153.458 deg ; T2  -- T2   3.1618 A

T2  -- O7  -- T2  = 129.857 deg ; T2  -- T2   2.9216 A


        T-O-T SUMMARY
          Range  = 120.8205° <--> 178.0851 deg
          Mean   = 148.3144 deg
          StdDev = 20.0862 deg

        T--T SUMMARY
          Range  = 2.8221 A <--> 3.2664 A
          Mean   = 3.0740 A
          StdDev = 0.1505 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

<TD10> = 867.000
Average ring size = 5.8182