Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_124_2_25931_AoR6qI.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 19.38 T-atoms per nm^3
Material density = 1.934 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6208 Angstrom
T1  -- O2  = 1.6213 Angstrom
T1  -- O3  = 1.6209 Angstrom
T1  -- O4  = 1.6091 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.005239  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001277  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6101 Angstrom
T2  -- O5  = 1.6219 Angstrom
T2  -- O6  = 1.6210 Angstrom
T2  -- O7  = 1.6215 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.005580  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001274  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6091 A <--> 1.6219 A
          Mean   = 1.6183 A
          StdDev = 0.0051 A

       t1 Range  = 0.0052 <-- 0.0054 --> 0.0056
       t2 Range  = 0.0013 <-- 0.0013 --> 0.0013

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.318 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.376 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.378 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.549 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.544 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.662 deg; O3  -- O4  = 3 A
       109.318 deg <-- 109.471 deg --> 109.662 deg

O4  -- T2  -- O5  = 109.455 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.572 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.496 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.417 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.334 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.554 deg; O6  -- O7  = 3 A
       109.334 deg <-- 109.471 deg --> 109.572 deg

        O-T-O SUMMARY
          Range  = 109.3177 deg <--> 109.6620 deg
          Mean   = 109.4867 deg
          StdDev = 0.1020 deg

        O--O SUMMARY
          Range  = 2.6356 A <--> 2.6488 A
          Mean   = 2.6414 A
          StdDev = 0.0041 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.992 deg; T1  -- T2  = 4.4246 A
T1  - O1  - T1  - O3  - T1  = 105.046 deg; T1  -- T1  = 4.8010 A
T1  - O1  - T1  - O4  - T1  = 120.654 deg; T1  -- T1  = 5.2775 A
T2  - O2  - T1  - O3  - T1  = 127.310 deg; T2  -- T1  = 5.5834 A
T2  - O2  - T1  - O4  - T1  =  90.029 deg; T2  -- T1  = 4.4253 A
T1  - O3  - T1  - O4  - T1  = 120.941 deg; T1  -- T1  = 5.2629 A

T1  - O4  - T2  - O5  - T2  = 127.405 deg; T1  -- T2  = 5.5874 A
T1  - O4  - T2  - O6  - T2  =  90.008 deg; T1  -- T2  = 4.4246 A
T1  - O4  - T2  - O7  - T2  =  89.971 deg; T1  -- T2  = 4.4253 A
T2  - O5  - T2  - O6  - T2  = 105.169 deg; T2  -- T2  = 4.8058 A
T2  - O5  - T2  - O7  - T2  = 120.846 deg; T2  -- T2  = 5.2650 A
T2  - O6  - T2  - O7  - T2  = 120.591 deg; T2  -- T2  = 5.2780 A

        T-T-T SUMMARY
          Range  = 89.9706 deg <--> 127.4046 deg
          Mean   = 108.1649 deg
          StdDev = 15.6691 deg

        T--T SUMMARY
          Range  = 4.4246 A <--> 5.5874 A
          Mean   = 4.9424 A
          StdDev = 0.4612 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.624 deg ; T1  -- T1   3.0121 A

T1  -- O2  -- T1  = 139.038 deg ; T1  -- T1   3.0376 A

T1  -- O3  -- T1  = 138.997 deg ; T1  -- T1   3.0365 A

T1  -- O4  -- T2  = 176.384 deg ; T1  -- T2   3.2176 A

T2  -- O5  -- T2  = 136.623 deg ; T2  -- T2   3.0141 A

T2  -- O6  -- T2  = 139.009 deg ; T2  -- T2   3.0367 A

T2  -- O7  -- T2  = 139.213 deg ; T2  -- T2   3.0398 A


        T-O-T SUMMARY
          Range  = 136.6232° <--> 176.3838 deg
          Mean   = 143.6981 deg
          StdDev = 13.4466 deg

        T--T SUMMARY
          Range  = 3.0121 A <--> 3.2176 A
          Mean   = 3.0563 A
          StdDev = 0.0670 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 37 57 81 110 143 180 223 269 319 375 435 499 567
TD10 = 867
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 24

<TD10> = 867.000
Average ring size = 5.8182