Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_123_5_170119_ebloOT.cif"

There are 64 T-atoms per unit cell
There are 128 O-atoms per unit cell

Framework density = 17.19 T-atoms per nm^3
Material density = 1.716 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6200 Angstrom
T1  -- O2  = 1.6195 Angstrom
T1  -- O3  = 1.6199 Angstrom
T1  -- O4  = 1.6184 Angstrom
      mean = 1.6195 Angstrom
        t1 = 0.006194  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001400  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6220 Angstrom
T2  -- O5  = 1.6216 Angstrom
T2  -- O6  = 1.6232 Angstrom
T2  -- O7  = 1.6219 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.007697  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001598  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6227 Angstrom
T3  -- O8  = 1.6222 Angstrom
T3  -- O9  = 1.6230 Angstrom
T3  -- O10 = 1.6218 Angstrom
      mean = 1.6225 Angstrom
        t1 = 0.007817  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001089  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6211 Angstrom
T4  -- O10 = 1.6211 Angstrom
T4  -- O11 = 1.6142 Angstrom
T4  -- O12 = 1.6207 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.005887  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001035  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6211 Angstrom
T5  -- O13 = 1.6138 Angstrom
T5  -- O14 = 1.6205 Angstrom
T5  -- O7  = 1.6211 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.005815  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000907  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6138 A <--> 1.6232 A
          Mean   = 1.6208 A
          StdDev = 0.0022 A

       t1 Range  = 0.0058 <-- 0.0067 --> 0.0078
       t2 Range  = 0.0009 <-- 0.0012 --> 0.0016

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.307 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.249 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.395 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.427 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.256 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.190 deg; O3  -- O4  = 3 A
       109.249 deg <-- 109.471 deg --> 110.190 deg

O3  -- T2  -- O5  = 109.817 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.091 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.301 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.488 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.796 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.330 deg; O6  -- O7  = 3 A
       109.091 deg <-- 109.471 deg --> 109.817 deg

O4  -- T3  -- O8  = 109.755 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.222 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.290 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.552 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.662 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.344 deg; O9  -- O10 = 3 A
       109.222 deg <-- 109.471 deg --> 109.755 deg

O10 -- T4  -- O10 = 109.625 deg; O10 -- O10 = 3 A
O10 -- T4  -- O11 = 109.459 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.417 deg; O10 -- O12 = 3 A
O10 -- T4  -- O11 = 109.459 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.417 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.451 deg; O11 -- O12 = 3 A
       109.417 deg <-- 109.471 deg --> 109.625 deg

O7  -- T5  -- O13 = 109.436 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 109.404 deg; O7  -- O14 = 3 A
O7  -- T5  -- O7  = 109.640 deg; O7  -- O7  = 3 A
O13 -- T5  -- O14 = 109.507 deg; O13 -- O14 = 3 A
O13 -- T5  -- O7  = 109.436 deg; O13 -- O7  = 3 A
O14 -- T5  -- O7  = 109.404 deg; O14 -- O7  = 3 A
       109.404 deg <-- 109.471 deg --> 109.640 deg

        O-T-O SUMMARY
          Range  = 109.0912 deg <--> 110.1905 deg
          Mean   = 109.4717 deg
          StdDev = 0.2242 deg

        O--O SUMMARY
          Range  = 2.6403 A <--> 2.6557 A
          Mean   = 2.6465 A
          StdDev = 0.0045 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  91.386 deg; T1  -- T2  = 4.2897 A
T1  - O1  - T1  - O3  - T3  = 113.354 deg; T1  -- T3  = 5.0084 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1944 A
T2  - O2  - T1  - O3  - T3  = 145.384 deg; T2  -- T3  = 5.7819 A
T2  - O2  - T1  - O4  - T1  = 113.345 deg; T2  -- T1  = 5.0085 A
T3  - O3  - T1  - O4  - T1  =  91.410 deg; T3  -- T1  = 4.2903 A

T1  - O3  - T2  - O5  - T2  =  88.614 deg; T1  -- T2  = 4.2897 A
T1  - O3  - T2  - O6  - T2  = 107.296 deg; T1  -- T2  = 4.8654 A
T1  - O3  - T2  - O7  - T5  =  94.803 deg; T1  -- T5  = 4.4691 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.6590 A
T2  - O5  - T2  - O7  - T5  =  91.082 deg; T2  -- T5  = 4.3936 A
T2  - O6  - T2  - O7  - T5  = 127.598 deg; T2  -- T5  = 5.4335 A

T1  - O4  - T3  - O8  - T3  = 107.320 deg; T1  -- T3  = 4.8641 A
T1  - O4  - T3  - O9  - T4  =  94.803 deg; T1  -- T4  = 4.4692 A
T1  - O4  - T3  - O10 - T3  =  88.590 deg; T1  -- T3  = 4.2903 A
T3  - O8  - T3  - O9  - T4  = 127.609 deg; T3  -- T4  = 5.4323 A
T3  - O8  - T3  - O10 - T3  = 135.000 deg; T3  -- T3  = 5.6594 A
T4  - O9  - T3  - O10 - T3  =  91.065 deg; T4  -- T3  = 4.3952 A

T3  - O10 - T4  - O10 - T3  = 123.682 deg; T3  -- T3  = 5.3664 A
T3  - O10 - T4  - O11 - T4  =  88.935 deg; T3  -- T4  = 4.3952 A
T3  - O10 - T4  - O12 - T4  = 118.135 deg; T3  -- T4  = 5.2186 A
T3  - O10 - T4  - O11 - T4  =  88.935 deg; T3  -- T4  = 4.3952 A
T3  - O10 - T4  - O12 - T4  = 118.135 deg; T3  -- T4  = 5.2186 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.4345 A

T2  - O7  - T5  - O13 - T5  =  88.918 deg; T2  -- T5  = 4.3936 A
T2  - O7  - T5  - O14 - T5  = 118.126 deg; T2  -- T5  = 5.2179 A
T2  - O7  - T5  - O7  - T2  = 123.699 deg; T2  -- T2  = 5.3659 A
T5  - O13 - T5  - O14 - T5  =  90.000 deg; T5  -- T5  = 4.4340 A
T5  - O13 - T5  - O7  - T2  =  88.918 deg; T5  -- T2  = 4.3936 A
T5  - O14 - T5  - O7  - T2  = 118.126 deg; T5  -- T2  = 5.2179 A

        T-T-T SUMMARY
          Range  = 88.5897 deg <--> 145.3842 deg
          Mean   = 106.5656 deg
          StdDev = 17.2346 deg

        T--T SUMMARY
          Range  = 4.1944 A <--> 5.7819 A
          Mean   = 4.8335 A
          StdDev = 0.4961 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.518 deg ; T1  -- T1   2.9659 A

T1  -- O2  -- T1  = 132.598 deg ; T1  -- T1   2.9659 A

T1  -- O3  -- T2  = 138.169 deg ; T1  -- T2   3.0283 A

T1  -- O4  -- T3  = 138.198 deg ; T1  -- T3   3.0278 A

T2  -- O5  -- T2  = 147.354 deg ; T2  -- T2   3.1124 A

T2  -- O6  -- T2  = 136.255 deg ; T2  -- T2   3.0128 A

T2  -- O7  -- T5  = 139.538 deg ; T2  -- T5   3.0429 A

T3  -- O8  -- T3  = 147.517 deg ; T3  -- T3   3.1149 A

T3  -- O9  -- T3  = 136.086 deg ; T3  -- T3   3.0106 A

T3  -- O10 -- T4  = 139.598 deg ; T3  -- T4   3.0434 A

T4  -- O11 -- T4  = 178.339 deg ; T4  -- T4   3.2281 A

T4  -- O12 -- T4  = 139.437 deg ; T4  -- T4   3.0405 A

T5  -- O13 -- T5  = 178.485 deg ; T5  -- T5   3.2273 A

T5  -- O14 -- T5  = 139.471 deg ; T5  -- T5   3.0405 A


        T-O-T SUMMARY
          Range  = 132.5177° <--> 178.4853 deg
          Mean   = 142.1413 deg
          StdDev = 11.8576 deg

        T--T SUMMARY
          Range  = 2.9659 A <--> 3.2281 A
          Mean   = 3.0494 A
          StdDev = 0.0696 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 15 28 50 74 100 128 170 216 250 288 346 412 468 522
TD10 = 795
Circuit symbol = 4.4.4.6.5.5
Weight = 15
Vertex symbol  = 4.4.4.6.5.5
Weight = 15

T2 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 31 50 76 103 133 166 207 255 304 350 400 463 532
TD10 = 800
Circuit symbol = 4.6.4.8.5.8_{2}
Weight = 22
Vertex symbol  = 4.6.4.8.5.8
Weight = 22

T3 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 19 31 50 76 103 133 166 207 255 304 350 400 463 532
TD10 = 800
Circuit symbol = 4.6.4.8.5.8_{2}
Weight = 22
Vertex symbol  = 4.6.4.8.5.8
Weight = 22

T4 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 34 52 71 95 129 173 210 239 284 356 426 468 511
TD10 = 796
Circuit symbol = 4.5.4.6.4.6
Weight = 10
Vertex symbol  = 4.5.4.8.4.8
Weight = 20

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 34 52 71 95 129 173 210 239 284 356 426 468 511
TD10 = 796
Circuit symbol = 4.5.4.6.4.6
Weight = 10
Vertex symbol  = 4.5.4.8.4.8
Weight = 20

<TD10> = 797.750
Average ring size = 5.0526