Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_123_3_449_c40A5x.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 14.88 T-atoms per nm^3
Material density = 1.485 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6250 Angstrom
T1  -- O2  = 1.6179 Angstrom
T1  -- O3  = 1.6158 Angstrom
T1  -- O4  = 1.6302 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.008070  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002540  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6190 Angstrom
T2  -- O3  = 1.6190 Angstrom
T2  -- O5  = 1.6192 Angstrom
T2  -- O6  = 1.6113 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004887  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001349  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6240 Angstrom
T3  -- O7  = 1.6180 Angstrom
T3  -- O8  = 1.6209 Angstrom
T3  -- O4  = 1.6240 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007980  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002463  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6113 A <--> 1.6302 A
          Mean   = 1.6208 A
          StdDev = 0.0051 A

       t1 Range  = 0.0049 <-- 0.0070 --> 0.0081
       t2 Range  = 0.0013 <-- 0.0021 --> 0.0025

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.929 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.177 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.458 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.212 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.970 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.061 deg; O3  -- O4  = 3 A
       108.458 deg <-- 109.468 deg --> 110.212 deg

O3  -- T2  -- O3  = 109.815 deg; O3  -- O3  = 3 A
O3  -- T2  -- O5  = 109.328 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.668 deg; O3  -- O6  = 3 A
O3  -- T2  -- O5  = 109.328 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.668 deg; O3  -- O6  = 3 A
O5  -- T2  -- O6  = 109.016 deg; O5  -- O6  = 3 A
       109.016 deg <-- 109.471 deg --> 109.815 deg

O4  -- T3  -- O7  = 109.742 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.719 deg; O4  -- O8  = 3 A
O4  -- T3  -- O4  = 108.053 deg; O4  -- O4  = 3 A
O7  -- T3  -- O8  = 109.840 deg; O7  -- O8  = 3 A
O7  -- T3  -- O4  = 109.742 deg; O7  -- O4  = 3 A
O8  -- T3  -- O4  = 109.719 deg; O8  -- O4  = 3 A
       108.053 deg <-- 109.469 deg --> 109.840 deg

        O-T-O SUMMARY
          Range  = 108.0528 deg <--> 110.2121 deg
          Mean   = 109.4587 deg
          StdDev = 0.5479 deg

        O--O SUMMARY
          Range  = 2.6285 A <--> 2.6602 A
          Mean   = 2.6462 A
          StdDev = 0.0079 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.810 deg; T1  -- T2  = 4.4480 A
T1  - O1  - T1  - O3  - T3  = 130.277 deg; T1  -- T3  = 5.6096 A
T1  - O1  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.6702 A
T2  - O2  - T1  - O3  - T3  = 128.870 deg; T2  -- T3  = 5.4320 A
T2  - O2  - T1  - O4  - T1  = 116.376 deg; T2  -- T1  = 5.0790 A
T3  - O3  - T1  - O4  - T1  =  60.506 deg; T3  -- T1  = 2.9518 A

T1  - O3  - T2  - O3  - T1  = 102.640 deg; T1  -- T1  = 4.7923 A
T1  - O3  - T2  - O5  - T2  = 116.076 deg; T1  -- T2  = 5.1735 A
T1  - O3  - T2  - O6  - T2  =  90.190 deg; T1  -- T2  = 4.4480 A
T1  - O3  - T2  - O5  - T2  = 116.076 deg; T1  -- T2  = 5.1735 A
T1  - O3  - T2  - O6  - T2  =  90.190 deg; T1  -- T2  = 4.4481 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.7632 A

T1  - O4  - T3  - O7  - T3  = 114.957 deg; T1  -- T3  = 5.2197 A
T1  - O4  - T3  - O8  - T1  =  58.987 deg; T1  -- T1  = 2.9065 A
T1  - O4  - T3  - O4  - T3  = 139.579 deg; T1  -- T3  = 5.6341 A
T3  - O7  - T3  - O8  - T1  = 114.957 deg; T3  -- T1  = 5.2197 A
T3  - O7  - T3  - O4  - T3  =  90.000 deg; T3  -- T3  = 4.4481 A
T1  - O8  - T3  - O4  - T3  = 139.579 deg; T1  -- T3  = 5.6341 A

        T-T-T SUMMARY
          Range  = 58.9872 deg <--> 139.5794 deg
          Mean   = 108.5437 deg
          StdDev = 24.9290 deg

        T--T SUMMARY
          Range  = 2.9065 A <--> 5.7632 A
          Mean   = 4.8494 A
          StdDev = 0.8461 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.838 deg ; T1  -- T1   2.9065 A

T1  -- O2  -- T1  = 172.823 deg ; T1  -- T1   3.2295 A

T1  -- O3  -- T2  = 143.203 deg ; T1  -- T2   3.0694 A

T1  -- O4  -- T3  = 130.208 deg ; T1  -- T3   2.9518 A

T2  -- O5  -- T2  = 138.508 deg ; T2  -- T2   3.0285 A

T2  -- O6  -- T2  = 169.523 deg ; T2  -- T2   3.2091 A

T3  -- O7  -- T3  = 179.738 deg ; T3  -- T3   3.2360 A

T3  -- O8  -- T3  = 140.581 deg ; T3  -- T3   3.0518 A


        T-O-T SUMMARY
          Range  = 126.8376° <--> 179.7378 deg
          Mean   = 147.8747 deg
          StdDev = 19.2985 deg

        T--T SUMMARY
          Range  = 2.9065 A <--> 3.2360 A
          Mean   = 3.0700 A
          StdDev = 0.1235 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 31 47 71 95 125 160 193 235 285 336 388 446 499
TD10 = 755
Circuit symbol = 3.4.6.8_{2}.6.8_{3}
Weight = 23
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 19 32 50 72 96 124 160 199 242 288 332 382 444 513
TD10 = 767
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 21
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 18 31 48 68 91 125 165 199 233 276 327 384 442 506
TD10 = 759
Circuit symbol = 3.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 3.4.6.8.6.8
Weight = 22

<TD10> = 759.000
Average ring size = 5.1892