Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_123_3_363_LeopyX.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 18.59 T-atoms per nm^3
Material density = 1.855 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6223 Angstrom
T1  -- O2  = 1.6163 Angstrom
T1  -- O3  = 1.6163 Angstrom
T1  -- O4  = 1.6168 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005179  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001135  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6191 Angstrom
T2  -- O5  = 1.6224 Angstrom
T2  -- O6  = 1.6150 Angstrom
T2  -- O3  = 1.6191 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.005559  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000622  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6196 Angstrom
T3  -- O4  = 1.6196 Angstrom
T3  -- O7  = 1.6217 Angstrom
T3  -- O8  = 1.6149 Angstrom
      mean = 1.6190 Angstrom
        t1 = 0.005610  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000465  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6149 A <--> 1.6224 A
          Mean   = 1.6184 A
          StdDev = 0.0026 A

       t1 Range  = 0.0052 <-- 0.0054 --> 0.0056
       t2 Range  = 0.0005 <-- 0.0007 --> 0.0011

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.570 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.203 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.170 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.879 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.845 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.156 deg; O3  -- O4  = 3 A
       109.156 deg <-- 109.470 deg --> 109.879 deg

O3  -- T2  -- O5  = 109.246 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.770 deg; O3  -- O6  = 3 A
O3  -- T2  -- O3  = 109.245 deg; O3  -- O3  = 3 A
O5  -- T2  -- O6  = 109.548 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 109.246 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 109.770 deg; O6  -- O3  = 3 A
       109.245 deg <-- 109.471 deg --> 109.770 deg

O4  -- T3  -- O4  = 109.256 deg; O4  -- O4  = 3 A
O4  -- T3  -- O7  = 109.239 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.766 deg; O4  -- O8  = 3 A
O4  -- T3  -- O7  = 109.239 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 109.766 deg; O4  -- O8  = 3 A
O7  -- T3  -- O8  = 109.560 deg; O7  -- O8  = 3 A
       109.239 deg <-- 109.471 deg --> 109.766 deg

        O-T-O SUMMARY
          Range  = 109.1558 deg <--> 109.8791 deg
          Mean   = 109.4597 deg
          StdDev = 0.2781 deg

        O--O SUMMARY
          Range  = 2.6347 A <--> 2.6460 A
          Mean   = 2.6429 A
          StdDev = 0.0031 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.7514 A
T1  - O1  - T1  - O3  - T2  = 111.160 deg; T1  -- T2  = 5.0058 A
T1  - O1  - T1  - O4  - T3  = 111.293 deg; T1  -- T3  = 5.0066 A
T1  - O2  - T1  - O3  - T2  =  89.975 deg; T1  -- T2  = 4.4555 A
T1  - O2  - T1  - O4  - T3  =  89.987 deg; T1  -- T3  = 4.4533 A
T2  - O3  - T1  - O4  - T3  = 118.446 deg; T2  -- T3  = 5.2755 A

T1  - O3  - T2  - O5  - T2  =  90.025 deg; T1  -- T2  = 4.4555 A
T1  - O3  - T2  - O6  - T2  = 111.122 deg; T1  -- T2  = 5.0055 A
T1  - O3  - T2  - O3  - T1  = 118.664 deg; T1  -- T1  = 5.2847 A
T2  - O5  - T2  - O6  - T2  = 135.000 deg; T2  -- T2  = 5.7498 A
T2  - O5  - T2  - O3  - T1  =  90.025 deg; T2  -- T1  = 4.4555 A
T2  - O6  - T2  - O3  - T1  = 111.122 deg; T2  -- T1  = 5.0055 A

T1  - O4  - T3  - O4  - T1  = 118.229 deg; T1  -- T1  = 5.2662 A
T1  - O4  - T3  - O7  - T3  =  90.013 deg; T1  -- T3  = 4.4533 A
T1  - O4  - T3  - O8  - T3  = 111.273 deg; T1  -- T3  = 4.9968 A
T1  - O4  - T3  - O7  - T3  =  90.013 deg; T1  -- T3  = 4.4533 A
T1  - O4  - T3  - O8  - T3  = 111.273 deg; T1  -- T3  = 4.9968 A
T3  - O7  - T3  - O8  - T3  = 135.000 deg; T3  -- T3  = 5.7397 A

        T-T-T SUMMARY
          Range  = 89.9747 deg <--> 135.0000 deg
          Mean   = 106.1014 deg
          StdDev = 13.7271 deg

        T--T SUMMARY
          Range  = 4.4533 A <--> 5.7514 A
          Mean   = 4.8949 A
          StdDev = 0.3878 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.847 deg ; T1  -- T1   2.9960 A

T1  -- O2  -- T1  = 174.278 deg ; T1  -- T1   3.2285 A

T1  -- O3  -- T2  = 143.429 deg ; T1  -- T2   3.0720 A

T1  -- O4  -- T3  = 142.884 deg ; T1  -- T3   3.0682 A

T2  -- O5  -- T2  = 134.930 deg ; T2  -- T2   2.9970 A

T2  -- O6  -- T2  = 174.166 deg ; T2  -- T2   3.2258 A

T3  -- O7  -- T3  = 133.922 deg ; T3  -- T3   2.9848 A

T3  -- O8  -- T3  = 175.199 deg ; T3  -- T3   3.2271 A


        T-O-T SUMMARY
          Range  = 133.9216° <--> 175.1985 deg
          Mean   = 150.7577 deg
          StdDev = 17.2252 deg

        T--T SUMMARY
          Range  = 2.9848 A <--> 3.2285 A
          Mean   = 3.0970 A
          StdDev = 0.0980 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{5}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 833.000
Average ring size = 5.3333