Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_123_2_29p_vM62ip.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 16.85 T-atoms per nm^3
Material density = 1.681 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6146 Angstrom
T1  -- O1  = 1.6146 Angstrom
T1  -- O2  = 1.6216 Angstrom
T1  -- O3  = 1.6122 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.005794  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003560  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6123 Angstrom
T2  -- O4  = 1.6229 Angstrom
T2  -- O4  = 1.6229 Angstrom
T2  -- O5  = 1.6102 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.006130  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003322  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6102 A <--> 1.6229 A
          Mean   = 1.6164 A
          StdDev = 0.0049 A

       t1 Range  = 0.0058 <-- 0.0060 --> 0.0061
       t2 Range  = 0.0033 <-- 0.0034 --> 0.0036

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 110.070 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.768 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.664 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.768 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.664 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.885 deg; O2  -- O3  = 3 A
       108.664 deg <-- 109.470 deg --> 110.070 deg

O3  -- T2  -- O4  = 109.916 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.916 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 108.684 deg; O3  -- O5  = 3 A
O4  -- T2  -- O4  = 109.553 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.376 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.376 deg; O4  -- O5  = 3 A
       108.684 deg <-- 109.470 deg --> 109.916 deg

        O-T-O SUMMARY
          Range  = 108.6644 deg <--> 110.0696 deg
          Mean   = 109.4700 deg
          StdDev = 0.5065 deg

        O--O SUMMARY
          Range  = 2.6183 A <--> 2.6515 A
          Mean   = 2.6396 A
          StdDev = 0.0118 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O1  - T1  = 126.981 deg; T2  -- T1  = 5.6516 A
T2  - O1  - T1  - O2  - T1  = 126.981 deg; T2  -- T1  = 5.6516 A
T2  - O1  - T1  - O3  - T1  = 121.711 deg; T2  -- T1  = 5.4109 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4370 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3524 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3524 A

T1  - O3  - T2  - O4  - T2  = 126.981 deg; T1  -- T2  = 5.5289 A
T1  - O3  - T2  - O4  - T2  = 126.981 deg; T1  -- T2  = 5.5289 A
T1  - O3  - T2  - O5  - T2  = 121.711 deg; T1  -- T2  = 5.5838 A
T2  - O4  - T2  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.2423 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3972 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.3972 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 126.9806 deg
          Mean   = 107.6120 deg
          StdDev = 17.7923 deg

        T--T SUMMARY
          Range  = 4.2423 A <--> 5.6516 A
          Mean   = 4.9612 A
          StdDev = 0.6057 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 152.620 deg ; T1  -- T1   3.1375 A

T1  -- O2  -- T1  = 136.894 deg ; T1  -- T1   3.0165 A

T1  -- O3  -- T2  = 160.547 deg ; T1  -- T2   3.1781 A

T2  -- O4  -- T2  = 135.096 deg ; T2  -- T2   2.9998 A

T2  -- O5  -- T2  = 173.400 deg ; T2  -- T2   3.2151 A


        T-O-T SUMMARY
          Range  = 135.0963° <--> 173.3999 deg
          Mean   = 151.7114 deg
          StdDev = 14.6402 deg

        T--T SUMMARY
          Range  = 2.9998 A <--> 3.2151 A
          Mean   = 3.1094 A
          StdDev = 0.0875 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 9 19 35 52 72 100 131 163 201 244 290 340 393 451 515
TD10 = 787
Circuit symbol = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29
Vertex symbol  = 4.8_{2}.4.8_{2}.4.8_{2}
Weight = 29

<TD10> = 787.000
Average ring size = 6.0000