Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_121_2_9927_tMJ9Vh.cif"

There are 20 T-atoms per unit cell
There are 40 O-atoms per unit cell

Framework density = 17.24 T-atoms per nm^3
Material density = 1.720 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6157 Angstrom
T1  -- O3  = 1.6208 Angstrom
T1  -- O4  = 1.5856 Angstrom
T1  -- O2  = 1.6295 Angstrom
      mean = 1.6129 Angstrom
        t1 = 0.006227  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008148  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6166 Angstrom
T2  -- O4  = 1.6166 Angstrom
T2  -- O4  = 1.6166 Angstrom
T2  -- O4  = 1.6166 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.007201  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006467  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5856 A <--> 1.6295 A
          Mean   = 1.6136 A
          StdDev = 0.0149 A

       t1 Range  = 0.0062 <-- 0.0067 --> 0.0072
       t2 Range  = 0.0065 <-- 0.0073 --> 0.0081

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.452 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.845 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.055 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.952 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.388 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 110.130 deg; O4  -- O2  = 3 A
       108.845 deg <-- 109.470 deg --> 110.130 deg

O4  -- T2  -- O4  = 110.148 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 108.127 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 110.148 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 110.148 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 108.127 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 110.148 deg; O4  -- O4  = 3 A
       108.127 deg <-- 109.474 deg --> 110.148 deg

        O-T-O SUMMARY
          Range  = 108.1265 deg <--> 110.1477 deg
          Mean   = 109.4970 deg
          StdDev = 0.7944 deg

        O--O SUMMARY
          Range  = 2.6037 A <--> 2.6525 A
          Mean   = 2.6356 A
          StdDev = 0.0166 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 129.352 deg; T1  -- T2  = 5.5046 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1510 A
T1  - O1  - T1  - O2  - T1  =  90.047 deg; T1  -- T1  = 4.3635 A
T2  - O3  - T1  - O4  - T1  = 129.290 deg; T2  -- T1  = 5.5080 A
T2  - O3  - T1  - O2  - T1  = 116.344 deg; T2  -- T1  = 5.4252 A
T1  - O4  - T1  - O2  - T1  =  89.953 deg; T1  -- T1  = 4.3635 A

T1  - O4  - T2  - O4  - T1  = 101.357 deg; T1  -- T1  = 4.8835 A
T1  - O4  - T2  - O4  - T1  = 127.312 deg; T1  -- T1  = 5.6571 A
T1  - O4  - T2  - O4  - T1  = 101.357 deg; T1  -- T1  = 4.8835 A
T1  - O4  - T2  - O4  - T1  = 101.357 deg; T1  -- T1  = 4.8835 A
T1  - O4  - T2  - O4  - T1  = 127.312 deg; T1  -- T1  = 5.6571 A
T1  - O4  - T2  - O4  - T1  = 101.357 deg; T1  -- T1  = 4.8835 A

        T-T-T SUMMARY
          Range  = 89.9532 deg <--> 129.3523 deg
          Mean   = 108.3017 deg
          StdDev = 15.3157 deg

        T--T SUMMARY
          Range  = 4.1510 A <--> 5.6571 A
          Mean   = 5.0017 A
          StdDev = 0.5107 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 175.428 deg ; T1  -- T1   3.2288 A

T1  -- O2  -- T1  = 128.696 deg ; T1  -- T1   2.9378 A

T1  -- O3  -- T1  = 129.558 deg ; T1  -- T1   2.9326 A

T1  -- O4  -- T2  = 160.583 deg ; T1  -- T2   3.1564 A


        T-O-T SUMMARY
          Range  = 128.6956° <--> 175.4284 deg
          Mean   = 148.5662 deg
          StdDev = 20.2971 deg

        T--T SUMMARY
          Range  = 2.9326 A <--> 3.2288 A
          Mean   = 3.0639 A
          StdDev = 0.1323 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 16
Coordination Sequence =
    1 4 9 19 34 48 66 96 127 151 183 232 281 316 357 427 499
TD10 = 738
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 18 28 52 78 88 112 162 204 220 254 328 396 414 448
TD10 = 759
Circuit symbol = 6.6.6.6.6.6
Weight = 23
Vertex symbol  = 6.6.6.6.6.6
Weight = 23

<TD10> = 742.200
Average ring size = 5.0000