Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_121_2_10829_Kp3Ndf.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.04 T-atoms per nm^3
Material density = 1.800 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O2  = 1.6098 Angstrom
T1  -- O3  = 1.6102 Angstrom
      mean = 1.6126 Angstrom
        t1 = 0.003842  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002215  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O3  = 1.6102 Angstrom
T2  -- O4  = 1.6151 Angstrom
T2  -- O4  = 1.6151 Angstrom
      mean = 1.6126 Angstrom
        t1 = 0.003819  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002201  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6098 A <--> 1.6152 A
          Mean   = 1.6126 A
          StdDev = 0.0026 A

       t1 Range  = 0.0038 <-- 0.0038 --> 0.0038
       t2 Range  = 0.0022 <-- 0.0022 --> 0.0022

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 110.429 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.437 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.041 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.437 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.041 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.439 deg; O2  -- O3  = 3 A
       109.041 deg <-- 109.471 deg --> 110.429 deg

O2  -- T2  -- O3  = 109.439 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.437 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.437 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.044 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.044 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 110.423 deg; O4  -- O4  = 3 A
       109.044 deg <-- 109.471 deg --> 110.423 deg

        O-T-O SUMMARY
          Range  = 109.0408 deg <--> 110.4289 deg
          Mean   = 109.4706 deg
          StdDev = 0.4648 deg

        O--O SUMMARY
          Range  = 2.6265 A <--> 2.6531 A
          Mean   = 2.6333 A
          StdDev = 0.0092 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O1  - T1  = 110.097 deg; T2  -- T1  = 5.2008 A
T2  - O1  - T1  - O2  - T1  = 110.097 deg; T2  -- T1  = 5.2008 A
T2  - O1  - T1  - O3  - T2  = 109.480 deg; T2  -- T2  = 5.2584 A
T1  - O1  - T1  - O2  - T1  =  83.219 deg; T1  -- T1  = 4.1508 A
T1  - O1  - T1  - O3  - T2  = 120.761 deg; T1  -- T2  = 5.5166 A
T1  - O2  - T1  - O3  - T2  = 120.761 deg; T1  -- T2  = 5.5166 A

T1  - O2  - T2  - O3  - T1  = 109.480 deg; T1  -- T1  = 5.2584 A
T1  - O2  - T2  - O4  - T2  = 110.097 deg; T1  -- T2  = 5.2008 A
T1  - O2  - T2  - O4  - T2  = 110.097 deg; T1  -- T2  = 5.2008 A
T1  - O3  - T2  - O4  - T2  = 120.761 deg; T1  -- T2  = 5.5166 A
T1  - O3  - T2  - O4  - T2  = 120.761 deg; T1  -- T2  = 5.5166 A
T2  - O4  - T2  - O4  - T2  =  83.219 deg; T2  -- T2  = 4.1508 A

        T-T-T SUMMARY
          Range  = 83.2195 deg <--> 120.7610 deg
          Mean   = 109.0692 deg
          StdDev = 12.6083 deg

        T--T SUMMARY
          Range  = 4.1508 A <--> 5.5166 A
          Mean   = 5.1407 A
          StdDev = 0.4650 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 150.702 deg ; T1  -- T1   3.1253 A

T1  -- O2  -- T2  = 179.918 deg ; T1  -- T2   3.2196 A

T1  -- O3  -- T2  = 180.000 deg ; T1  -- T2   3.2203 A

T2  -- O4  -- T2  = 150.709 deg ; T2  -- T2   3.1253 A


        T-O-T SUMMARY
          Range  = 150.7018° <--> 180.0000 deg
          Mean   = 165.3322 deg
          StdDev = 14.8610 deg

        T--T SUMMARY
          Range  = 3.1253 A <--> 3.2203 A
          Mean   = 3.1726 A
          StdDev = 0.0481 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 39 60 86 116 151 190 235 284 338 396 459 526 599
TD10 = 915
Circuit symbol = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22
Vertex symbol  = 4.6_{2}.6.6_{3}.6.6_{3}
Weight = 22

<TD10> = 915.000
Average ring size = 5.7391