Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_16003_8onfS_.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 23.76 T-atoms per nm^3
Material density = 2.371 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6154 Angstrom
T1  -- O2  = 1.6214 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6224 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006440  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001359  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6179 Angstrom
T2  -- O4  = 1.6217 Angstrom
T2  -- O5  = 1.6220 Angstrom
T2  -- O3  = 1.6213 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.006746  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000885  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6224 A
          Mean   = 1.6204 A
          StdDev = 0.0023 A

       t1 Range  = 0.0064 <-- 0.0066 --> 0.0067
       t2 Range  = 0.0009 <-- 0.0011 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.186 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.417 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.841 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.498 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.369 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.516 deg; O3  -- O4  = 3 A
       109.186 deg <-- 109.471 deg --> 109.841 deg

O2  -- T2  -- O4  = 109.370 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.396 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.620 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.685 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.392 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.365 deg; O5  -- O3  = 3 A
       109.365 deg <-- 109.471 deg --> 109.685 deg

        O-T-O SUMMARY
          Range  = 109.1856 deg <--> 109.8409 deg
          Mean   = 109.4712 deg
          StdDev = 0.1690 deg

        O--O SUMMARY
          Range  = 2.6382 A <--> 2.6520 A
          Mean   = 2.6461 A
          StdDev = 0.0036 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  =  94.793 deg; T2  -- T1  = 4.6059 A
T2  - O1  - T1  - O3  - T2  = 112.527 deg; T2  -- T2  = 5.0207 A
T2  - O1  - T1  - O4  - T2  = 103.361 deg; T2  -- T2  = 4.7417 A
T1  - O2  - T1  - O3  - T2  = 102.131 deg; T1  -- T2  = 4.8592 A
T1  - O2  - T1  - O4  - T2  = 130.208 deg; T1  -- T2  = 5.6706 A
T2  - O3  - T1  - O4  - T2  = 112.357 deg; T2  -- T2  = 5.0125 A

T1  - O2  - T2  - O4  - T2  = 109.441 deg; T1  -- T2  = 4.9346 A
T1  - O2  - T2  - O5  - T1  = 103.361 deg; T1  -- T1  = 4.7417 A
T1  - O2  - T2  - O3  - T1  = 112.527 deg; T1  -- T1  = 5.0207 A
T2  - O4  - T2  - O5  - T1  = 109.467 deg; T2  -- T1  = 4.9322 A
T2  - O4  - T2  - O3  - T1  = 109.510 deg; T2  -- T1  = 4.9283 A
T1  - O5  - T2  - O3  - T1  = 112.357 deg; T1  -- T1  = 5.0125 A

        T-T-T SUMMARY
          Range  = 94.7930 deg <--> 130.2079 deg
          Mean   = 109.3367 deg
          StdDev = 8.2983 deg

        T--T SUMMARY
          Range  = 4.6059 A <--> 5.6706 A
          Mean   = 4.9567 A
          StdDev = 0.2528 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2308 A

T1  -- O2  -- T2  = 137.965 deg ; T1  -- T2   3.0238 A

T1  -- O3  -- T2  = 136.697 deg ; T1  -- T2   3.0136 A

T1  -- O4  -- T2  = 137.152 deg ; T1  -- T2   3.0199 A

T2  -- O5  -- T2  = 137.259 deg ; T2  -- T2   3.0209 A


        T-O-T SUMMARY
          Range  = 136.6968° <--> 180.0000 deg
          Mean   = 145.8147 deg
          StdDev = 17.5417 deg

        T--T SUMMARY
          Range  = 3.0136 A <--> 3.2308 A
          Mean   = 3.0618 A
          StdDev = 0.0868 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000