Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15906_DO9bbC.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 25.98 T-atoms per nm^3
Material density = 2.592 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6644 Angstrom
T1  -- O2  = 1.6159 Angstrom
T1  -- O3  = 1.6020 Angstrom
T1  -- O4  = 1.5962 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.066619  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042385  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6057 Angstrom
T2  -- O3  = 1.5988 Angstrom
T2  -- O2  = 1.6752 Angstrom
T2  -- O4  = 1.5986 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.066879  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.078415  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5962 A <--> 1.6752 A
          Mean   = 1.6196 A
          StdDev = 0.0301 A

       t1 Range  = 0.0666 <-- 0.0667 --> 0.0669
       t2 Range  = 0.0424 <-- 0.0604 --> 0.0784

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 125.753 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.070 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.541 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  97.665 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  =  97.958 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  = 118.221 deg; O3  -- O4  = 3 A
       97.665 deg <-- 109.535 deg --> 125.753 deg

O5  -- T2  -- O3  =  98.287 deg; O5  -- O3  = 2 A
O5  -- T2  -- O2  = 125.155 deg; O5  -- O2  = 3 A
O5  -- T2  -- O4  =  97.568 deg; O5  -- O4  = 2 A
O3  -- T2  -- O2  = 108.620 deg; O3  -- O2  = 3 A
O3  -- T2  -- O4  = 117.952 deg; O3  -- O4  = 3 A
O2  -- T2  -- O4  = 109.507 deg; O2  -- O4  = 3 A
       97.568 deg <-- 109.515 deg --> 125.155 deg

        O-T-O SUMMARY
          Range  = 97.5675 deg <--> 125.7529 deg
          Mean   = 109.5247 deg
          StdDev = 10.1058 deg

        O--O SUMMARY
          Range  = 2.4104 A <--> 2.9196 A
          Mean   = 2.6365 A
          StdDev = 0.1772 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.105 deg; T1  -- T2  = 4.5059 A
T1  - O1  - T1  - O3  - T2  = 151.286 deg; T1  -- T2  = 6.1139 A
T1  - O1  - T1  - O4  - T2  =  91.417 deg; T1  -- T2  = 4.5684 A
T2  - O2  - T1  - O3  - T2  = 100.957 deg; T2  -- T2  = 4.6379 A
T2  - O2  - T1  - O4  - T2  = 128.828 deg; T2  -- T2  = 5.4823 A
T2  - O3  - T1  - O4  - T2  = 101.603 deg; T2  -- T2  = 4.6725 A

T2  - O5  - T2  - O3  - T1  = 107.713 deg; T2  -- T1  = 5.0323 A
T2  - O5  - T2  - O2  - T1  = 108.119 deg; T2  -- T1  = 4.9925 A
T2  - O5  - T2  - O4  - T1  = 107.815 deg; T2  -- T1  = 5.0221 A
T1  - O3  - T2  - O2  - T1  = 101.603 deg; T1  -- T1  = 4.6725 A
T1  - O3  - T2  - O4  - T1  = 128.828 deg; T1  -- T1  = 5.4823 A
T1  - O2  - T2  - O4  - T1  = 100.957 deg; T1  -- T1  = 4.6379 A

        T-T-T SUMMARY
          Range  = 90.1051 deg <--> 151.2859 deg
          Mean   = 109.9360 deg
          StdDev = 17.1916 deg

        T--T SUMMARY
          Range  = 4.5059 A <--> 6.1139 A
          Mean   = 4.9850 A
          StdDev = 0.4715 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.3288 A

T1  -- O2  -- T2  = 129.895 deg ; T1  -- T2   2.9816 A

T1  -- O3  -- T2  = 144.405 deg ; T1  -- T2   3.0476 A

T1  -- O4  -- T2  = 143.111 deg ; T1  -- T2   3.0307 A

T2  -- O5  -- T2  = 164.812 deg ; T2  -- T2   3.1832 A


        T-O-T SUMMARY
          Range  = 129.8950° <--> 180.0000 deg
          Mean   = 152.4448 deg
          StdDev = 18.1947 deg

        T--T SUMMARY
          Range  = 2.9816 A <--> 3.3288 A
          Mean   = 3.1144 A
          StdDev = 0.1296 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 442 503 563 623
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 441 503 563 623
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000