Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15874_S9WTKM.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.22 T-atoms per nm^3
Material density = 2.217 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6162 Angstrom
T1  -- O2  = 1.6227 Angstrom
T1  -- O3  = 1.6195 Angstrom
T1  -- O4  = 1.6218 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006362  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001396  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6220 Angstrom
T2  -- O4  = 1.6207 Angstrom
T2  -- O5  = 1.6156 Angstrom
T2  -- O3  = 1.6193 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006123  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001220  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6156 A <--> 1.6227 A
          Mean   = 1.6197 A
          StdDev = 0.0025 A

       t1 Range  = 0.0061 <-- 0.0062 --> 0.0064
       t2 Range  = 0.0012 <-- 0.0013 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.481 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.388 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.417 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.488 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.545 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.508 deg; O3  -- O4  = 3 A
       109.388 deg <-- 109.471 deg --> 109.545 deg

O2  -- T2  -- O4  = 109.643 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.643 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 109.705 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 109.276 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.188 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 109.370 deg; O5  -- O3  = 3 A
       109.188 deg <-- 109.471 deg --> 109.705 deg

        O-T-O SUMMARY
          Range  = 109.1883 deg <--> 109.7053 deg
          Mean   = 109.4710 deg
          StdDev = 0.1485 deg

        O--O SUMMARY
          Range  = 2.6393 A <--> 2.6505 A
          Mean   = 2.6450 A
          StdDev = 0.0041 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 108.268 deg; T2  -- T1  = 5.0852 A
T2  - O1  - T1  - O3  - T2  = 108.593 deg; T2  -- T2  = 4.9209 A
T2  - O1  - T1  - O4  - T2  = 107.633 deg; T2  -- T2  = 4.9118 A
T1  - O2  - T1  - O3  - T2  = 110.562 deg; T1  -- T2  = 5.1397 A
T1  - O2  - T1  - O4  - T2  = 113.502 deg; T1  -- T2  = 5.2504 A
T2  - O3  - T1  - O4  - T2  = 108.144 deg; T2  -- T2  = 4.9098 A

T1  - O2  - T2  - O4  - T2  = 110.742 deg; T1  -- T2  = 5.1577 A
T1  - O2  - T2  - O5  - T1  = 107.633 deg; T1  -- T1  = 4.9118 A
T1  - O2  - T2  - O3  - T1  = 108.593 deg; T1  -- T1  = 4.9209 A
T2  - O4  - T2  - O5  - T1  = 110.717 deg; T2  -- T1  = 5.1597 A
T2  - O4  - T2  - O3  - T1  = 110.901 deg; T2  -- T1  = 5.1446 A
T1  - O5  - T2  - O3  - T1  = 108.144 deg; T1  -- T1  = 4.9098 A

        T-T-T SUMMARY
          Range  = 107.6331 deg <--> 113.5022 deg
          Mean   = 109.4527 deg
          StdDev = 1.7482 deg

        T--T SUMMARY
          Range  = 4.9098 A <--> 5.2504 A
          Mean   = 5.0352 A
          StdDev = 0.1272 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2325 A

T1  -- O2  -- T2  = 139.185 deg ; T1  -- T2   3.0410 A

T1  -- O3  -- T2  = 140.098 deg ; T1  -- T2   3.0445 A

T1  -- O4  -- T2  = 137.187 deg ; T1  -- T2   3.0188 A

T2  -- O5  -- T2  = 173.312 deg ; T2  -- T2   3.2258 A


        T-O-T SUMMARY
          Range  = 137.1868° <--> 180.0000 deg
          Mean   = 153.9565 deg
          StdDev = 19.1633 deg

        T--T SUMMARY
          Range  = 3.0188 A <--> 3.2325 A
          Mean   = 3.1125 A
          StdDev = 0.0981 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000