Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15857_GKXISB.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.99 T-atoms per nm^3
Material density = 1.795 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6154 Angstrom
T1  -- O2  = 1.6145 Angstrom
T1  -- O4  = 1.6214 Angstrom
T1  -- O3  = 1.6197 Angstrom
      mean = 1.6177 Angstrom
        t1 = 0.005083  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001035  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6151 Angstrom
T2  -- O6  = 1.6171 Angstrom
T2  -- O4  = 1.6215 Angstrom
T2  -- O3  = 1.6193 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.005275  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000842  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6145 A <--> 1.6215 A
          Mean   = 1.6180 A
          StdDev = 0.0027 A

       t1 Range  = 0.0051 <-- 0.0052 --> 0.0053
       t2 Range  = 0.0008 <-- 0.0009 --> 0.0010

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.409 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.382 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.326 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.434 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.562 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.714 deg; O4  -- O3  = 3 A
       109.326 deg <-- 109.471 deg --> 109.714 deg

O5  -- T2  -- O6  = 109.489 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.371 deg; O5  -- O4  = 3 A
O5  -- T2  -- O3  = 109.312 deg; O5  -- O3  = 3 A
O6  -- T2  -- O4  = 109.512 deg; O6  -- O4  = 3 A
O6  -- T2  -- O3  = 109.728 deg; O6  -- O3  = 3 A
O4  -- T2  -- O3  = 109.415 deg; O4  -- O3  = 3 A
       109.312 deg <-- 109.471 deg --> 109.728 deg

        O-T-O SUMMARY
          Range  = 109.3116 deg <--> 109.7282 deg
          Mean   = 109.4731 deg
          StdDev = 0.1384 deg

        O--O SUMMARY
          Range  = 2.6362 A <--> 2.6503 A
          Mean   = 2.6426 A
          StdDev = 0.0037 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 110.411 deg; T1  -- T1  = 5.3037 A
T1  - O1  - T1  - O4  - T2  =  90.046 deg; T1  -- T2  = 4.4470 A
T1  - O1  - T1  - O3  - T2  = 111.769 deg; T1  -- T2  = 5.1832 A
T1  - O2  - T1  - O4  - T2  = 124.182 deg; T1  -- T2  = 5.5567 A
T1  - O2  - T1  - O3  - T2  = 124.486 deg; T1  -- T2  = 5.5426 A
T2  - O4  - T1  - O3  - T2  =  90.076 deg; T2  -- T2  = 4.3078 A

T2  - O5  - T2  - O6  - T2  = 110.322 deg; T2  -- T2  = 5.3044 A
T2  - O5  - T2  - O4  - T1  = 111.769 deg; T2  -- T1  = 5.1873 A
T2  - O5  - T2  - O3  - T1  =  89.954 deg; T2  -- T1  = 4.4470 A
T2  - O6  - T2  - O4  - T1  = 124.755 deg; T2  -- T1  = 5.5489 A
T2  - O6  - T2  - O3  - T1  = 124.132 deg; T2  -- T1  = 5.5549 A
T1  - O4  - T2  - O3  - T1  =  89.924 deg; T1  -- T1  = 4.3021 A

        T-T-T SUMMARY
          Range  = 89.9244 deg <--> 124.7554 deg
          Mean   = 108.3147 deg
          StdDev = 14.9530 deg

        T--T SUMMARY
          Range  = 4.3021 A <--> 5.5567 A
          Mean   = 5.0347 A
          StdDev = 0.5229 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2308 A

T1  -- O2  -- T1  = 176.736 deg ; T1  -- T1   3.2277 A

T1  -- O3  -- T2  = 141.346 deg ; T1  -- T2   3.0565 A

T1  -- O4  -- T2  = 138.404 deg ; T1  -- T2   3.0316 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2303 A

T2  -- O6  -- T2  = 176.261 deg ; T2  -- T2   3.2325 A


        T-O-T SUMMARY
          Range  = 138.4036° <--> 180.0000 deg
          Mean   = 165.4577 deg
          StdDev = 18.5574 deg

        T--T SUMMARY
          Range  = 3.0316 A <--> 3.2325 A
          Mean   = 3.1682 A
          StdDev = 0.0900 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182