Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15852_pZZ4bO.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 24.82 T-atoms per nm^3
Material density = 2.476 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6586 Angstrom
T1  -- O2  = 1.6842 Angstrom
T1  -- O3  = 1.5784 Angstrom
T1  -- O4  = 1.6089 Angstrom
      mean = 1.6325 Angstrom
        t1 = 0.080217  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.055460  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6371 Angstrom
T2  -- O5  = 1.6113 Angstrom
T2  -- O6  = 1.5929 Angstrom
T2  -- O3  = 1.6891 Angstrom
      mean = 1.6326 Angstrom
        t1 = 0.048573  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033048  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5784 A <--> 1.6891 A
          Mean   = 1.6326 A
          StdDev = 0.0395 A

       t1 Range  = 0.0486 <-- 0.0644 --> 0.0802
       t2 Range  = 0.0330 <-- 0.0443 --> 0.0555

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 116.718 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 116.283 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.019 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 104.555 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 120.977 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  89.619 deg; O3  -- O4  = 2 A
       89.619 deg <-- 109.029 deg --> 120.977 deg

O4  -- T2  -- O5  = 103.050 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.042 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 117.018 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 103.679 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 116.894 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 108.013 deg; O6  -- O3  = 3 A
       103.050 deg <-- 109.283 deg --> 117.018 deg

        O-T-O SUMMARY
          Range  = 89.6192 deg <--> 120.9765 deg
          Mean   = 109.0608 deg
          StdDev = 8.6881 deg

        O--O SUMMARY
          Range  = 2.2463 A <--> 2.8661 A
          Mean   = 2.6529 A
          StdDev = 0.1749 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 119.351 deg; T1  -- T1  = 5.4952 A
T1  - O1  - T1  - O3  - T2  =  88.610 deg; T1  -- T2  = 4.2736 A
T1  - O1  - T1  - O4  - T2  = 125.558 deg; T1  -- T2  = 5.3101 A
T1  - O2  - T1  - O3  - T2  =  95.967 deg; T1  -- T2  = 4.7493 A
T1  - O2  - T1  - O4  - T2  = 113.628 deg; T1  -- T2  = 5.2279 A
T2  - O3  - T1  - O4  - T2  =  74.075 deg; T2  -- T2  = 3.6133 A

T2  - O4  - T2  - O5  - T1  = 125.558 deg; T2  -- T1  = 5.1773 A
T2  - O4  - T2  - O6  - T2  = 123.422 deg; T2  -- T2  = 5.3917 A
T2  - O4  - T2  - O3  - T1  =  91.390 deg; T2  -- T1  = 4.2736 A
T1  - O5  - T2  - O6  - T2  = 104.909 deg; T1  -- T2  = 4.8769 A
T1  - O5  - T2  - O3  - T1  = 105.925 deg; T1  -- T1  = 4.7867 A
T2  - O6  - T2  - O3  - T1  =  98.338 deg; T2  -- T1  = 4.7633 A

        T-T-T SUMMARY
          Range  = 74.0753 deg <--> 125.5584 deg
          Mean   = 104.9638 deg
          StdDev = 16.4221 deg

        T--T SUMMARY
          Range  = 3.6133 A <--> 5.4952 A
          Mean   = 4.7957 A
          StdDev = 0.5410 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.3173 A

T1  -- O2  -- T1  = 129.529 deg ; T1  -- T1   3.0470 A

T1  -- O3  -- T2  = 140.083 deg ; T1  -- T2   3.0714 A

T1  -- O4  -- T2  = 128.534 deg ; T1  -- T2   2.9241 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2225 A

T2  -- O6  -- T2  = 130.909 deg ; T2  -- T2   2.8980 A


        T-O-T SUMMARY
          Range  = 128.5336° <--> 180.0000 deg
          Mean   = 148.1759 deg
          StdDev = 23.3040 deg

        T--T SUMMARY
          Range  = 2.8980 A <--> 3.3173 A
          Mean   = 3.0800 A
          StdDev = 0.1533 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.2463 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182