Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15845_kHXGZe.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.73 T-atoms per nm^3
Material density = 1.968 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5896 Angstrom
T1  -- O2  = 1.6446 Angstrom
T1  -- O3  = 1.6009 Angstrom
T1  -- O4  = 1.5899 Angstrom
      mean = 1.6062 Angstrom
        t1 = 0.026634  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032594  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6105 Angstrom
T2  -- O5  = 1.6119 Angstrom
T2  -- O6  = 1.6490 Angstrom
T2  -- O3  = 1.6181 Angstrom
      mean = 1.6224 Angstrom
        t1 = 0.038930  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024237  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5896 A <--> 1.6490 A
          Mean   = 1.6143 A
          StdDev = 0.0214 A

       t1 Range  = 0.0266 <-- 0.0328 --> 0.0389
       t2 Range  = 0.0242 <-- 0.0284 --> 0.0326

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.715 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.525 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.688 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.043 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.427 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.205 deg; O3  -- O4  = 3 A
       103.525 deg <-- 109.434 deg --> 113.043 deg

O4  -- T2  -- O5  =  98.335 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 108.892 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 110.307 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 116.192 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 113.391 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 109.135 deg; O6  -- O3  = 3 A
       98.335 deg <-- 109.375 deg --> 116.192 deg

        O-T-O SUMMARY
          Range  = 98.3350 deg <--> 116.1920 deg
          Mean   = 108.9456 deg
          StdDev = 4.4945 deg

        O--O SUMMARY
          Range  = 2.4381 A <--> 2.7684 A
          Mean   = 2.6245 A
          StdDev = 0.0864 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 142.349 deg; T1  -- T1  = 5.6736 A
T1  - O1  - T1  - O3  - T2  =  90.543 deg; T1  -- T2  = 4.2513 A
T1  - O1  - T1  - O4  - T2  =  90.553 deg; T1  -- T2  = 4.2093 A
T1  - O2  - T1  - O3  - T2  =  99.640 deg; T1  -- T2  = 4.8434 A
T1  - O2  - T1  - O4  - T2  = 118.893 deg; T1  -- T2  = 5.4104 A
T2  - O3  - T1  - O4  - T2  = 109.879 deg; T2  -- T2  = 5.1272 A

T2  - O4  - T2  - O5  - T1  =  89.447 deg; T2  -- T1  = 4.2093 A
T2  - O4  - T2  - O6  - T2  = 139.656 deg; T2  -- T2  = 5.7249 A
T2  - O4  - T2  - O3  - T1  =  89.457 deg; T2  -- T1  = 4.2513 A
T1  - O5  - T2  - O6  - T2  = 122.218 deg; T1  -- T2  = 5.5401 A
T1  - O5  - T2  - O3  - T1  = 109.879 deg; T1  -- T1  = 5.1272 A
T2  - O6  - T2  - O3  - T1  = 100.573 deg; T2  -- T1  = 4.9111 A

        T-T-T SUMMARY
          Range  = 89.4469 deg <--> 142.3488 deg
          Mean   = 106.4366 deg
          StdDev = 17.2915 deg

        T--T SUMMARY
          Range  = 4.2093 A <--> 5.7249 A
          Mean   = 4.8793 A
          StdDev = 0.5576 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1791 A

T1  -- O2  -- T1  = 117.622 deg ; T1  -- T1   2.8139 A

T1  -- O3  -- T2  = 149.210 deg ; T1  -- T2   3.1035 A

T1  -- O4  -- T2  = 161.830 deg ; T1  -- T2   3.1602 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2238 A

T2  -- O6  -- T2  = 121.235 deg ; T2  -- T2   2.8738 A


        T-O-T SUMMARY
          Range  = 117.6217° <--> 180.0000 deg
          Mean   = 151.6494 deg
          StdDev = 25.7074 deg

        T--T SUMMARY
          Range  = 2.8139 A <--> 3.2238 A
          Mean   = 3.0590 A
          StdDev = 0.1606 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 170 202 228 253 277 299 325 351
TD10 = 818
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 170 202 228 253 277 299 325 351
TD10 = 818
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 818.000
Average ring size = 5.6000