Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15843_MdRZ4T.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.57 T-atoms per nm^3
Material density = 1.753 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6187 Angstrom
T1  -- O2  = 1.6232 Angstrom
T1  -- O4  = 1.6121 Angstrom
T1  -- O3  = 1.6225 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.006347  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003308  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6238 Angstrom
T2  -- O4  = 1.6089 Angstrom
T2  -- O6  = 1.6139 Angstrom
T2  -- O5  = 1.6171 Angstrom
      mean = 1.6159 Angstrom
        t1 = 0.006773  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004123  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6089 A <--> 1.6238 A
          Mean   = 1.6175 A
          StdDev = 0.0053 A

       t1 Range  = 0.0063 <-- 0.0066 --> 0.0068
       t2 Range  = 0.0033 <-- 0.0037 --> 0.0041

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.555 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.133 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.275 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.527 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.906 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.428 deg; O4  -- O3  = 3 A
       109.133 deg <-- 109.471 deg --> 109.906 deg

O3  -- T2  -- O4  = 109.738 deg; O3  -- O4  = 3 A
O3  -- T2  -- O6  = 109.688 deg; O3  -- O6  = 3 A
O3  -- T2  -- O5  = 110.581 deg; O3  -- O5  = 3 A
O4  -- T2  -- O6  = 108.733 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 109.411 deg; O4  -- O5  = 3 A
O6  -- T2  -- O5  = 108.655 deg; O6  -- O5  = 3 A
       108.655 deg <-- 109.468 deg --> 110.581 deg

        O-T-O SUMMARY
          Range  = 108.6551 deg <--> 110.5809 deg
          Mean   = 109.5023 deg
          StdDev = 0.4890 deg

        O--O SUMMARY
          Range  = 2.6194 A <--> 2.6642 A
          Mean   = 2.6418 A
          StdDev = 0.0122 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 115.132 deg; T1  -- T1  = 5.3975 A
T1  - O1  - T1  - O4  - T2  = 115.434 deg; T1  -- T2  = 5.3882 A
T1  - O1  - T1  - O3  - T2  =  89.882 deg; T1  -- T2  = 4.3440 A
T1  - O2  - T1  - O4  - T2  = 112.060 deg; T1  -- T2  = 5.3519 A
T1  - O2  - T1  - O3  - T2  = 131.411 deg; T1  -- T2  = 5.6769 A
T2  - O4  - T1  - O3  - T2  =  90.148 deg; T2  -- T2  = 4.3968 A

T2  - O3  - T2  - O4  - T1  = 115.434 deg; T2  -- T1  = 5.3778 A
T2  - O3  - T2  - O6  - T2  = 115.400 deg; T2  -- T2  = 5.3924 A
T2  - O3  - T2  - O5  - T1  =  90.118 deg; T2  -- T1  = 4.3440 A
T1  - O4  - T2  - O6  - T2  = 110.891 deg; T1  -- T2  = 5.3122 A
T1  - O4  - T2  - O5  - T1  =  89.852 deg; T1  -- T1  = 4.3855 A
T2  - O6  - T2  - O5  - T1  = 132.574 deg; T2  -- T1  = 5.6995 A

        T-T-T SUMMARY
          Range  = 89.8523 deg <--> 132.5744 deg
          Mean   = 107.6802 deg
          StdDev = 14.8183 deg

        T--T SUMMARY
          Range  = 4.3440 A <--> 5.6995 A
          Mean   = 5.0471 A
          StdDev = 0.5308 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2374 A

T1  -- O2  -- T1  = 153.109 deg ; T1  -- T1   3.1574 A

T1  -- O3  -- T2  = 134.160 deg ; T1  -- T2   2.9900 A

T1  -- O4  -- T2  = 173.557 deg ; T1  -- T2   3.2159 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2342 A

T2  -- O6  -- T2  = 153.989 deg ; T2  -- T2   3.1451 A


        T-O-T SUMMARY
          Range  = 134.1597° <--> 180.0000 deg
          Mean   = 162.4693 deg
          StdDev = 17.1871 deg

        T--T SUMMARY
          Range  = 2.9900 A <--> 3.2374 A
          Mean   = 3.1633 A
          StdDev = 0.0872 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 267 311 350 385 419 451
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 313 351 386 420 450
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182