Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15841_7OmXzH.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.47 T-atoms per nm^3
Material density = 1.743 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6153 Angstrom
T1  -- O2  = 1.6175 Angstrom
T1  -- O3  = 1.6140 Angstrom
T1  -- O4  = 1.6154 Angstrom
      mean = 1.6155 Angstrom
        t1 = 0.004356  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003020  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6161 Angstrom
T2  -- O6  = 1.6190 Angstrom
T2  -- O4  = 1.6145 Angstrom
T2  -- O3  = 1.6168 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.005143  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003290  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6140 A <--> 1.6190 A
          Mean   = 1.6161 A
          StdDev = 0.0016 A

       t1 Range  = 0.0044 <-- 0.0047 --> 0.0051
       t2 Range  = 0.0030 <-- 0.0032 --> 0.0033

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.389 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.919 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.072 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.129 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.461 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.850 deg; O3  -- O4  = 3 A
       108.919 deg <-- 109.470 deg --> 110.129 deg

O5  -- T2  -- O6  = 109.304 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.928 deg; O5  -- O4  = 3 A
O5  -- T2  -- O3  = 109.098 deg; O5  -- O3  = 3 A
O6  -- T2  -- O4  = 109.329 deg; O6  -- O4  = 3 A
O6  -- T2  -- O3  = 110.224 deg; O6  -- O3  = 3 A
O4  -- T2  -- O3  = 109.935 deg; O4  -- O3  = 3 A
       108.928 deg <-- 109.470 deg --> 110.224 deg

        O-T-O SUMMARY
          Range  = 108.9191 deg <--> 110.2240 deg
          Mean   = 109.4811 deg
          StdDev = 0.4619 deg

        O--O SUMMARY
          Range  = 2.6277 A <--> 2.6542 A
          Mean   = 2.6390 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 114.279 deg; T1  -- T1  = 5.3887 A
T1  - O1  - T1  - O3  - T2  = 115.170 deg; T1  -- T2  = 5.3234 A
T1  - O1  - T1  - O4  - T2  =  90.015 deg; T1  -- T2  = 4.4619 A
T1  - O2  - T1  - O3  - T2  = 118.940 deg; T1  -- T2  = 5.4718 A
T1  - O2  - T1  - O4  - T2  = 123.312 deg; T1  -- T2  = 5.5936 A
T2  - O3  - T1  - O4  - T2  =  89.955 deg; T2  -- T2  = 4.4149 A

T2  - O5  - T2  - O6  - T1  = 115.170 deg; T2  -- T1  = 5.3248 A
T2  - O5  - T2  - O4  - T2  = 114.235 deg; T2  -- T2  = 5.3899 A
T2  - O5  - T2  - O3  - T1  =  89.985 deg; T2  -- T1  = 4.4619 A
T1  - O6  - T2  - O4  - T2  = 118.843 deg; T1  -- T2  = 5.4703 A
T1  - O6  - T2  - O3  - T1  =  90.045 deg; T1  -- T1  = 4.4184 A
T2  - O4  - T2  - O3  - T1  = 123.464 deg; T2  -- T1  = 5.5989 A

        T-T-T SUMMARY
          Range  = 89.9552 deg <--> 123.4643 deg
          Mean   = 108.0626 deg
          StdDev = 14.1175 deg

        T--T SUMMARY
          Range  = 4.4149 A <--> 5.5989 A
          Mean   = 5.0874 A
          StdDev = 0.5026 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2307 A

T1  -- O2  -- T1  = 159.719 deg ; T1  -- T1   3.1844 A

T1  -- O3  -- T2  = 150.539 deg ; T1  -- T2   3.1246 A

T1  -- O4  -- T2  = 150.228 deg ; T1  -- T2   3.1215 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2321 A

T2  -- O6  -- T2  = 159.437 deg ; T2  -- T2   3.1860 A


        T-O-T SUMMARY
          Range  = 150.2276° <--> 180.0000 deg
          Mean   = 163.3205 deg
          StdDev = 12.6439 deg

        T--T SUMMARY
          Range  = 3.1215 A <--> 3.2321 A
          Mean   = 3.1799 A
          StdDev = 0.0454 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182