Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15837_RmpNe5.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.82 T-atoms per nm^3
Material density = 1.778 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6152 Angstrom
T1  -- O2  = 1.6158 Angstrom
T1  -- O3  = 1.6216 Angstrom
T1  -- O4  = 1.6189 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.007708  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007296  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6169 Angstrom
T2  -- O5  = 1.6153 Angstrom
T2  -- O6  = 1.6158 Angstrom
T2  -- O3  = 1.6235 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005378  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001929  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6235 A
          Mean   = 1.6179 A
          StdDev = 0.0030 A

       t1 Range  = 0.0054 <-- 0.0065 --> 0.0077
       t2 Range  = 0.0019 <-- 0.0046 --> 0.0073

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.244 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.025 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.962 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.372 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.437 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.773 deg; O3  -- O4  = 3 A
       107.962 deg <-- 109.469 deg --> 111.025 deg

O4  -- T2  -- O5  = 109.450 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.285 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 109.861 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 109.270 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 109.472 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 109.488 deg; O6  -- O3  = 3 A
       109.270 deg <-- 109.471 deg --> 109.861 deg

        O-T-O SUMMARY
          Range  = 107.9623 deg <--> 111.0252 deg
          Mean   = 109.4893 deg
          StdDev = 0.6836 deg

        O--O SUMMARY
          Range  = 2.6158 A <--> 2.6679 A
          Mean   = 2.6426 A
          StdDev = 0.0124 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 110.137 deg; T1  -- T2  = 5.2054 A
T1  - O1  - T1  - O3  - T1  = 109.405 deg; T1  -- T1  = 5.2739 A
T1  - O1  - T1  - O4  - T2  =  90.002 deg; T1  -- T2  = 4.3928 A
T2  - O2  - T1  - O3  - T1  = 120.457 deg; T2  -- T1  = 5.5102 A
T2  - O2  - T1  - O4  - T2  =  89.952 deg; T2  -- T2  = 4.3077 A
T1  - O3  - T1  - O4  - T2  = 132.276 deg; T1  -- T2  = 5.6764 A

T2  - O4  - T2  - O5  - T2  = 109.400 deg; T2  -- T2  = 5.2741 A
T2  - O4  - T2  - O6  - T1  = 110.137 deg; T2  -- T1  = 5.2056 A
T2  - O4  - T2  - O3  - T1  =  89.998 deg; T2  -- T1  = 4.3928 A
T2  - O5  - T2  - O6  - T1  = 121.797 deg; T2  -- T1  = 5.5468 A
T2  - O5  - T2  - O3  - T1  = 130.536 deg; T2  -- T1  = 5.6379 A
T1  - O6  - T2  - O3  - T1  =  90.048 deg; T1  -- T1  = 4.3113 A

        T-T-T SUMMARY
          Range  = 89.9522 deg <--> 132.2757 deg
          Mean   = 108.0161 deg
          StdDev = 15.7134 deg

        T--T SUMMARY
          Range  = 4.3077 A <--> 5.6764 A
          Mean   = 5.0326 A
          StdDev = 0.5428 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2303 A

T1  -- O2  -- T1  = 179.677 deg ; T1  -- T1   3.2315 A

T1  -- O3  -- T2  = 132.969 deg ; T1  -- T2   2.9755 A

T1  -- O4  -- T2  = 148.899 deg ; T1  -- T2   3.1173 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2306 A

T2  -- O6  -- T2  = 179.549 deg ; T2  -- T2   3.2317 A


        T-O-T SUMMARY
          Range  = 132.9689° <--> 180.0000 deg
          Mean   = 166.8491 deg
          StdDev = 19.2999 deg

        T--T SUMMARY
          Range  = 2.9755 A <--> 3.2317 A
          Mean   = 3.1695 A
          StdDev = 0.0982 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182