Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15833_XqkxOz.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 18.24 T-atoms per nm^3
Material density = 1.820 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6140 Angstrom
T1  -- O2  = 1.6158 Angstrom
T1  -- O3  = 1.6167 Angstrom
T1  -- O4  = 1.6175 Angstrom
      mean = 1.6160 Angstrom
        t1 = 0.004604  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002436  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6166 Angstrom
T2  -- O5  = 1.6161 Angstrom
T2  -- O6  = 1.6164 Angstrom
T2  -- O3  = 1.6175 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.004735  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002507  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6140 A <--> 1.6175 A
          Mean   = 1.6163 A
          StdDev = 0.0010 A

       t1 Range  = 0.0046 <-- 0.0047 --> 0.0047
       t2 Range  = 0.0024 <-- 0.0025 --> 0.0025

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.505 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.090 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.041 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.077 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.953 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.152 deg; O3  -- O4  = 3 A
       109.041 deg <-- 109.470 deg --> 110.077 deg

O4  -- T2  -- O5  = 108.991 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.007 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 109.304 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 109.516 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 109.117 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 109.885 deg; O6  -- O3  = 3 A
       108.991 deg <-- 109.470 deg --> 110.007 deg

        O-T-O SUMMARY
          Range  = 108.9910 deg <--> 110.0772 deg
          Mean   = 109.4662 deg
          StdDev = 0.4176 deg

        O--O SUMMARY
          Range  = 2.6315 A <--> 2.6492 A
          Mean   = 2.6395 A
          StdDev = 0.0071 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 114.985 deg; T1  -- T1  = 5.4352 A
T1  - O1  - T1  - O3  - T2  =  90.014 deg; T1  -- T2  = 4.4628 A
T1  - O1  - T1  - O4  - T2  =  90.014 deg; T1  -- T2  = 4.4585 A
T1  - O2  - T1  - O3  - T2  = 118.065 deg; T1  -- T2  = 5.4201 A
T1  - O2  - T1  - O4  - T2  = 118.300 deg; T1  -- T2  = 5.4214 A
T2  - O3  - T1  - O4  - T2  = 117.180 deg; T2  -- T2  = 5.2733 A

T2  - O4  - T2  - O5  - T2  = 114.922 deg; T2  -- T2  = 5.4380 A
T2  - O4  - T2  - O6  - T1  =  89.986 deg; T2  -- T1  = 4.4585 A
T2  - O4  - T2  - O3  - T1  =  89.986 deg; T2  -- T1  = 4.4628 A
T2  - O5  - T2  - O6  - T1  = 118.435 deg; T2  -- T1  = 5.4289 A
T2  - O5  - T2  - O3  - T1  = 117.987 deg; T2  -- T1  = 5.4214 A
T1  - O6  - T2  - O3  - T1  = 117.180 deg; T1  -- T1  = 5.2733 A

        T-T-T SUMMARY
          Range  = 89.9864 deg <--> 118.4354 deg
          Mean   = 107.3042 deg
          StdDev = 13.2705 deg

        T--T SUMMARY
          Range  = 4.4585 A <--> 5.4380 A
          Mean   = 5.0475 A
          StdDev = 0.4522 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2281 A

T1  -- O2  -- T1  = 169.035 deg ; T1  -- T1   3.2169 A

T1  -- O3  -- T2  = 145.212 deg ; T1  -- T2   3.0863 A

T1  -- O4  -- T2  = 145.965 deg ; T1  -- T2   3.0924 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2322 A

T2  -- O6  -- T2  = 169.171 deg ; T2  -- T2   3.2184 A


        T-O-T SUMMARY
          Range  = 145.2116° <--> 180.0000 deg
          Mean   = 164.8971 deg
          StdDev = 14.6705 deg

        T--T SUMMARY
          Range  = 3.0863 A <--> 3.2322 A
          Mean   = 3.1791 A
          StdDev = 0.0650 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000