Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15827_oynEHE.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 17.77 T-atoms per nm^3
Material density = 1.773 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6163 Angstrom
T1  -- O2  = 1.6123 Angstrom
T1  -- O3  = 1.6207 Angstrom
T1  -- O4  = 1.6199 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.006663  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006191  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6235 Angstrom
T2  -- O5  = 1.6144 Angstrom
T2  -- O6  = 1.6202 Angstrom
T2  -- O4  = 1.6149 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.006149  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003198  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6123 A <--> 1.6235 A
          Mean   = 1.6178 A
          StdDev = 0.0036 A

       t1 Range  = 0.0061 <-- 0.0064 --> 0.0067
       t2 Range  = 0.0032 <-- 0.0047 --> 0.0062

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.087 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.728 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.642 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.350 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.097 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.908 deg; O3  -- O4  = 3 A
       108.642 deg <-- 109.469 deg --> 110.728 deg

O3  -- T2  -- O5  = 109.601 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.718 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.724 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.558 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 108.692 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.530 deg; O6  -- O4  = 3 A
       108.692 deg <-- 109.470 deg --> 109.724 deg

        O-T-O SUMMARY
          Range  = 108.6420 deg <--> 110.7284 deg
          Mean   = 109.4830 deg
          StdDev = 0.5659 deg

        O--O SUMMARY
          Range  = 2.6240 A <--> 2.6634 A
          Mean   = 2.6423 A
          StdDev = 0.0115 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.146 deg; T1  -- T2  = 4.3944 A
T1  - O1  - T1  - O3  - T2  = 110.388 deg; T1  -- T2  = 5.2125 A
T1  - O1  - T1  - O4  - T1  = 109.814 deg; T1  -- T1  = 5.2833 A
T2  - O2  - T1  - O3  - T2  =  89.710 deg; T2  -- T2  = 4.3044 A
T2  - O2  - T1  - O4  - T1  = 132.195 deg; T2  -- T1  = 5.6785 A
T2  - O3  - T1  - O4  - T1  = 120.092 deg; T2  -- T1  = 5.5075 A

T1  - O3  - T2  - O5  - T2  =  89.854 deg; T1  -- T2  = 4.3944 A
T1  - O3  - T2  - O6  - T1  =  90.290 deg; T1  -- T1  = 4.3262 A
T1  - O3  - T2  - O4  - T2  = 130.814 deg; T1  -- T2  = 5.6443 A
T2  - O5  - T2  - O6  - T1  = 110.388 deg; T2  -- T1  = 5.2251 A
T2  - O5  - T2  - O4  - T2  = 109.552 deg; T2  -- T2  = 5.2841 A
T1  - O6  - T2  - O4  - T2  = 121.181 deg; T1  -- T2  = 5.5340 A

        T-T-T SUMMARY
          Range  = 89.7101 deg <--> 132.1946 deg
          Mean   = 109.4688 deg
          StdDev = 15.4113 deg

        T--T SUMMARY
          Range  = 4.3044 A <--> 5.6785 A
          Mean   = 5.0890 A
          StdDev = 0.5327 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2327 A

T1  -- O2  -- T1  = 178.546 deg ; T1  -- T1   3.2244 A

T1  -- O3  -- T2  = 133.205 deg ; T1  -- T2   2.9774 A

T1  -- O4  -- T2  = 149.860 deg ; T1  -- T2   3.1235 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2289 A

T2  -- O6  -- T2  = 177.572 deg ; T2  -- T2   3.2396 A


        T-O-T SUMMARY
          Range  = 133.2052° <--> 180.0000 deg
          Mean   = 166.5306 deg
          StdDev = 18.7321 deg

        T--T SUMMARY
          Range  = 2.9774 A <--> 3.2396 A
          Mean   = 3.1711 A
          StdDev = 0.0973 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 37 57 81 109 142 180 222 268 318 373 433 497 565
TD10 = 864
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 23
Vertex symbol  = 4.6.4.6.6.8_{3}
Weight = 23

<TD10> = 864.000
Average ring size = 5.8182