Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15825_hEs_3O.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.63 T-atoms per nm^3
Material density = 2.258 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6226 Angstrom
T1  -- O2  = 1.6194 Angstrom
T1  -- O3  = 1.6177 Angstrom
T1  -- O4  = 1.6224 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.012180  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014361  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6346 Angstrom
T2  -- O5  = 1.6324 Angstrom
T2  -- O6  = 1.6232 Angstrom
T2  -- O4  = 1.6506 Angstrom
      mean = 1.6352 Angstrom
        t1 = 0.022499  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011457  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6177 A <--> 1.6506 A
          Mean   = 1.6279 A
          StdDev = 0.0104 A

       t1 Range  = 0.0122 <-- 0.0173 --> 0.0225
       t2 Range  = 0.0115 <-- 0.0129 --> 0.0144

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.111 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.829 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.949 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.377 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.392 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.123 deg; O3  -- O4  = 3 A
       107.123 deg <-- 109.464 deg --> 112.829 deg

O3  -- T2  -- O5  = 107.531 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.738 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 108.193 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 108.868 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 114.701 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 108.671 deg; O6  -- O4  = 3 A
       107.531 deg <-- 109.450 deg --> 114.701 deg

        O-T-O SUMMARY
          Range  = 107.1226 deg <--> 114.7008 deg
          Mean   = 109.4995 deg
          StdDev = 2.1833 deg

        O--O SUMMARY
          Range  = 2.6066 A <--> 2.7643 A
          Mean   = 2.6588 A
          StdDev = 0.0400 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.147 deg; T1  -- T2  = 4.1441 A
T1  - O1  - T1  - O3  - T1  = 130.368 deg; T1  -- T1  = 5.6853 A
T1  - O1  - T1  - O4  - T2  =  90.147 deg; T1  -- T2  = 4.1492 A
T2  - O2  - T1  - O3  - T1  = 134.673 deg; T2  -- T1  = 5.6107 A
T2  - O2  - T1  - O4  - T2  = 109.067 deg; T2  -- T2  = 4.6201 A
T1  - O3  - T1  - O4  - T2  =  92.397 deg; T1  -- T2  = 4.4009 A

T1  - O3  - T2  - O5  - T2  =  89.853 deg; T1  -- T2  = 4.1441 A
T1  - O3  - T2  - O6  - T2  =  91.467 deg; T1  -- T2  = 4.3768 A
T1  - O3  - T2  - O4  - T1  = 109.067 deg; T1  -- T1  = 4.6201 A
T2  - O5  - T2  - O6  - T2  = 129.742 deg; T2  -- T2  = 5.7019 A
T2  - O5  - T2  - O4  - T1  =  89.853 deg; T2  -- T1  = 4.1492 A
T2  - O6  - T2  - O4  - T1  = 136.071 deg; T2  -- T1  = 5.6640 A

        T-T-T SUMMARY
          Range  = 89.8530 deg <--> 136.0706 deg
          Mean   = 107.5369 deg
          StdDev = 19.0215 deg

        T--T SUMMARY
          Range  = 4.1441 A <--> 5.7019 A
          Mean   = 4.7585 A
          StdDev = 0.6449 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2452 A

T1  -- O2  -- T1  = 137.413 deg ; T1  -- T1   3.0176 A

T1  -- O3  -- T2  = 121.136 deg ; T1  -- T2   2.8326 A

T1  -- O4  -- T2  = 120.388 deg ; T1  -- T2   2.8401 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2648 A

T2  -- O6  -- T2  = 138.147 deg ; T2  -- T2   3.0322 A


        T-O-T SUMMARY
          Range  = 120.3882° <--> 180.0000 deg
          Mean   = 146.1806 deg
          StdDev = 25.4402 deg

        T--T SUMMARY
          Range  = 2.8326 A <--> 3.2648 A
          Mean   = 3.0387 A
          StdDev = 0.1750 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000