Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_15824_TPfr_n.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 19.17 T-atoms per nm^3
Material density = 1.913 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6155 Angstrom
T1  -- O2  = 1.6207 Angstrom
T1  -- O3  = 1.6185 Angstrom
T1  -- O4  = 1.6219 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.005722  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000672  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6181 Angstrom
T2  -- O5  = 1.6160 Angstrom
T2  -- O6  = 1.6209 Angstrom
T2  -- O4  = 1.6221 Angstrom
      mean = 1.6193 Angstrom
        t1 = 0.005931  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001034  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6155 A <--> 1.6221 A
          Mean   = 1.6192 A
          StdDev = 0.0024 A

       t1 Range  = 0.0057 <-- 0.0058 --> 0.0059
       t2 Range  = 0.0007 <-- 0.0009 --> 0.0010

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.474 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.556 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.640 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.518 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.377 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.261 deg; O3  -- O4  = 3 A
       109.261 deg <-- 109.471 deg --> 109.640 deg

O3  -- T2  -- O5  = 109.274 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.578 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.684 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.401 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.519 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.372 deg; O6  -- O4  = 3 A
       109.274 deg <-- 109.471 deg --> 109.684 deg

        O-T-O SUMMARY
          Range  = 109.2609 deg <--> 109.6837 deg
          Mean   = 109.4742 deg
          StdDev = 0.1367 deg

        O--O SUMMARY
          Range  = 2.6374 A <--> 2.6491 A
          Mean   = 2.6443 A
          StdDev = 0.0031 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.981 deg; T1  -- T2  = 4.3225 A
T1  - O1  - T1  - O3  - T1  = 128.675 deg; T1  -- T1  = 5.6538 A
T1  - O1  - T1  - O4  - T2  =  89.981 deg; T1  -- T2  = 4.2737 A
T2  - O2  - T1  - O3  - T1  =  98.961 deg; T2  -- T1  = 4.7934 A
T2  - O2  - T1  - O4  - T2  = 111.242 deg; T2  -- T2  = 5.0157 A
T1  - O3  - T1  - O4  - T2  = 131.065 deg; T1  -- T2  = 5.6760 A

T1  - O3  - T2  - O5  - T2  =  90.019 deg; T1  -- T2  = 4.3225 A
T1  - O3  - T2  - O6  - T1  = 111.242 deg; T1  -- T1  = 5.0157 A
T1  - O3  - T2  - O4  - T2  = 124.630 deg; T1  -- T2  = 5.5837 A
T2  - O5  - T2  - O6  - T1  =  90.019 deg; T2  -- T1  = 4.2737 A
T2  - O5  - T2  - O4  - T2  = 128.708 deg; T2  -- T2  = 5.6536 A
T1  - O6  - T2  - O4  - T2  = 106.981 deg; T1  -- T2  = 5.0141 A

        T-T-T SUMMARY
          Range  = 89.9807 deg <--> 131.0653 deg
          Mean   = 110.1369 deg
          StdDev = 15.8200 deg

        T--T SUMMARY
          Range  = 4.2737 A <--> 5.6760 A
          Mean   = 5.0273 A
          StdDev = 0.5428 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2310 A

T1  -- O2  -- T1  = 139.475 deg ; T1  -- T1   3.0408 A

T1  -- O3  -- T2  = 143.420 deg ; T1  -- T2   3.0731 A

T1  -- O4  -- T2  = 135.652 deg ; T1  -- T2   3.0041 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2320 A

T2  -- O6  -- T2  = 139.237 deg ; T2  -- T2   3.0388 A


        T-O-T SUMMARY
          Range  = 135.6525° <--> 180.0000 deg
          Mean   = 152.9641 deg
          StdDev = 19.6626 deg

        T--T SUMMARY
          Range  = 3.0041 A <--> 3.2320 A
          Mean   = 3.1033 A
          StdDev = 0.0948 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 541
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 476 539
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000