Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_11_2_14927_CbDbYZ.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 27.12 T-atoms per nm^3
Material density = 2.706 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6456 Angstrom
T1  -- O3  = 1.6191 Angstrom
T1  -- O4  = 1.5755 Angstrom
T1  -- O2  = 1.6267 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.041128  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038377  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6392 Angstrom
T2  -- O3  = 1.6299 Angstrom
T2  -- O5  = 1.6389 Angstrom
T2  -- O4  = 1.6442 Angstrom
      mean = 1.6381 Angstrom
        t1 = 0.024911  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015552  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5755 A <--> 1.6456 A
          Mean   = 1.6274 A
          StdDev = 0.0217 A

       t1 Range  = 0.0249 <-- 0.0330 --> 0.0411
       t2 Range  = 0.0156 <-- 0.0270 --> 0.0384

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 114.304 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 102.695 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 116.593 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 105.238 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 111.723 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 104.634 deg; O4  -- O2  = 3 A
       102.695 deg <-- 109.198 deg --> 116.593 deg

O2  -- T2  -- O3  = 104.029 deg; O2  -- O3  = 3 A
O2  -- T2  -- O5  = 112.112 deg; O2  -- O5  = 3 A
O2  -- T2  -- O4  = 109.530 deg; O2  -- O4  = 3 A
O3  -- T2  -- O5  = 112.136 deg; O3  -- O5  = 3 A
O3  -- T2  -- O4  = 110.693 deg; O3  -- O4  = 3 A
O5  -- T2  -- O4  = 108.304 deg; O5  -- O4  = 3 A
       104.029 deg <-- 109.467 deg --> 112.136 deg

        O-T-O SUMMARY
          Range  = 102.6948 deg <--> 116.5928 deg
          Mean   = 109.3325 deg
          StdDev = 4.2547 deg

        O--O SUMMARY
          Range  = 2.5159 A <--> 2.7840 A
          Mean   = 2.6539 A
          StdDev = 0.0868 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  =  77.916 deg; T1  -- T2  = 3.8163 A
T1  - O1  - T1  - O4  - T2  = 132.391 deg; T1  -- T2  = 5.8382 A
T1  - O1  - T1  - O2  - T2  = 113.466 deg; T1  -- T2  = 5.2047 A
T2  - O3  - T1  - O4  - T2  = 100.516 deg; T2  -- T2  = 4.4878 A
T2  - O3  - T1  - O2  - T2  = 109.199 deg; T2  -- T2  = 4.6222 A
T2  - O4  - T1  - O2  - T2  = 111.806 deg; T2  -- T2  = 4.9844 A

T2  - O2  - T2  - O3  - T1  = 111.489 deg; T2  -- T1  = 4.9110 A
T2  - O2  - T2  - O5  - T1  = 110.324 deg; T2  -- T1  = 5.0082 A
T2  - O2  - T2  - O4  - T1  = 113.054 deg; T2  -- T1  = 4.8006 A
T1  - O3  - T2  - O5  - T1  = 111.806 deg; T1  -- T1  = 4.9844 A
T1  - O3  - T2  - O4  - T1  = 109.199 deg; T1  -- T1  = 4.6222 A
T1  - O5  - T2  - O4  - T1  = 100.516 deg; T1  -- T1  = 4.4878 A

        T-T-T SUMMARY
          Range  = 77.9160 deg <--> 132.3905 deg
          Mean   = 108.4735 deg
          StdDev = 12.0781 deg

        T--T SUMMARY
          Range  = 3.8163 A <--> 5.8382 A
          Mean   = 4.8140 A
          StdDev = 0.4694 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2912 A

T1  -- O2  -- T2  = 127.493 deg ; T1  -- T2   2.9290 A

T1  -- O3  -- T2  = 143.915 deg ; T1  -- T2   3.0892 A

T1  -- O4  -- T2  = 116.623 deg ; T1  -- T2   2.7400 A

T2  -- O5  -- T2  = 133.572 deg ; T2  -- T2   3.0124 A


        T-O-T SUMMARY
          Range  = 116.6225° <--> 180.0000 deg
          Mean   = 140.3205 deg
          StdDev = 22.2856 deg

        T--T SUMMARY
          Range  = 2.7400 A <--> 3.2912 A
          Mean   = 3.0124 A
          StdDev = 0.1863 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7400 Angstrom
T2  -- T1  = 2.7400 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 442 503 563 623
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 441 503 563 623
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000